Polymorphism and orientation control of copper-dicarboxylate metal-organic framework thin films through vapour- and liquid-phase growth.

Precise control over the crystalline phase and crystallographic orientation within thin films of metal-organic frameworks (MOFs) is highly desirable. Here, we report a comparison of the liquid- and vapour-phase film deposition of two copper-dicarboxylate MOFs starting from an oriented metal hydroxide precursor. X-ray diffraction revealed that the vapour- or liquid-phase reaction of the linker with this precursor results in different crystalline phases, morphologies, and orientations. Pole figure analysis showed that solution-based growth of the MOFs follows the axial texture of the metal hydroxide precursor, resulting in heteroepitaxy. In contrast, the vapour-phase method results in non-epitaxial growth with uniplanar texture only.

Humidity Response of Cellulose Thin Films.

Cellulose-water interactions are crucial to understand biological processes as well as to develop tailor made cellulose-based products. However, the main challenge to study these interactions is the diversity of natural cellulose fibers and alterations in their supramolecular structure. Here, we study the humidity response of different, well-defined, ultrathin cellulose films as a function of industrially relevant treatments using different techniques. As treatments, drying at elevated temperature, swelling, and swelling followed by drying at elevated temperatures were chosen. The cellulose films were prepared by spin coating a soluble cellulose derivative, trimethylsilyl cellulose, onto solid substrates followed by conversion to cellulose by HCl vapor. For the highest investigated humidity levels (97%), the layer thickness increased by ca. 40% corresponding to the incorporation of 3.6 molecules of water per anhydroglucose unit (AGU), independent of the cellulose source used. The aforementioned treatments affected this ratio significantly with drying being the most notable procedure (2.0 and 2.6 molecules per AGU). The alterations were investigated in real time with X-ray reflectivity and quartz crystal microbalance with dissipation, equipped with a humidity module to obtain information about changes in the thickness, roughness, and electron density of the films and qualitatively confirmed using grazing incidence small angle X-ray scattering measurements using synchrotron irradiation.

Structural Order in Cellulose Thin Films Prepared from a Trimethylsilyl Precursor.

Biopolymer cellulose is investigated in terms of the crystallographic order within thin films. The films were prepared by spin-coating of a trimethylsilyl cellulose precursor followed by an exposure to HCl vapors; two different source materials were used. Careful precharacterization of the films was performed by infrared spectroscopy and atomic force microscopy. Subsequently, the films were investigated by grazing incidence X-ray diffraction using synchrotron radiation. The results showed broad diffraction peaks, indicating a rather short correlation length of the molecular packing in the range of a few nanometers. The analysis of the diffraction patterns was based on the known structures of crystalline cellulose, as the observed peak pattern was comparable to cellulose phase II and phase III. The dominant fraction of the film is formed by two different types of layers, which are oriented parallel to the substrate surface. The stacking of the layers results in a one-dimensional crystallographic order with a defined interlayer distance of either 7.3 or 4.2 Å. As a consequence, two different preferred orientations of the polymer chains are observed. In both cases, polymer chain axes are aligned parallel to the substrate surface, and the orientation of the cellulose molecules are concluded to be either edge-on or flat-on. A minor fraction of the cellulose molecules form nanocrystals that are randomly distributed within the films. In this case, the molecular packing density was found to be smaller in comparison to the known crystalline phases of cellulose.

Substrate-Induced Phase of a Benzothiophene Derivative Detected by Mid-Infrared and Lattice Phonon Raman Spectroscopy.

The presence of a substrate-induced polymorph of 2,7-dioctyloxy[1]benzothieno[3,2-b]benzothiophene is probed in microscopic crystals and in thin films. Two experimental techniques are used: lattice phonon Raman and IR spectroscopy. The bulk crystal and substrate-induced phase have an entirely different molecular packing, and therefore, their Raman spectra are characteristic fingerprints of the respective polymorphs. These spectra can be unambiguously assigned to the individual polymorphs. Drop-cast and spin-coated thin films on solid substrates are investigated in the as-prepared state and after solvent-vapor annealing. Because Raman spectroscopy is less sensitive with decreasing film thickness, IR spectroscopy is shown to be a more feasible tool for phase detection. The surface-induced phase is mainly present in the as-prepared thin films, whereas the bulk phase is present after solvent-vapor annealing. This result suggests that the surface-induced phase is a metastable polymorph.

Crystal alignment of caffeine deposited onto single crystal surfaces via hot-wall epitaxy.

