Vapor-Phase-Deposited Ag/Ir and Ag/Au Film Heterostructures for Implant Materials: Cytotoxic, Antibacterial and Histological Studies.

Using gas-phase deposition (Physical Vapor Deposition (PVD) and Metal Organic Chemical Vapor Deposition (MOCVD)) methods, modern implant samples (Ti alloy and CFR-PEEK polymer, 30% carbon fiber) were functionalized with film heterostructures consisting of an iridium or gold sublayer, on the surface of which an antibacterial component (silver) was deposited: Ag/Ir(Au)/Ti(CFR-PEEK). The biocidal effect of the heterostructures was investigated, the effect of the surface relief of the carrier and the metal sublayer on antibacterial activity was established, and the dynamics of silver dissolution was evaluated. It has been shown that the activity of Ag/Ir heterostructures was due to high Ag+ release rates, which led to rapid (2-4 h) inhibition of P. aeruginosa growth. In the case of Ag/Au type heterostructures, the inhibition of the growth of P. aeruginosa and S. aureus occurred more slowly (from 6 h), and the antibacterial activity appeared to be due to the contribution of two agents (Ag+ and Au+ ions). It was found, according to the in vitro cytotoxicity study, that heterostructures did not exhibit toxic effects (cell viability > 95-98%). An in vivo biocompatibility assessment based on the results of a morphohistological study showed that after implantation for a period of 30 days, the samples were characterized by the presence of a thin fibrous capsule without volume thickening and signs of inflammation.

Potassium and Cesium Fluorinated ß-Diketonates: Effect of a Cation and Terminal Substituent on Structural and Thermal Properties.

As potential precursors for the synthesis of fluoroperovskites, a family of heavy alkali metal (MI = K, Cs) fluorinated ß-diketonates were prepared and characterized by elemental analysis, IR, and powder-XRD. The crystal structures of the new six complexes, MI(ß-dikF)(H2O)X, X = 0 or 1, were also determined. The structural diversity of this poorly explored class of complexes was discussed, including the preferred types of cation polyhedra and the ligand coordination modes, and the thermal properties of the metal ß-diketonates were studied by TG-DTA in an inert (He) atmosphere. The data obtained allowed us to reveal the effect of the metal cation and the terminal substituent on the structural and thermal features of this family of complexes.

Structural Diversity of Silver Fluorinated ß-Diketonates: Effect of the Terminal Substituent and Solvent.

In order to demonstrate the role of the fluorination and some solvents in the structural organization of the Ag(I) coordination polymers with ß-diketonate ligands (R1C(O)CαHC(O)R2)- we synthesized a series of the compounds containing tfac- (R1 = CH3, R2 = CF3) and pfpac- (R1 = CH3, R2 = C2F5) anions. Solvent-free [Ag(L)]∞ (L = tfac 1, pfpac 2) compounds and the corresponding acetonitrile and toluene adducts have been characterized by elemental analysis and/or NMR, IR and single-crystal XRD. This series includes five new coordination polymers. Compound 1 is a 3D coordination framework based on Ag-Ochelate/bridge, Ag-Cα bonds, and argentophilic interactions. An increase in the fluorinated group leads to a chain coordination polymer 2 of an unusual structural organization. These chains can be represented as a "DNA-type", where two intertwined helices based on Ag-Ochelate and Ag-Cα bonds are connected through Ag-Obridge ones. Two structural types of chain coordination polymers, [Ag(tfac)(CH3CN)] and [Ag2(L)2(solvent)], have been revealed for the adducts. The latter structural type differs significantly from the previously studied toluene and acetonitrile adducts of fluorinated Ag(I) ß-diketonates of the same stoichiometry. Thermal analysis in helium showed that both 1 and 2 decompose to metallic silver with the compound of pfpac-ligand being slightly more stable.

"Vitruvian" precursor for gas phase deposition: structural insights into iridium ß-diketonate volatilities.

