Piranha-etched titanium nanostructure reduces biofilm formation in vitro.

OBJECTIVES: Nano-modified surfaces for dental implants may improve gingival fibroblast adhesion and antibacterial characteristics through cell-surface interactions. The present study investigated how a nanocavity titanium surface impacts the viability and adhesion of human gingival fibroblasts (HGF-1) and compared its response to Porphyromonas gingivalis with those of marketed implant surfaces. MATERIAL AND METHODS: Commercial titanium and zirconia disks, namely, sandblasted and acid-etched titanium (SLA), sandblasted and acid-etched zirconia (ZLA), polished titanium (PT) and polished zirconia (ZrP), and nanostructured disks (NTDs) were tested. Polished titanium disks were etched with a 1:1 combination of 98% H2SO4 and 30% H2O2 (piranha etching) for 5 h at room temperature to produce the NTDs. Atomic force microscopy was used to measure the surface topography, roughness, adhesion force, and work of adhesion. MTT assays and immunofluorescence staining were used to examine cell viability and adhesion after incubation of HGF-1 cells on the disk surfaces. After incubation with P. gingivalis, conventional culture, live/dead staining, and SEM were used to determine the antibacterial properties of NTD, SLA, ZLA, PT, and ZrP. RESULTS: Etching created nanocavities with 10-20-nm edge-to-edge diameters. Chemical etching increased the average surface roughness and decreased the surface adherence, while polishing and flattening of ZrP increased adhesion. However, only the NTDs inhibited biofilm formation and bacterial adherence. The NTDs showed antibacterial effects and P. gingivalis vitality reductions. The HGF-1 cells demonstrated greater viability on the NTDs compared to the controls. CONCLUSION: Nanocavities with 10-20-nm edge-to-edge diameters on titanium disks hindered P. gingivalis adhesion and supported the adhesion of gingival fibroblasts when compared to the surfaces of currently marketed titanium or zirconia dental implants. CLINICAL RELEVANCE: This study prepared an effective antibacterial nanoporous surface, assessed its effects against oral pathogens, and demonstrated that surface characteristics on a nanoscale level influenced oral pathogens and gingival fibroblasts. CLINICAL TRIAL REGISTRATION: not applicable.

Cytokines Activate JAK-STAT Signaling Pathway in MG-63 Cells on Titanium and Zirconia.

Although titanium has been traditionally used as the gold standard for dental implants, recent years have seen the widespread application of zirconia implants given their superiority with regards to reduced bacterial adhesion, inflammation and cellular-interaction in terms of bio-compatibility. The JAK-STAT signaling pathway plays an important role in bone remodeling and formation. The aim of the study was to investigate the activation of the JAK-STAT pathway through different cytokines in osteoblast-like cells (MG-63) on zirconia in comparison to titanium discs. IFN-γ induced the very strong activation of STAT1 protein, IFN-α activated both STAT1 and STAT3 molecules, IL-6 activated STAT3 and IL-4 induced the activation of STAT6 on both surfaces. The activation of STAT proteins was confirmed by western blot, immunofluorescence and flow cytometry using phospho-specific anti-STAT antibodies, which recognize only phosphorylated STAT proteins. The incubation of MG-63 cells with IFN-γ caused the upregulation of MHC class I and class II proteins when MG-63 cells were grown on zirconia and titanium discs. In sum, the present study shows that the JAK-STAT pathway is activated in MG-63 cells when they are incubated on titanium or zirconia surfaces.