Unraveling Ce3+ detection at the surface of ceria nanopowders by UPS analysis.

A sequential analysis using Ultra-violet Photoelectron Spectroscopy (UPS) and X-ray Photoelectron Spectroscopy (XPS) on ceria nanopowders has been implemented to identify the influence of the X-ray beam on the surface of this oxide. For the first time, UPS analysis evidenced the photoreductive effect of XPS analysis on ceria after an oxidative in situ pretreatment, leading to an overestimation of the Ce3+/Ce4+ ratio obtained by XPS. Based on this spectroscopy methodology, UPS imposes itself as a leading technique for analyzing powders with minimal impact on the authentic chemical state, thus paving the way for identifying the real ratio of Ce4+ and Ce3+ of ceria after oxidative and reductive in situ treatments.

Tuning the Structure of Platinum Particles on Ceria In†Situ for Enhancing the Catalytic Performance of Exhaust Gas Catalysts.

A dynamic structural behavior of Pt nanoparticles on the ceria surface under reducing/oxidizing conditions was found at moderate temperatures (<500 °C) and exploited to enhance the catalytic activity of Pt/CeO2 -based exhaust gas catalysts. Redispersion of platinum in an oxidizing atmosphere already occurred at 400 °C. A protocol with reducing pulses at 250-400 °C was applied in a subsequent step for controlled Pt-particle formation. Operando X-ray absorption spectroscopy unraveled the different extent of reduction and sintering of Pt particles: The choice of the reductant allowed the tuning of the reduction degree/particle size and thus the catalytic activity (CO>H2 >C3 H6 ). This dynamic nature of Pt on ceria at such low temperatures (250-500 °C) was additionally confirmed by in situ environmental transmission electron microscopy. A general concept is proposed to adjust the noble metal dispersion (size, structure), for example, during operation of an exhaust gas catalyst.

Nano-Structuration of WO3 Nanoleaves by Localized Hydrolysis of an Organometallic Zn Precursor: Application to Photocatalytic NO2 Abatement.

WO3 is a known photocatalytic metal oxide frequently studied for its depollution properties. However, it suffers from a high recombination rate of the photogenerated electron/holes pair that is detrimental to its performance. In this paper, we present a new chemical method to decorate WO3 nanoleaves (NLs) with a complementary metal oxide (ZnWO4) in order to improve the photocatalytic performance of the composite material for the abatement of 400 ppb NO2 under mild UV exposure. Our strategy was to synthesize WO3·2H2O nanoleaves, then, to expose them, in water-free organic solution, to an organometallic precursor of Zn(Cy)2. A structural water molecule from WO3·2H2O spontaneously decomposes Zn(Cy)2 and induces the formation of the ZnO@WO3·H2O nanocomposite. The material was characterized by electronic microscopy (SEM, TEM), TGA, XRD, Raman and solid NMR spectroscopies. A simple thermal treatment under air at 500 °C affords the ZnWO4@WO3 nanocomposite. The resulting material, additionally decorated with 1% wt. Au, presents a remarkable increase (+166%) in the photocatalytic abatement of NO2 under UV compared to the pristine WO3 NLs. This synthesis method paves the way to the versatile preparation of a wide range of MOx@WO3 nanocomposites (MOx = metal oxide).

Supported Cobalt Catalysts for Acceptorless Alcohol Dehydrogenation.

The acceptor-less dehydrogenation of 2-octanol was tested over cobalt supported on Al2 O3 , C, ZnO, ZrO2 and various TiO2 substrates. The catalysts were characterized by ICP, XRD and TGA-H2 . For Co/TiO2 P25, the effects of passivation, aging (storage at room temperature), and in situ activation under H2 were investigated. The catalysts must be tested shortly after synthesis in order to prevent deactivation. Cobalt supported on TiO2 P25 was the most active and 69 % yield of 2-octanone was obtained, using decane as a solvent. Selectivities for 2-octanone were observed in the range of 90 % to 99.9 %. Small amounts of C16 compounds were also formed due to aldol condensation/dehydration reactions. The catalysts exhibited higher conversion in the dehydrogenation of secondary alcohols (65-69 %), in comparison to primary alcohols (2-10 %). The dehydrogenation of 1,2-octanediol led to 1-hydroxy-2-octanone, with a selectivity of 90 % and 69 % for Co/TiO2 P25 and Co/TiO2 P90, respectively.

