RESUMEN
Novel nanomaterials used for wound healing should have many beneficial properties, including high biological and antibacterial activity. Immobilization of proteins can stimulate cell migration and viability, and implanted Ag ions provide an antimicrobial effect. However, the ion implantation method, often used to introduce a bactericidal element into the surface, can lead to the degradation of vital proteins. To analyze the surface structure of nanofibers coated with a layer of plasma COOH polymer, fibronectin/gentamicin, and implanted with Ag ions, a new X-ray photoelectron spectroscopy (XPS) fitting method is used for the first time, allowing for a quantitative assessment of surface biomolecules. The results demonstrated noticeable changes in the composition of fibronectin- and gentamicin-modified nanofibers upon the introduction of Ag ions. Approximately 60% of the surface chemistry has changed, mainly due to an increase in hydrocarbon content and the introduction of up to 0.3 at.% Ag. Despite the significant degradation of fibronectin molecules, the biological activity of Ag-implanted nanofibers remained high, which is explained by the positive effect of Ag ions inducing the generation of reactive oxygen species. The PCL nanofibers with immobilized gentamicin and implanted silver ions exhibited very significant antipathogen activity to a wide range of Gram-positive and Gram-negative strains. Thus, the results of this work not only make a significant contribution to the development of new hybrid fiber materials for wound dressings but also demonstrate the capabilities of a new XPS fitting methodology for quantitative analysis of surface-related proteins and antibiotics.
RESUMEN
Zn-containing TiO2-based coatings with Na, Ca, Si, and K additives were obtained by plasma electrolytic oxidation (PEO) of Ti in order to achieve an effective and broad bactericidal protection without compromising biocompatibility. A protocol has been developed for cleaning the coating surface from electrolyte residues, ensuring the preservation of the microstructure and composition of the surface layer. Using high-resolution transmission electron microscopy, three characteristic microstructural zones in the PEO-Zn coating are well documented: zone 1 with a TiO2-based nanocrystalline structure, zone 2 with an amorphous structure, and zone 3 around pores with an amorphous-nanocrystalline structure. The excellent cytocompatibility of PEO-Zn samples was confirmed by three different methods: monitoring the proliferation of MC3T3-E1 cells, assessing the viability of sheep osteoblast cells using calcein-AM staining and fluorescence microscopy, and incubation with spheroids based on primary osteoblast cells and mouse embryonic fibroblast NIH3T3 cells. The PEO-Zn coatings absorb >60% of the incident light over the UV and Vis-NIR spectral ranges. After 24 h, the PEO-Zn coatings completely inactivate four types of strains: Gram-positive Staphylococcus aureus CSA154 and ATCC29213 and Gram-negative Escherichia coli K261 and U20, and also prevent E. coli U20 and K261 biofilm formation. The superior antibacterial activity is associated with the synergistic effect of Zn2+ ions in safe concentration and reactive oxygen species (ROS) generated in response to either UV irradiation or soft short-term X-ray irradiation. The X-ray irradiation-induced ROS formation by a PEO coating is reported for the first time. The enhanced bactericidal activity after X-ray irradiation compared to UV illumination is attributed to the more intense ROS generation in the first few hours. The results obtained significantly expand the possibilities of using PEO coatings on the surfaces of titanium implants.