Calcium carbonate synthesis from Kambara reactor desulphurization slag via indirect carbonation for CO2 capture and utilization.

In this work, industrial Kambara reactor desulphurization slag (KR slag) was indirectly carbonated. The effects of leaching time, leaching temperature, leaching agent types, and leaching agent concentration on the leaching ratio of calcium from KR slag were investigated. Subsequently, precipitated calcium carbonate (PCC) was synthesized by bubbling CO2 gas (flow rate of 15 mL/min) into 400 mL leaching solutions at 40 °C for 120 min with magnetic stirring at 300 rpm. It is found that calcium in KR slag can be selectively extracted using a diluted solution of ammonium acetate (CH3COONH4) or ammonium chloride (NH4Cl), while ammonium sulfate ((NH4)2SO4) solution is not suitable as leaching agent due to the formation of slightly soluble calcium sulfate (CaSO4). The leaching ratio of calcium is improved by extending the leaching time or increasing the leaching solvent concentration. However, leaching temperature has little effect on calcium extraction. After carbonating the NH4Cl- and CH3COONH4-leachate for 120 min, calcite and vaterite type PCC with a purity of 99% is synthesized. Each gram of KR slag can produce 0.794 g and 0.803 g PCC using NH4Cl and CH3COONH4 leaching agents respectively. Calculations show that 349.6 kg CO2 is captured by per ton of KR slag. The CO2 capture capacity of KR slag is significantly higher compared with previously studied materials.

Unveiling Non-isothermal Crystallization of CaO-Al2O3-B2O3-Na2O-Li2O-SiO2 Glass via In Situ X-ray Scattering and Raman Spectroscopy.

The crystallization in glasses is a paradoxical phenomenon and scarcely investigated. This work explores the non-isothermal crystallization of a multicomponent alumino-borosilicate glass via in situ high-energy synchrotron X-ray diffraction, atomic pair distribution function, and Raman spectroscopy. Results depict the crystallization sequence as Ca3Al2O6 and CaSiO4 followed by LiAlO2 with the final compound formation of Ca3B2O6. These precipitations occur in a narrow temperature range and overlap, resulting in a single exothermic peak in the differential scanning calorimetry thermogram. The concurrent nucleation of Ca3Al2O6 and CaSiO4 is intermediated by their corresponding hydrates, which have dominantly short-range order. Moreover, the crystallization of LiAlO2 and Ca3B2O6 is strongly linked with the changes of structural units during the incubation stage in non-isothermal heating. These findings clarify the crystallization of multicomponent glass, which have been inferred from ex situ reports but never evidenced via in situ studies.

Synergetic valorization of basic oxygen furnace slag and stone coal: Metal recovery and preparation of glass-ceramics.

A synergetic valorization method was proposed to convert the basic oxygen furnace (BOF) slag and stone coal into ferroalloy and glass-ceramic in this work. Effects of reduction time, temperature, and the mass ratio of BOF slag to stone coal on the reduction were studied. The reduction mechanism was investigated by in-situ observation and dissolution experiments. The effect of sintering temperature on the properties of glass-ceramics prepared from the final slag was further studied. The in-situ observation results indicate that the reduction reactions occurred mainly in the temperature range of 1673-1793 K. The reduction ratio of oxides and size of metal droplets can be improved by increasing reduction time, temperature, and decreasing stone coal addition. The recovered ferroalloys consisted of Fe, Mn, P, and V, which has the potential of returning to the steelmaking process or extracting vanadium. The modified final slag was suitable material for preparing glass-ceramic. Wollastonite-based glass-ceramic with a maximum bending strength of 95.83 MPa was prepared, which could be applied as abrasion-resistant and building decoration materials. Therefore, the present technological route can convert two kinds of industrial solid waste into two kinds of cleaner products and achieve the target of "zero waste".