Defined crystal growth is highly demanded for technological applications but also fundamental research. Within this work, the crystal growth of the asymmetric molecule caffeine was studied on single crystalline surfaces of muscovite mica, sodium chloride and potassium chloride. While elongated needle-like crystals grow on muscovite mica and sodium chloride, smaller individual "bird-like" structures were observed on potassium chloride. Depending on the surface type and temperature, the disk-shaped caffeine molecules prefer either an edge-on or flat-on orientation with respect to the surface, but in each case, a defined crystallographic relation between the surface and caffeine crystallites was determined by using the X-ray pole figure technique. On muscovite mica and sodium chloride, needle-like crystallites with edge-on oriented molecules aligned mainly with the unit cell c-axis (which coincides with the long needle axis) along the [1-10]mica, [100]mica, [110]mica and [110]NaCl, [1-10]NaCl directions, respectively. Crystals consisting of flat-on oriented molecules on KCl showed also defined alignments with respect to the substrate, but due to the altered molecule-substrate contact, the b-axis aligned along [110]KCl and [1-10]KCl. Growth at elevated temperatures enabled changes in the crystal growth whereby more defined structures formed on NaCl. On KCl, the bird-like structures remained very similar, while caffeine on the mica surface at elevated temperatures resulted in even additional texture forming with the caffeine molecules now also favoring a flat-on orientation with respect to the surface. The systematic variation of various system parameters demonstrates how sensitive the growth behavior of caffeine on this variety of substrates is.

Solution of an elusive pigment crystal structure from a thin film: a combined X-ray diffraction and computational study.

Epindolidione, a hydrogen-bonded derivative of the organic semiconductor tetracene, is an organic pigment which has previously been used to produce stable OFETs with relatively high hole mobilities. Despite its use as an inkjet pigment and organic semiconductor, the crystal structure of epindolidione has proved elusive and is currently unknown. In this work, we report a crystal structure solution of epindolidione determined from vapor deposited thin films using a combined experimental and theoretical approach. The structure is found to be similar to one of the previously reported epindolidione derivatives and is most likely a surface-mediated polymorph, with a slightly different crystal packing compared to the bulk powder. The effect of substrate temperature on film morphology and structure is also investigated, where it is found that the crystallite orientation can be tuned by deposition at different substrate temperatures. The results also illustrate the possibilities for crystal structures to be solved from thin films.

Quasi-one-dimensional cyano-phenylene aggregates: Uniform molecule alignment contrasts varying electrostatic surface potential.

The epitaxial growth of the mono-functionalized para-quaterphenylene molecule CNHP4 on muscovite mica is investigated. The vacuum deposited molecules aggregate into nanofibers of varying morphology. Due to muscovite's cm symmetry, almost mutually parallel fibers grow. Polarized light microscopy together with X-ray diffraction resolves the projected orientation of the molecules on the substrate surface and within the fibers. Several different contact planes with the substrate are detected. For all of them, the molecules orient with their long molecule axis approximately perpendicular to the grooved muscovite direction, so that the alignment of the molecules on the substrate is uniform. Kelvin probe force microscopy finds vastly different electrostatic properties of different fiber types and facets.

Multiple scattering in grazing-incidence X-ray diffraction: impact on lattice-constant determination in thin films.

Dynamical scattering effects are observed in grazing-incidence X-ray diffraction experiments using an organic thin film of 2,2':6',2''-ternaphthalene grown on oxidized silicon as substrate. Here, a splitting of all Bragg peaks in the out-of-plane direction (z-direction) has been observed, the magnitude of which depends both on the incidence angle of the primary beam and the out-of-plane angle of the scattered beam. The incident angle was varied between 0.09° and 0.25° for synchrotron radiation of 10.5 keV. This study reveals comparable intensities of the split peaks with a maximum for incidence angles close to the critical angle of total external reflection of the substrate. This observation is rationalized by two different scattering pathways resulting in diffraction peaks at different positions at the detector. In order to minimize the splitting, the data suggest either using incident angles well below the critical angle of total reflection or angles well above, which sufficiently attenuates the contributions from the second scattering path. This study highlights that the refraction of X-rays in (organic) thin films has to be corrected accordingly to allow for the determination of peak positions with sufficient accuracy. Based thereon, a reliable determination of the lattice constants becomes feasible, which is required for crystallographic structure solutions from thin films.

Adsorption, desorption, and film formation of quinacridone and its thermal cracking product indigo on clean and carbon-covered silicon dioxide surfaces.

