RESUMEN
The formation of an asymmetric junction is key to graphene-based photodetectors of high-sensitive photodetectability, because such a junction can not only facilitate the diffusion or drift of photogenerated carriers but also realize a self-powered operation. Here, a monolayer-multilayer graphene junction photodetector is accomplished by selectively thinning part of a multilayer graphene to a high-quality monolayer. Benefiting from the large photoabsorption cross section of multilayer graphene and strong asymmetry caused by the significant differences in optoelectronic properties between monolayer and multilayer graphene, the monolayer-multilayer graphene junction shows a 7-fold increase in short-circuit photocurrent as compared with that at the monolayer graphene-metal contact in scanning photocurrent images. The asymmetric configuration also enables the photodetector to work at zero bias with minimized dark current noise and stand-by power consumption. Under global illumination with visible light, a photoswitching ratio of 3.4 × 103, a responsivity of 8.8 mA W-1, a specific detectivity of 1.3 × 108Jones and a response time of 11 ns can be obtained, suggesting a promising photoresponse. Moreover, it is worth mentioning that such a performance enhancement is achieved without compromising the broadband spectral response of graphene photodetector and it is hence applicable for long wavelength spectral range including infrared and terahertz.
RESUMEN
Large-area high-quality graphene enabled by chemical vapor deposition (CVD) can possibly pave the path for advanced flexible electronics and spintronics. CVD-grown method utilizing liquid carbon precursor has recently been demonstrated as an appealing choice for mass graphene production, thanks to its low cost and safe operation. However, the quality of the graphene film has been the major obstacle for the implementation of the liquid-precursor-based CVD method. Here we report the growth of centimeter-scale easily-transferable single-layer graphene (SLG) using acetone as a liquid carbon precursor. The dry-transfer technique was used to prepare the graphene device. The typical mobility of the dry-transferred SLG device is as high as 12 500 cm2V-1s-1at room temperature. Thanks to the high quality of the device, the robust quantum Hall effect can survive up to room temperature. The excellent device quality also enables us to observe the Shubnikov-de Haas oscillation in the low magnetic field regime and systemically study the leading scattering mechanism. We extracted both the transport scattering timeτtand the quantum scattering timeτqover a wide range of carrier density. The ratio of the scattering times suggests that the charged-impurity resided near the surface of the graphene restricted the device performance.
RESUMEN
Precursors and catalysts play vital roles in chemical reactions. Considerable efforts have been devoted to the investigation of catalysts for graphene growth by chemical vapor deposition in recent years. However, there has been little research on precursors because of a lack of innovation in term of creating a controllable feeding method. Herein, we present a novel sustained and controlled release approach, and develop a convenient, safe, and potentially scalable feeding system with the assistance of matrix materials and a simple portable feeder. As a result, a highly volatile liquid precursor can be fed accurately to grow large-area, uniform graphene films with optimal properties. This feeding approach will further benefit the synthesis of other two-dimensional materials from various precursors.
RESUMEN
Chemical vapor deposition (CVD) is a widely used method for graphene synthesis, but it struggles to produce large-area uniform bilayer graphene (BLG). This study introduces a novel approach to meet the demands of large-scale integrated circuit applications, challenging the conventional reliance on uniform BLG over extensive areas. We developed a unique method involving the direct growth of bilayer graphene arrays (BLGA) on Cu foil substrates using patterned titanium (Ti) as a diffusion barrier. The use of the Ti layer can effectively control carbon atom diffusion through the Cu foil without altering the growth conditions or compromising the graphene quality, thereby showcasing its versatility. The approach allows for targeted BLG growth and achieved a yield of 100% for a 10 × 10 BLG units array. Then a 10 × 10 BLG memristor array was fabricated, and a yield of 96% was achieved. The performances of these devices show good uniformity, evidenced by the set voltages concentrated around 4 V, and a high resistance state (HRS) to low resistance state (LRS) ratio predominantly around 107, reflecting the spatial uniformity of the prepared BLGA. This study provides insight into the BLG growth mechanism and opens new possibilities for BLG-based electronics.