CO Oxidation over Pd/ZrO2 Catalysts: Role of Support's Donor Sites.

A series of supported Pd/ZrO2 catalysts with Pd loading from 0.2 to 2 wt % was synthesized. The ZrO2 material prepared by a similar technique was used as a reference sample. The samples have been characterized by means of transmission electron microscopy (TEM), X-ray diffraction analysis (XRD), X-ray photoelectron spectroscopy (XPS), temperature-programmed reduction (TPR), testing reaction of ethane hydrogenolysis (HGE), N2 adsorption, and electron paramagnetic resonance (EPR) spectroscopy. 1,3,5-trinitrobenzene was used as a probe molecule for the EPR spin probe method. The catalytic performance of samples was tested in the model reaction of CO oxidation. It was shown that the concentration of donor sites of support measured by EPR spin probe correlates with catalytic behavior during light-off tests. Low concentration of donor sites on a support's surface was found to be caused by the presence of the specific surface defects that are related to existence of coordinately unsaturated structures.

Characterization of electron donor sites on Al2O3 surface.

Formation of radical anions after adsorption of 1,3,5-trinitrobenzene (TNB) on electron donor sites of fully oxidized Al(2)O(3) samples with different phase compositions is studied by EPR. It is shown that the maximum concentration of the radical anions does not substantially depend on the choice of solvent and reaction temperature, and can be used to measure the total concentration of the donor sites. The donor sites are observed in almost the same concentration about 5 × 10(16) m(-2) on all alumina polymorphs except for α-Al(2)O(3). The formation rate of the TNB radical anions and the activation energy of this process are found to depend on the donor properties of the solvent. The EPR in situ experiments showed that a substantial amount of the adsorbate forming a liquid phase is required for generation of the radical anions. These results prove that the sites measured by the formation of the TNB radical anions are not genuine electron donor sites capable of direct electron transfer to the adsorbed TNB molecules. A model of the observed paramagnetic species based on the obtained experimental data and the results of quantum chemical simulations is suggested. According to this model, a TNB radical anion substitutes a hydroxyl group forming a neutral ion pair with a surface aluminum cation. The suggested mechanism for the formation of such ion pairs involves the migration of simple radicals and does not require long-distance charge separation. It is supposed that the donor site where the process is initiated includes a negatively charged surface hydroxyl group.

Mayenite Synthesis from Hydroxide Precursors: Structure Formation and Active Sites on Its Surface.

We studied the formation process of a mayenite structure from hydroxide precursors in different gas media. According to X-ray diffraction data, this method allows a well-crystallized mayenite (Ca12Al14O33 or C12A7) phase to be obtained at low (500-900 °C) temperatures with an insignificant impurity of CaO. It was shown that the lattice parameters for C12A7 obtained in an inert atmosphere (Ar) were lower when compared with similar samples in the air. These results can be explained by the different levels of oxygen nonstoichiometry in the resulting phase. We noted that sintering and crystallization of mayenite proceeds at lower temperatures in Ar than in the air medium. We found the presence of donor and acceptor active sites on the surface of mayenite, which was detected by the spin probe method. The specific (per unit surface) concentration of such sites (2.5 × 1016 m-2 and 1.5 × 1015 m-2 for donor and acceptor sites, respectively) is comparable to that of γ-Al2O3, which is traditionally used as catalyst support. This allows it to be used in adsorption and catalytic technologies, taking into account its high specific surface area (~30-50 m2/g at a low synthesis temperature).

Aluminothermic Synthesis of Dispersed Electrides Based on Mayenite: XRD and EPR Study.

The evolution of the structure and the phase composition of a dispersed mayenite at its interaction with metallic aluminum was studied in a temperature range from 900 to 1400 °C in both argon and air atmospheres. The aluminum loading was varied from 0 to 50 wt%. It was found that the addition of aluminum significantly affects the stability of the mayenite and other calcium aluminate phases within the studied temperature range. The formation of the electride state registered by the appearance of a characteristic electron paramagnetic resonance (EPR) signal from F+-like centers (g~1.994) in an argon atmosphere was shown to take place already at 1150 °C due to an aluminothermic reduction of this material. The super-narrow (Hp-p < 0.5 G) EPR spectra from F+-like centers, which were recently observed for the core−shell structures of the C12A7@C type only, were registered for mayenite for the first time. The results obtained in the present study testify firstly towards the possibility of significantly diminishing the temperatures required for the formation of the electride state in such systems and secondly towards the ability to stabilize the size of small electride nanoparticles within the synthesized calcium aluminate matrix.

Comparative Study on Carbon Erosion of Nickel Alloys in the Presence of Organic Compounds under Various Reaction Conditions.

The processes of carbon erosion of nickel alloys during the catalytic pyrolysis of organic compounds with the formation of carbon nanofibers in a flow-through reactor as well as under reaction conditions in a close volume (Reactions under Autogenic Pressure at Elevated Temperature, RAPET) were studied. The efficiency of the ferromagnetic resonance method to monitor the appearance of catalytically active nickel particles in these processes has been shown. As found, the interaction of bulk Ni-Cr alloy with the reaction medium containing halogenated hydrocarbons (1,2-dichloroethane, 1-iodobutane, 1-bromobutane) results in the appearance of ferromagnetic particles of similar dimensions (~200-300 nm). In the cases of hexachlorobenzene and hexafluorobenzene, the presence of a hydrogen source (hexamethylbenzene) in the reaction mixture was shown to be highly required. The microdispersed samples of Ni-Cu and Ni-Mo alloys were prepared by mechanochemical alloying of powders and by reductive thermolysis of salts-precursors, accordingly. Their interaction with polymers (polyethylene and polyvinyl chloride) under RAPET conditions and with ethylene and 1,2-dichloroethane in a flow-through reactor are comparatively studied as well. According to microscopic data, the morphology of the formed carbon nanofibers is affected by the alloy composition and by the nature of the used organic substrate.