The evaporation of quinacridone from a stainless steel Knudsen cell leads to the partial decomposition of this molecule in the cell, due to its comparably high sublimation temperature. At least one additional type of molecules, namely indigo, could be detected in the effusion flux. Thermal desorption spectroscopy and atomic force microscopy have been used to study the co-deposition of these molecules on sputter-cleaned and carbon-covered silicon dioxide surfaces. Desorption of indigo appears at temperatures of about 400 K, while quinacridone desorbs at around 510 K. For quinacridone, a desorption energy of 2.1 eV and a frequency factor for desorption of 1 × 10(19) s(-1) were calculated, which in this magnitude is typical for large organic molecules. A fraction of the adsorbed quinacridone molecules (∼5%) decomposes during heating, nearly independent of the adsorbed amount, resulting in a surface composed of small carbon islands. The sticking coefficients of indigo and quinacridone were found to be close to unity on a carbon covered SiO2 surface but significantly smaller on a sputter-cleaned substrate. The reason for the latter can be attributed to insufficient energy dissipation for unfavorably oriented impinging molecules. However, due to adsorption via a hot-precursor state, the sticking probability is increased on the surface covered with carbon islands, which act as accommodation centers.

Crystallization of Tyrian Purple (6,6'-Dibromoindigo) Thin Films: The Impact of Substrate Surface Modifications.

The pigment 6,6'-dibromoindigo (Tyrian purple) shows strong intermolecular hydrogen bonds and the film formation is, therefore, expected to be influenced by the polar character of the substrate surface. Thin films of Tyrian purple were prepared by physical vapor deposition on a variety of substrates with different surface energies: from highly polar silicon dioxide surfaces to hydrophobic polymer surfaces. The crystallographic properties were investigated by X-ray diffraction techniques such as X-ray reflectivity and grazing incidence X-ray diffraction. In all cases, crystallites with "standing" molecules relative to the substrate surface were observed independently of the substrate surface energy. In the case of polymer surfaces, additional crystallites are formed containing "lying" molecules with their aromatic planes parallel to the substrate surface. Small differences in the crystallographic lattice constants were observed as a function of substrate surface energy, the corresponding small changes in the molecular packing are explained by a variation of the hydrogen bond geometries. This work reveals that despite the limited influence of the surface energy on the molecular orientation, the crystalline packing of Tyrian purple within thin films is altered and slightly different structures form.

Thermal stability and molecular ordering of organic semiconductor monolayers: effect of an anchor group.

The thermal stability and molecular order in monolayers of two organic semiconductors, PBI-PA and PBI-alkyl, based on perylene derivatives with an identical molecular structure except for an anchor group for attachment to the substrate in PBI-PA, are reported. In situ X-ray reflectivity measurements are used to follow the stability of these monolayers in terms of order and thickness as temperature is increased. Films have thicknesses corresponding approximately to the length of one molecule; molecules stand upright on the substrate with a defined structure. PBI-PA monolayers have a high degree of order at room temperature and a stable film exists up to 250 °C, but decomposes rapidly above 300 °C. In contrast, stable physisorbed PBI-alkyl monolayers only exist up to 100 °C. Above the bulk melting point at 200 °C no more order exists. The results encourage using anchor groups in monolayers for various applications as it allows enhanced stability at the interface with the substrate.

Polymorphism of dioctyl-terthiophene within thin films: The role of the first monolayer.

The origins of specific polymorphic phases within thin films are still not well understood. The polymorphism of the molecule dioctyl-terthiophene is investigated during the presence of a silicon-oxide surface during the crystallisation process. It is found that a monolayer of molecules forms two-dimensional crystals on the surface. In the case of thicker films crystalline islands are formed, a comparison of the three polymorphic phases observed within thin films and the thermodynamically more stable single crystal phases reveals distinct differences which can be related to an adaption of the molecular packing with the flat surface of the substrate.

Film growth, adsorption and desorption kinetics of indigo on SiO2.

Organic dyes have recently been discovered as promising semiconducting materials, attributable to the formation of hydrogen bonds. In this work, the adsorption and desorption behavior, as well as thin film growth was studied in detail for indigo molecules on silicon dioxide with different substrate treatments. The material was evaporated onto the substrate by means of physical vapor deposition under ultra-high vacuum conditions and was subsequently studied by Thermal Desorption Spectroscopy (TDS), Auger Electron Spectroscopy, X-Ray Diffraction, and Atomic Force Microscopy. TDS revealed initially adsorbed molecules to be strongly bonded on a sputter cleaned surface. After further deposition a formation of dimers is suggested, which de-stabilizes the bonding mechanism to the substrate and leads to a weakly bonded adsorbate. The dimers are highly mobile on the surface until they get incorporated into energetically favourable three-dimensional islands in a dewetting process. The stronger bonding of molecules within those islands could be shown by a higher desorption temperature. On a carbon contaminated surface no strongly bonded molecules appeared initially, weakly bonded monomers rather rearrange into islands at a surface coverage that is equivalent to one third of a monolayer of flat-lying molecules. The sticking coefficient was found to be unity on both substrates. The desorption energies from carbon covered silicon dioxide calculated to 1.67 ± 0.05 eV for multilayer desorption from the islands and 0.84 ± 0.05 eV for monolayer desorption. Corresponding values for desorption from a sputter cleaned surface are 1.53 ± 0.05 eV for multilayer and 0.83 ± 0.05 eV for monolayer desorption.