Structural characterization and oxidative dehydrogenation activity of V2O5/Ce(x)Zr(1-x)O2/SiO2 catalysts.

The thermal stability of a nanosized Ce(x)Zr(1-x)O2 solid solution on a silica surface and the dispersion behavior of V2O5 over Ce(x)Zr(1-x)O2/SiO2 have been investigated using XRD, Raman spectroscopy, XPS, HREM, and BET surface area techniques. Oxidative dehydrogenation of ethylbenzene to styrene was performed as a test reaction to assess the usefulness of the VOx/Ce(x)Zr(1-x)O2/SiO2 catalyst. Ce(x)Zr(1-x)O2/SiO2 (1:1:2 mol ratio based on oxides) was synthesized through a soft-chemical route from ultrahigh dilute solutions by adopting a deposition coprecipitation technique. A theoretical monolayer equivalent to 10 wt % V2O5 was impregnated over the calcined Ce(x)Zr(1-x)O2/SiO2 sample (773 K) by an aqueous wet impregnation technique. The prepared V2O5/Ce(x)Zr(1-x)O2/SiO2 sample was subjected to thermal treatments from 773 to 1073 K. The XRD measurements indicate the presence of cubic Ce0.75Zr0.25O2 in the case of Ce(x)Zr(1-x)O2/SiO2, while cubic Ce0.5Zr0.5O2 and tetragonal Ce0.16Zr0.84O2 in the case of V2O5/Ce(x)Zr(1-x)O2/SiO2 when calcined at various temperatures. Dispersed vanadium oxide induces more incorporation of zirconium into the ceria lattice, thereby decreasing its lattice size and also accelerating the crystallization of Ce-Zr-O solid solutions at higher calcination temperatures. Further, it interacts selectively with the ceria portion of the composite oxide to form CeVO4. The RS measurements provide good evidence about the dispersed form of vanadium oxide and the CeVO4 compound. The HREM studies show the presence of small Ce-Zr-oxide particles of approximately 5 nm size over the surface of amorphous silica and corroborate with the results obtained from other techniques. The catalytic activity studies reveal the ability of vanadium oxide supported on Ce(x)Zr(1-x)O2/SiO2 to efficiently catalyze the ODH of ethylbenzene at normal atmospheric pressure. The remarkable ability of Ce(x)Zr(1-x)O2 to prevent the deactivation of supported vanadium oxide leading to stable activity in the time-on-stream experiments and high selectivity to styrene are other important observations.

Structural characterization of nanosized CeO(2)-SiO(2), CeO(2)-TiO(2), and CeO(2)-ZrO(2) catalysts by XRD, Raman, and HREM techniques.

Structural characteristics of nanosized ceria-silica, ceria-titania, and ceria-zirconia mixed oxide catalysts have been investigated using X-ray diffraction (XRD), Raman spectroscopy, BET surface area, thermogravimetry, and high-resolution transmission electron microscopy (HREM). The effect of support oxides on the crystal modification of ceria cubic lattice was mainly focused. The investigated oxides were obtained by soft chemical routes with ultrahighly dilute solutions and were subjected to thermal treatments from 773 to 1073 K. The XRD results suggest that the CeO(2)-SiO(2) sample primarily consists of nanocrystalline CeO(2) on the amorphous SiO(2) surface. Both crystalline CeO(2) and TiO(2) anatase phases were noted in the case of CeO(2)-TiO(2) sample. Formation of cubic Ce(0.75)Zr(0.25)O(2) and Ce(0.6)Zr(0.4)O(2) (at 1073 K) were observed in the case of the CeO(2)-ZrO(2) sample. Raman measurements disclose the fluorite structure of ceria and the presence of oxygen vacancies/Ce(3+). The HREM results reveal well-dispersed CeO(2) nanocrystals over the amorphous SiO(2) matrix in the cases of CeO(2)-SiO(2), isolated CeO(2), and TiO(2) (anatase) nanocrystals, some overlapping regions in the case of CeO(2)-TiO(2), and nanosized CeO(2) and Ce-Zr oxides in the case of CeO(2)-ZrO(2) sample. The exact structural features of these crystals as determined by digital diffraction analysis of HREM experimental images reveal that the CeO(2) is mainly in cubic fluorite geometry. The oxygen storage capacity (OSC) as determined by thermogravimetry reveals that the OSC of the mixed oxide systems is more than that of pure CeO(2) and is system dependent.

