RESUMEN
OBJECTIVES: In this study, we evaluated the quality and quantity of bone formation in maxillary sinus floor elevation procedure using a new fully synthetic biphasic calcium phosphate (BCP) consisting of a mixture of 60% hydroxyapatite and 40% of beta-tricalcium phosphate (Straumann Bone Ceramic). MATERIAL AND METHODS: A unilateral maxillary sinus floor elevation procedure was performed in six patients using 100% BCP. Biopsy retrieval for histological and histomorphometric analysis was carried out before implant placement after a 6-month healing period. RESULTS: In this study, the maxillary sinus floor elevation procedure with the use of BCP showed uneventful healing. Radiological evaluation after 6 months showed maintenance of vertical height gained immediately after surgery. Primary stability was achieved with all Straumann SLA dental implants of 4.1 mm diameter and 10 or 12 mm length. The implants appeared to be osseointegrated well after a 3-month healing period. Histological investigation showed no signs of inflammation. Cranial from the native alveolar bone, newly formed mineralized tissue was observed. Also, osteoid islands as well as connective tissue were seen around the BCP particles, cranial from the front of newly formed mineralized tissue. Close bone-to-substitute contact was observed. Histomorphometric analysis showed an average bone volume/total volume (BV/TV) of 27.3% [standard deviation (SD) 4.9], bone surface/total volume (BS/TV) 4.5 mm(2)/mm(3) (SD 1.1), trabecula-thickness (TbTh) 132.1 mum (SD 38.4), osteoid-volume/bone volume (OV/BV) 7.5% (SD 4.3), osteoid surface/bone surface (OS/BS) 41.3% (SD 28.5), osteoid thickness (O.Th) 13.3 mum (SD 4.7) and number of osteoclasts/total area (N.Oc/Tar) 4.4 1/mm (SD 5.7). CONCLUSIONS: Although a small number of patients were treated, this study provides radiological and histological evidence in humans confirming the suitability of this new BCP for vertical augmentation of the atrophied maxilla by means of a maxillary sinus floor elevation procedure allowing subsequent dental implant placement after a 6-month healing period. The newly formed bone had a trabecular structure and was in intimate contact with the substitute material, outlining the osteoconductive properties of the BCP material. Bone maturation was evident by the presence of lamellar bone.
Asunto(s)
Aumento de la Cresta Alveolar/métodos , Sustitutos de Huesos/uso terapéutico , Cerámica/uso terapéutico , Seno Maxilar/cirugía , Procedimientos Quirúrgicos Preprotésicos Orales/métodos , Oseointegración/fisiología , Osteogénesis/fisiología , Adulto , Anciano , Materiales Biocompatibles/uso terapéutico , Biopsia , Femenino , Humanos , Masculino , Seno Maxilar/diagnóstico por imagen , Seno Maxilar/fisiología , Persona de Mediana Edad , Radiografía Panorámica , Resultado del Tratamiento , Cicatrización de Heridas/fisiologíaRESUMEN
BACKGROUND: This study evaluates the clinical, radiological, histological, and histomorphometric aspects of a fully synthetic biphasic calcium phosphate (BCP) (60% hydroxyapatite and 40% ß-tricalcium phosphate), used in a human maxillary sinus floor elevation (MSFE) procedure with 9- and 12-month healing time. METHODS: A unilateral MSFE procedure, using 100% BCP, was performed in two series of five patients with healing times of 9 and 12 months respectively. Clinical and radiological parameters were measured up to 5 years postoperatively. Biopsy retrieval was carried out during dental implants placement. Histology and histomorphometry were performed on 5-µm sections of undecalcified bone biopsies. RESULTS: The MSFE procedure with BCP showed uneventful healing in all cases. All dental implants appeared to be well osseointegrated after 3 months. Radiological evaluation showed less than 1 mm tissue height loss from MSFE to the 5-year follow-up examination. No signs of inflammation were detected on histological examination. Newly formed mineralized tissue was found cranially from the native bone. The BCP particles were surrounded by connective tissue, osteoid islands, and newly formed bone. Mineralized bone tissue was in intimate contact with the BCP particles. After 12 months, remnants of BCP were still present. The newly formed bone had a trabecular structure. Bone maturation was demonstrated by the presence of lamellar bone. Histomorphometric analysis showed at 9 and 12 months respectively an average vital bone volume/total volume of 35.2 and 28.2%, bone surface/total volume of 4.2 mm2/mm3 and 8.3 mm2/mm3, trabecular thickness of 224.7 and 66.7 µm, osteoid volume/bone volume of 8.8 and 3.4%, osteoid surface/bone surface (OS/BS) of 42.4 and 8.2%, and osteoid thickness of 93.9 and 13.6 µm. CONCLUSIONS: MFSE with BCP resulted in new bone formation within the augmented sinus floor and allowed the osseointegration of dental implants in both groups. From a histological and histomorphometric perspective, a 9-month healing time for this type of BCP may be the optimal time for placement of dental implants.