Icephobic Gradient Polymer Coatings Deposited via iCVD: A Novel Approach for Icing Control and Mitigation.

Materials against ice formation and accretion are highly desirable for different industrial applications and daily activities affected by icing. Although several concepts have been proposed, no material has so far shown wide-ranging icephobic features, enabling durability and manufacturing on large scales. Herein, we present gradient polymers made of 1,3,5,7-tetravinyl-1,3,5,7-tetramethylcyclotetrasiloxane (V4D4) and 1H,1H,2H,2H-perfluorodecyl acrylate (PFDA) deposited in one step via initiated chemical vapor deposition (iCVD) as an effective coating to mitigate ice accretion and reduce ice adhesion. The gradient structures easily overcome adhesion, stability, and durability issues of traditional fluorinated coatings. The coatings show promising icephobic performance by reducing ice adhesion, depressing the freezing point, delaying drop freezing, and inhibiting ice nucleation and frost propagation. Icephobicity correlates with surface energy discontinuities at the surface plane resulting from the random orientation of the fluorinated groups of PFDA, as confirmed by grazing-incidence X-ray diffraction measurements. The icephobicity could be further improved by tuning the surface crystallinity rather than surface wetting, as samples with random crystal orientation show the lowest ice adhesion despite high contact angle hysteresis. The iCVD-manufactured coatings show promising results, indicating the potential for ice control on larger scales and various applications.

Interfacial Engineering of Soft Matter Substrates by Solid-State Polymer Adsorption.

Polymer coating to substrates alters surface chemistry and imparts bulk material functionalities with a minute thickness, even in nanoscale. Specific surface modification of a substate usually requires an active substrate that, e.g., undergoes a chemical reaction with the modifying species. Here, we present a generic method for surface modification, namely, solid-state adsorption, occurring purely by entropic strive. Formed by heating above the melting point or glass transition and subsequent rinsing of the excess polymer, the emerging ultrathin (<10 nm) layers are known in fundamental polymer physics but have never been utilized as building blocks for materials and they have never been explored on soft matter substrates. We show with model surfaces as well as bulk substrates, how solid-state adsorption of common polymers, such as polystyrene and poly(lactic acid), can be applied on soft, cellulose-based substrates. Our study showcases the versatility of solid-state adsorption across various polymer/substrate systems. Specifically, we achieve proof-of-concept hydrophobization on flexible cellulosic substrates, maintaining irreversible and miniscule adsorption yet with nearly 100% coverage without compromising the bulk material properties. The method can be considered generic for all polymers whose Tg and Tm are below those of the to-be-coated adsorbed layer, and whose integrity can withstand the solvent leaching conditions. Its full potential has broad implications for diverse materials systems where surface coatings play an important role, such as packaging, foldable electronics, or membrane technology.

X-ray based tools for the investigation of buried interfaces in organic electronic devices.

X-ray reflectivity combined with grazing incidence diffraction is a valuable tool for investigating organic multilayer structures that can be used in devices. We focus on a bilayer stack consisting of two materials (poly-(3-hexylthiophene)) (P3HT) and poly-(4-styrenesulfonic acid) (PSSA) spin cast from orthogonal solvents (water in the case of PSSA and chloroform or toluene for P3HT). X-ray reflectivity is used to determine the thickness of all layers as well as the roughness of the organic-organic hetero-interface and the P3HT surface. The surface roughness is found to be consistent with the results of atomic force microscopy measurements. For the roughness of P3HT/PSSA interface, we observe a strong dependence on the solvent used for P3HT deposition. The solvent also strongly impacts the texturing of the P3HT crystallites as revealed by grazing incidence diffraction. When applying the various PSSA/P3HT multilayers in organic thin-film transistors, we find an excellent correlation between the determined interface morphology, structure and the device performance.

Dynamics of monolayer-island transitions in 2,7-dioctyl-benzothienobenzthiophene thin films.

