Efficient 2075-nm laser emission from Ho3+-doped fluorotellurite glass in a compact all-fiber structure.

In this Letter, we report an Ho3+-doped fluorotellurite glass all-fiber laser at 2075 nm. The gain fiber is pumped in-band with a 1976-nm fiber laser and connected by fusion splicing. A high-quality fusion splicing point with a loss of < 0.1 dB was obtained by finely adjusting the splicing power and offset. In addition, by optimizing the writing parameters, a third-order fiber Bragg grating (FBG) with a reflectivity of 98% was achieved at 2075 nm using the femtosecond laser direct-writing method. Using the FBG as the laser cavity mirror and a relatively short 28-cm-long home-made Ho3+-doped fluorotellurite fiber as the laser medium, a laser with a maximum unsaturated output power of 7.33 W was obtained, and the corresponding slope efficiency was as high as 93.4%. The first, to the best of our knowledge, demonstration of the fluorotellurite glass all-fiber ∼2.1-µm laser presented in this work may pave the way for a high-power 2.1-µm fiber laser with a compact structure.

Direct femtosecond laser inscription of Bragg gratings in Ho3+/Pr3+ co-doped AlF3-based glass fibers for a 2.86†µm laser.

In this Letter, we report the fabrication of fiber Bragg gratings (FBGs) in home-made Ho3+/Pr3+ co-doped single-cladding fluoroaluminate (AlF3) glass fibers and its application in watt-level lasing at the mid-infrared (MIR) wavelength of 2.86 µm. The FBGs were inscribed using an 800 nm femtosecond (fs) laser direct-writing technique. The FBG properties were investigated for different pulse energies, inscription speeds, grating orders, and transversal lengths. A second-order FBG with a high reflectivity of 99% was obtained at one end of a 16.5-cm-long gain fiber. Under 1150 nm laser pumping, this fiber yielded a power exceeding 1 W at 2863.9 nm with an overall laser efficiency of 17.7%. The fiber laser showed a FWHM bandwidth of 0.46 nm and long-term spectral stability.