New data on the thermodynamic properties of the melting and sublimation of a series of volatile iridium(i) complexes [Ir(cod)(L)] with cyclooctadiene-1,5 (cod) and ß-diketones (L = RC(O)CHC(O)R') have been obtained with differential scanning calorimetry and vapor pressure measurements. Combining experimental, empirical and theoretical methods, ways to estimate difference in heat capacities between gas and crystal phases have been suggested. An effect on the volatility in introducing the simplest alkyl, fluorinated alkyl and aryl terminal groups (R and R') into the chelate ligand has been explained in terms of a detailed crystal packing analysis supported by a quantum chemical calculation of crystal lattice energies. To reveal the influence of the coordination center, the thermal behavior of complexes was compared with that for the tris-chelates, [Ir(L)3]. The study broadens our understanding of relationships between the structure and thermal properties of volatile precursors, which is useful for further tuning effective compounds for metal-organic chemical vapor deposition purposes.

Invisible Surface Oxygen Vacancies in a Thin MgO Film: Impacts on the Chemical Activity and Secondary Electron Emission.

Today, Fs defects in MgO as isolated surface neutral oxygen vacancies are in the focus of surface science, catalysis research, and emission coating of microchannel plates. With the 10-4 atom % content at 750 K and under pO2 = 10-9 Torr, estimated by us from the known equilibrium T-x and p-T-x diagrams of MgO, Fs defects remain invisible or difficult-to-detect objects. The MgO(100) → MgO(100) + Fs + 1/2O2 phase transition was studied in MgO films deposited by the metal-organic chemical vapor deposition (MOCVD) procedure from the mixed-ligand Mg precursor on Si substrates at 725 K in the O2 flow where the nonstoichiometric phase (MgO/Fs) is formed in the gas medium containing simultaneous H2, CO, H2O, CO, and O2 species in unbalanced concentrations. Realization of the above transition was proven theoretically and experimentally through kinetic-thermodynamic analysis of the nonequilibrium system with revealing thermodynamic motive forces, i.e., the positive enthalpy and entropy, as well as through a new combination of diagnostic methods including the original differential dissolution method, due to which separate determination of the point and morphological defects was achieved. It was found that Fs defects occur when oxygen in the immediate vicinity to the substrate surface is replaced practically completely by the oxidized products of the precursor and the resulting oxygen pressure becomes enough for this process. The 90 mass % of the as-deposited MgO-film-involved (MgO/Fs) phase; its chemical activity is demonstrated through dissolution in hot water, while the electron donor activity is through 9 at 750 eV secondary electron yield. A good understanding of gas-phase reactions between the precursors and oxygen provides the fundamental basis of the MOCVD process to deposit MgO films that are dense, free from carbon, and of homogeneous texture. This makes the MOCVD process suitable also for use as coatings of microchannel plates.

Bimetallic Pt,Ir-containing coatings formed by MOCVD for medical applications.

Biocompatible PtxIr(1-x) layers combining high mechanical strength of the iridium component and outstanding corrosion resistance of the platinum component providing reversible charge transfer reactions in the living tissue are one of the important materials required for implantable medical electrodes. The modern trend to complicate the shape and reduce the electrode dimensions includes the challenge to develop precise methods to obtain such bimetallic coatings with enhanced surface area and advanced electrochemical characteristics. Herein, PtxIr(1-x) coatings were firstly obtained on cathode and anode pole tips of endocardial electrodes for pacemakers using chemical vapor deposition technique. To deposit PtxIr(1-x) coatings with a wide range of metal ratios (x = 0.5-0.9) the combination of acetylacetonate-based volatile precursors with compatible thermal characteristics was used for the first time. The expected metal ratio in the coatings was regulated by a partial pressure of the precursor vapors in the reaction zone and was in the good agreement with its real value measured by various methods, including energy-dispersive and wavelength dispersive spectroscopy, X-ray photoelectron spectroscopy. According to the X-ray powder diffraction analysis, PtxIr(1-x) coatings consisted of fcc-PtxIr(1-x) solid solution phases. The microscopy data confirmed the formation of PtxIr1-x coatings with the enhanced surface areas. The effect of electrochemical activation on the surface composition and morphology of the samples was studied. The electrochemical characteristics of samples were estimated from cyclic voltammetry and electrochemical impedance spectroscopy data. The charge storage capacity (CSC) values of activated samples were in the range of 19-108 mCcm-2 (phosphate buffer saline solution, 100 mV/s).

