RESUMEN
We study important aspects of shape selectivity effects of zeolites for hydroisomerization of linear alkanes, which produces a myriad of isomers, particularly for long chain hydrocarbons. To investigate the conditions for achieving an optimal yield of branched hydrocarbons, it is important to understand the role of chemical equilibrium in these reversible reactions. We conduct an extensive analysis of shape selectivity effects of different zeolites for the hydroisomerization of C7 and C8 isomers at chemical reaction equilibrium conditions. The reaction ensemble Monte Carlo method, coupled with grand-canonical Monte Carlo simulations, is commonly used for computing reaction equilibrium of heterogeneous reactions. The computational demands become prohibitive for a large number of reactions. We used a faster alternative in which reaction equilibrium is obtained by imposing chemical equilibrium in the gas phase and phase equilibrium between the gas phase components and the adsorbed phase counterparts. This effectively mimics the chemical equilibrium distribution in the adsorbed phase. Using Henry's law at infinite dilution and mixture adsorption isotherm models at elevated pressures, we calculate the adsorbed loadings in the zeolites. This study shows that zeolites with cage or channel-like structures exhibit significant differences in selectivity for alkane isomers. We also observe a minimal impact of pressure on the gas-phase equilibrium of these reactions at typical experimental reaction temperatures 400-700K. This study marks initial strides in understanding the reaction product distribution for long-chain alkanes.
RESUMEN
Mesoporous zeolites are useful solid catalysts for conversion of bulky molecules because they offer fast mass transfer along with size and shape selectivity. We report here the successful synthesis of mesoporous aluminosilicate zeolite Beta from a commercial cationic polymer that acts as a dual-function template to generate zeolitic micropores and mesopores simultaneously. This is the first demonstration of a single nonsurfactant polymer acting as such a template. Using high-resolution electron microscopy and tomography, we discovered that the resulting material (Beta-MS) has abundant and highly interconnected mesopores. More importantly, we demonstrated using a three-dimensional electron diffraction technique that each Beta-MS particle is a single crystal, whereas most previously reported mesoporous zeolites are comprised of nanosized zeolitic grains with random orientations. The use of nonsurfactant templates is essential to gaining single-crystalline mesoporous zeolites. The single-crystalline nature endows Beta-MS with better hydrothermal stability compared with surfactant-derived mesoporous zeolite Beta. Beta-MS also exhibited remarkably higher catalytic activity than did conventional zeolite Beta in acid-catalyzed reactions involving large molecules.
RESUMEN
The separation of xylenes is one of the most important processes in the petrochemical industry. In this article, the competitive adsorption from a fluid-phase mixture of xylenes in zeolites is studied. Adsorption from both vapor and liquid phases is considered. Computations of adsorption of pure xylenes and a mixture of xylenes at chemical equilibrium in several zeolite types at 250 °C are performed by Monte Carlo simulations. It is observed that shape and size selectivity entropic effects are predominant for small one-dimensional systems. Entropic effects due to the efficient arrangement of xylenes become relevant for large one-dimensional systems. For zeolites with two intersecting channels, the selectivity is determined by a competition between enthalpic and entropic effects. Such effects are related to the orientation of the methyl groups of the xylenes. m-Xylene is preferentially adsorbed if xylenes fit tightly in the intersection of the channels. If the intersection is much larger than the adsorbed molecules, p-xylene is preferentially adsorbed. This study provides insight into how the zeolite topology can influence the competitive adsorption and selectivity of xylenes at reaction conditions. Different selectivities are observed when a vapor phase is adsorbed compared to the adsorption from a liquid phase. These insight have a direct impact on the design criteria for future applications of zeolites in the industry. MRE-type and AFI-type zeolites exclusively adsorb p-xylene and o-xylene from the mixture of xylenes in the liquid phase, respectively. These zeolite types show potential to be used as high-performing molecular sieves for xylene separation and catalysis.
RESUMEN
Dehydration of glucose to 5-hydroxymethylfurfural (HMF) remains a significant problem in the context of the valorization of lignocellulosic biomass. Hydrolysis of WCl6 and NbCl5 leads to precipitation of Nb-containing tungstite (WO3 â H2 O) at low Nb content and mixtures of tungstite and niobic acid at higher Nb content. Tungstite is a promising catalyst for the dehydration of glucose to HMF. Compared with Nb2 O5 , fewer by-products are formed because of the low Brønsted acidity of the (mixed) oxides. In water, an optimum yield of HMF was obtained for Nb-W oxides with low Nb content owing to balanced Lewis and Brønsted acidity. In THF/water, the strong Lewis acidity and weak Brønsted acidity caused the reaction to proceed through isomerization to fructose and dehydration of fructose to a partially dehydrated intermediate, which was identified by LC-ESI-MS. The addition of HCl to the reaction mixture resulted in rapid dehydration of this intermediate to HMF. The HMF yield obtained in this way was approximately 56 % for all tungstite catalysts. Density functional theory calculations show that the Lewis acid centers on the tungstite surface can isomerize glucose into fructose. Substitution of W by Nb lowers the overall activation barrier for glucose isomerization by stabilizing the deprotonated glucose adsorbate.
Asunto(s)
Furaldehído/análogos & derivados , Glucosa/química , Niobio/química , Óxidos/química , Tungsteno/química , Agua/química , Furaldehído/química , Teoría Cuántica , Solventes/químicaRESUMEN
Hierarchically porous SAPO-11 zeolite (H-SAPO-11) is rationally synthesized from a starting silicoaluminophosphate gel in the presence of polyhexamethylene biguanidine as a mesoscale template. The sample is well characterized by XRD, N2 sorption, SEM, TEM, NMR, XPS, NH3-TPD, and TG techniques. The results show that the sample obtained has good crystallinity, hierarchical porosity (mesopores at ca. 10 nm and macropores at ca. 50-200 nm), high BET surface area (226 m(2)/g), large pore volume (0.25 cm(3)/g), and abundant medium and strong acidic sites (0.36 mmol/g). After loading Pt (0.5 wt.%) on H-SAPO-11 by using wet impregnation method, catalytic hydroisomerization tests of n-dodecane show that the hierarchical Pt/SAPO-11 zeolite exhibits high conversion of n-dodecane and enhanced selectivity for branched products as well as reduced selectivity for cracking products, compared with conventional Pt/SAPO-11 zeolite. This phenomenon is reasonably attributed to the presence of hierarchical porosity, which is favorable for access of reactants on catalytically active sites. The improvement in catalytic performance in long-chain paraffin hydroisomerization over Pt/SAPO-11-based catalyst is of great importance for its industrial applications in the future.
RESUMEN
A novel synthetic route is designed, employing both high temperature and a nontoxic organic structure-directing agent (SDA), for the synthesis of high silica zeolite Y. The N-methylpyridinium used as an organic SDA is stable during the synthesis, and the high silica zeolite Y shows high hydrothermal stability and good catalytic performance, as well as excellent adsorptive properties.
RESUMEN
The most acidic OH groups in silica-aluminas (zeolites, clays, amorphous silica-aluminas) can be made to react selectively with C(6)D(6) to give acidic OD groups; quantification by IR spectroscopy shows that differences in the overall Brønsted acidity of aluminosilicates are dominated by differences in the density of sites of similar acid strength.