The order in molecular monolayers is a crucial aspect for their technological application. However, the preparation of defined monolayers by spin-coating is a challenge, since the involved processes are far from thermodynamic equilibrium. In the work reported herein, the dynamic formation of dioctyl-benzothienobenzothiophene monolayers is explored as a function of temperature by using X-ray scattering techniques and atomic force microscopy. Starting with a disordered monolayer after the spin-coating process, post-deposition self-reassembly at room temperature transforms the initially amorphous layer into a well-ordered bilayer structure with a molecular herringbone packing, whereas at elevated temperature the formation of crystalline islands occurs. At the temperature of the liquid-crystalline crystal-smectic transition, rewetting of the surface follows resulting in a complete homogeneous monolayer. By subsequent controlled cooling to room temperature, cooling-rate-dependent kinetics is observed; at rapid cooling, a stable monolayer is preserved at room temperature, whereas slow cooling causes bilayer structures. Increasing the understanding and control of monolayer formation is of high relevance for achieving ordered functional monolayers with defined two-dimensional packing, for future applications in the field of organic electronics.

Exploring the effects of graphene and temperature in reducing electron beam damage: A TEM and electron diffraction-based quantitative study on Lead Phthalocyanine (PbPc) crystals.

High-resolution transmission electron microscopy (TEM) of organic crystals, such as Lead Phthalocyanine (PbPc), is very challenging since these materials are prone to electron beam damage leading to the breakdown of the crystal structure during investigation. Quantification of the damage is imperative to enable high-resolution imaging of PbPc crystals with minimum structural changes. In this work, we performed a detailed electron diffraction study to quantitatively measure degradation of PbPc crystals upon electron beam irradiation. Our study is based on the quantification of the fading intensity of the spots in the electron diffraction patterns. At various incident dose rates (e/Å2/s) and acceleration voltages, we experimentally extracted the decay rate (1/s), which directly correlates with the rate of beam damage. In this manner, a value for the critical dose (e/Å2) could be determined, which can be used as a measure to quantify beam damage. Using the same methodology, we explored the influence of cryogenic temperatures, graphene TEM substrates, and graphene encapsulation in prolonging the lifetime of the PbPc crystal structure during TEM investigation. The knowledge obtained by diffraction experiments is then translated to real space high-resolution TEM imaging of PbPc.

Synergistic Effect of Solvent Vapor Annealing and Chemical Doping for Achieving High-Performance Organic Field-Effect Transistors with Ideal Electrical Characteristics.

Contact resistance and charge trapping are two key obstacles, often intertwined, that negatively impact on the performance of organic field-effect transistors (OFETs) by reducing the overall device mobility and provoking a nonideal behavior. Here, we expose organic semiconductor (OSC) thin films based on blends of 2,7-dioctyl[1]benzothieno[3,2-b][1]benzothiophene (C8-BTBT-C8) with polystyrene (PS) to (i) a CH3CN vapor annealing process, (ii) a doping I2/water procedure, and (iii) vapors of I2/CH3CN to simultaneously dope and anneal the films. After careful analysis of the OFET electrical characteristics and by performing local Kelvin probe force microscopy studies, we found that the vapor annealing process predominantly reduces interfacial shallow traps, while the chemical doping of the OSC film is responsible for the diminishment of deeper traps and promoting a significant reduction of the contact resistance. Remarkably, the devices treated with I2/CH3CN reveal ideal electrical characteristics with a low level of shallow/deep traps and a very high and almost gate-independent mobility. Hence, this work demonstrates the promising synergistic effects of performing simultaneously a solvent vapor annealing and doping procedure, which can lead to trap-free OSC films with negligible contact resistance problems.

Memory Effect by Melt Crystallization Observed in Polymorphs of a Benzothieno-Benzothiophene Derivative.

This work provides a comprehensive illustration of a crystalline melt memory effect recorded for three solvates of the 2,7-bis(2-(2-methoxyethoxy)ethoxy)benzo[b]benzo[4,5] thieno[2,3-d]thiophene (OEG-BTBT) molecule with dichloromethane (DCM) molecules. Combined optical microscopy and X-ray diffraction measurements at different temperatures are used to get an overview of the structural and morphological properties like melting points, isotropic transition temperatures, induction times, and crystallization kinetics of the three forms. An outstanding observation is made upon annealing the three polymorphs at temperatures well above their respective melting points as well as above the optical clearance temperature. After cooling back to room temperature, recrystallization results in the formation of the initial phase present before the annealing process. This melt memory effect is observed for all three solvates. These observations can be correlated to the strong interaction between the DCM molecules and the oligoethylene glycol side chains, even in the molten state. This conclusion rationalizes the experimental observation made upon solvent vapor annealing of the crystalline sample with DCM, which unambiguously transformed the system into a disordered state.