Pulsed Laser Ablation of Oxygen deficiency Enriched Superlattice Vanadium Pentoxide (V2O5) Ultrathin Nextrode aiming for Flexible Binder-less Tandem Energy Harvesting Devices.

For the initial instance, oxygen deficiency-enriched vanadium pentoxide (O─V2O5@500) thin film electrodes are tuned by the Pulsed Laser Ablation technique. The O─V2O5@500 thin film electrode shows remarkable electrochemical performances confirming the greater potential window of -0.4 to 0.9 V versus Hg/HgO in an alkaline electrolyte; also, the O─V2O5@ 500 thin film electrode exhibits a noteworthy volumetric capacity of 167.7 mAh cm-3 (areal capacity of 73.3 µAh cm-2). Additionally, Density Functional Theory (DFT) theory calculations are carried out for oxygen-deficient V2O5. From the partial density of states (pDOS) and partial charge density analysis, it is clear that oxygen vacancy improves the electrical conductivity due to the higher degree of electron delocalization of V─O─V near the vacancy and enhances the redox properties due to the formation of in-gap states. Further, it is reported that a O─V2O5@ 500 ||PVA-KOH|| Bi2O3 A-650 thin film supercapbattery (TFSCB) device attains an exceptional discharge volumetric capacitance of 182.85 F cm-3 (equal volumetric capacity of 124.5 mAh cm-3). Furthermore, the TFSCB device exhibits an extraordinary maximum volumetric energy (power) density of 14.28 mWh cm-3 (1.66 W cm-3); TFSCB succeeds in supreme capacity retention of 86% with outstanding coulombic efficiency of 94.4% after 21 000 cycles.

Synergistic Bactericidal Effect of Zn2+ Ions and Reactive Oxygen Species Generated in Response to Either UV or X-ray Irradiation of Zn-Doped Plasma Electrolytic Oxidation TiO2 Coatings.

Zn-containing TiO2-based coatings with Na, Ca, Si, and K additives were obtained by plasma electrolytic oxidation (PEO) of Ti in order to achieve an effective and broad bactericidal protection without compromising biocompatibility. A protocol has been developed for cleaning the coating surface from electrolyte residues, ensuring the preservation of the microstructure and composition of the surface layer. Using high-resolution transmission electron microscopy, three characteristic microstructural zones in the PEO-Zn coating are well documented: zone 1 with a TiO2-based nanocrystalline structure, zone 2 with an amorphous structure, and zone 3 around pores with an amorphous-nanocrystalline structure. The excellent cytocompatibility of PEO-Zn samples was confirmed by three different methods: monitoring the proliferation of MC3T3-E1 cells, assessing the viability of sheep osteoblast cells using calcein-AM staining and fluorescence microscopy, and incubation with spheroids based on primary osteoblast cells and mouse embryonic fibroblast NIH3T3 cells. The PEO-Zn coatings absorb >60% of the incident light over the UV and Vis-NIR spectral ranges. After 24 h, the PEO-Zn coatings completely inactivate four types of strains: Gram-positive Staphylococcus aureus CSA154 and ATCC29213 and Gram-negative Escherichia coli K261 and U20, and also prevent E. coli U20 and K261 biofilm formation. The superior antibacterial activity is associated with the synergistic effect of Zn2+ ions in safe concentration and reactive oxygen species (ROS) generated in response to either UV irradiation or soft short-term X-ray irradiation. The X-ray irradiation-induced ROS formation by a PEO coating is reported for the first time. The enhanced bactericidal activity after X-ray irradiation compared to UV illumination is attributed to the more intense ROS generation in the first few hours. The results obtained significantly expand the possibilities of using PEO coatings on the surfaces of titanium implants.