Surface stabilized nanosized Ce(x)Zr(1-x)O(2) solid solutions over SiO(2): characterization by XRD, Raman, and HREM techniques.

Ce(x)Zr(1)(-)(x)O(2) solid solutions deposited over silica surface were investigated by X-ray diffraction (XRD), Raman spectroscopy (RS), and high-resolution transmission electron microscopy (HREM) techniques in order to understand the role of silica support and the temperature stability of these composite oxides. For the purpose of comparison, an unsupported Ce(x)Zr(1)(-)(x)O(2) was also synthesized and subjected to characterization by various techniques. The Ce(x)Zr(1)(-)(x)O(2)/SiO(2) (CZ/S) (1:1:2 mole ratio based on oxides) was synthesized by depositing Ce(x)Zr(1)(-)(x)O(2) solid solution over a colloidal SiO(2) support by a deposition precipitation method and unsupported Ce(x)Zr(1)(-)(x)O(2) (CZ) (1:1 mole ratio based on oxides) was prepared by a coprecipitation procedure, and the obtained catalysts were subjected to thermal treatments from 773 to 1073 K. The XRD measurements disclose the presence of cubic phases with the composition Ce(0.75)Zr(0.25)O(2) and Ce(0.6)Zr(0.4)O(2) in CZ samples, while CZ/S samples possess Ce(0.75)Zr(0.25)O(2), Ce(0.6)Zr(0.4)O(2), and Ce(0.5)Zr(0.5)O(2) in different proportions. The crystallinity of these phases increased with increasing calcination temperature. The cell a parameter estimations indicate contraction of ceria lattice due to the incorporation of zirconium cations into the CeO(2) unit cell. Raman measurements indicate the presence of oxygen vacancies, lattice defects, and displacement of oxygen ions from their normal lattice positions in both the series of samples. The HREM results reveal, in the case of CZ/S samples, a well-dispersed nanosized Ce-Zr-oxides over the surface of amorphous SiO(2). The structural features of these crystals as determined by digital diffraction analysis of experimental images reveal that the Ce-Zr-oxides are mainly in the cubic geometry and exhibit high thermal stability. Oxygen storage capacity measurements by a thermogravimetric method reveal a substantial enhancement in the oxygen vacancy concentration of CZ/S sample over the unsupported CZ sample.

One-pot synthesis of sub-3 nm gold nanoparticle networks connected by thio-based multidentate fullerene adducts.

A new organo-soluble [60]fullerene hexaadduct bearing twelve thiocyanate functions has been synthesized and successfully used as a stabilizing/assembling agent to assemble homogeneous sub-3 nm gold nanoparticles into extended tridimensional networks.

Selective conversion of {Mo132} Keplerate ion into 4-electron reduced crown-capped Keggin derivative [Te5Mo15O57](8-). A key intermediate to single-phase M1 multielement MoVTeO light-alkanes oxidation catalyst.

{Mo(132)} Keplerate anion reacts with tellurites to give a soluble precursor to produce in hydrothermal conditions single-phase M1 MoVTeO light-alkanes oxidation catalyst. Characterization of this Te-containing intermediate by single-crystal X-ray diffraction, (125)Te NMR, UV-visible and redox titration reveals a molybdotellurite anion as a crown-capped Keggin derivative.