The controllable synthesis of carbon nanofibers (CNF) and composites based on CNF (Metals/CNF) is of particular interest. In the present work, the samples of CNF were produced via ethylene decomposition over Co-Pt (0-100 at.% Pt) microdispersed alloys prepared by a reductive thermolysis of multicomponent precursors. XRD analysis showed that the crystal structure of alloys in the composition range of 5-35 at.% Pt corresponds to a fcc lattice based on cobalt (Fm-3m), while the CoPt (50 at.% Pt) and CoPt3 (75 at.% Pt) samples are intermetallics with the structure P4/mmm and Pm-3m, respectively. The microstructure of the alloys is represented by agglomerates of polycrystalline particles (50-150 nm) interconnected by the filaments. The impact of Pt content in the Co1-xPtx samples on their activity in CNF production was revealed. The interaction of alloys with ethylene is accompanied by the generation of active particles on which the growth of nanofibers occurs. Plane Co showed low productivity (~5.5 g/gcat), while Pt itself exhibited no activity at all. The addition of 15-25 at.% Pt to cobalt catalyst leads to an increase in activity by 3-5 times. The maximum yield of CNF reached 40 g/gcat for Co0.75Pt0.25 sample. The local composition of the active alloyed particles and the structural features of CNF were explored.
RESUMEN
The processes of carbon erosion of nickel alloys during the catalytic pyrolysis of organic compounds with the formation of carbon nanofibers in a flow-through reactor as well as under reaction conditions in a close volume (Reactions under Autogenic Pressure at Elevated Temperature, RAPET) were studied. The efficiency of the ferromagnetic resonance method to monitor the appearance of catalytically active nickel particles in these processes has been shown. As found, the interaction of bulk Ni-Cr alloy with the reaction medium containing halogenated hydrocarbons (1,2-dichloroethane, 1-iodobutane, 1-bromobutane) results in the appearance of ferromagnetic particles of similar dimensions (~200-300 nm). In the cases of hexachlorobenzene and hexafluorobenzene, the presence of a hydrogen source (hexamethylbenzene) in the reaction mixture was shown to be highly required. The microdispersed samples of Ni-Cu and Ni-Mo alloys were prepared by mechanochemical alloying of powders and by reductive thermolysis of salts-precursors, accordingly. Their interaction with polymers (polyethylene and polyvinyl chloride) under RAPET conditions and with ethylene and 1,2-dichloroethane in a flow-through reactor are comparatively studied as well. According to microscopic data, the morphology of the formed carbon nanofibers is affected by the alloy composition and by the nature of the used organic substrate.