Biological Studies of New Implant Materials Based on Carbon and Polymer Carriers with Film Heterostructures Containing Noble Metals.

This paper presents pioneering results on the evaluation of noble metal film hetero-structures to improve some functional characteristics of carbon-based implant materials: carbon-composite material (CCM) and carbon-fiber-reinforced polyetheretherketone (CFR-PEEK). Metal-organic chemical vapor deposition (MOCVD) was successfully applied to the deposition of Ir, Pt, and PtIr films on these carriers. A noble metal layer as thin as 1 µm provided clear X-ray imaging of 1−2.5 mm thick CFR-PEEK samples. The coated and pristine CCM and CFR-PEEK samples were further surface-modified with Au and Ag nanoparticles (NPs) through MOCVD and physical vapor deposition (PVD) processes, respectively. The composition and microstructural features, the NPs sizes, and surface concentrations were determined. In vitro biological studies included tests for cytotoxicity and antibacterial properties. A series of samples were selected for subcutaneous implantation in rats (up to 3 months) and histological studies. The bimetallic PtIr-based heterostructures showed no cytotoxicity in vitro, but were less biocompatible due to a dense two-layered fibrous capsule. AuNP heterostructures on CFR-PEEK promoted cell proliferation in vitro and exhibited a strong inhibition of bacterial growth (p < 0.05) and high in vitro biocompatibility, especially Au/Ir structures. AgNP heterostructures showed a more pronounced antibacterial effect, while their in vivo biocompatibility was better than that of the pristine CFR-PEEK, but worse than that of AuNP heterostructures.

Noble Metals for Modern Implant Materials: MOCVD of Film Structures and Cytotoxical, Antibacterial, and Histological Studies.

This work is aimed at developing the modification of the surface of medical implants with film materials based on noble metals in order to improve their biological characteristics. Gas-phase transportation methods were proposed to obtain such materials. To determine the effect of the material of the bottom layer of heterometallic structures, Ir, Pt, and PtIr coatings with a thickness of 1.4-1.5 µm were deposited by metal-organic chemical vapor deposition (MOCVD) on Ti6Al4V alloy discs. Two types of antibacterial components, namely, gold nanoparticles (AuNPs) and discontinuous Ag coatings, were deposited on the surface of these coatings. AuNPs (11-14 nm) were deposited by a pulsed MOCVD method, while Ag films (35-40 nm in thickness) were obtained by physical vapor deposition (PVD). The cytotoxic (24 h and 48 h, toward peripheral blood mononuclear cells (PBMCs)) and antibacterial (24 h) properties of monophase (Ag, Ir, Pt, and PtIr) and heterophase (Ag/Pt, Ag/Ir, Ag/PtIr, Au/Pt, Au/Ir, and Au/PtIr) film materials deposited on Ti-alloy samples were studied in vitro and compared with those of uncoated Ti-alloy samples. Studies of the cytokine production by PBMCs in response to incubation of the samples for 24 and 48 h and histological studies at 1 and 3 months after subcutaneous implantation in rats were also performed. Despite the comparable thickness of the fibrous capsule after 3 months, a faster completion of the active phase of encapsulation was observed for the coated implants compared to the Ti alloy analogs. For the Ag-containing samples, growth inhibition of S. epidermidis, S. aureus, Str. pyogenes, P. aeruginosa, and Ent. faecium was observed.