Synthesis of non-planar graphene-wrapped copper nanoparticles with iron(III) oxide decoration for high performance supercapacitors.

The performance of supercapacitors strongly depends on the electrochemical characterizations of electrode materials. Herein, a composite material consisted of iron(III) oxide (Fe2O3) and multilayer graphene-wrapped copper nanoparticles (Fe2O3/MLG-Cu NPs) is fabricated on a flexible carbon cloth (CC) substrate via two-step synthesis process for supercapacitor application. Where, MLG-Cu NPs are prepared on CC by one-step chemical vapor deposition synthesis approach; thereafter, the Fe2O3is further deposited on the MLG-Cu NPs/CC via successive ionic layer adsorption and reaction method. The related material characterizations of Fe2O3/MLG-Cu NPs are well investigated by scanning electron microscopic, high resolution transmission electron microscopy), Raman spectrometer and X-ray photoelectron spectroscopy; the electrochemical behaviors of the pertinent electrodes are studied by cyclic voltammogram, galvanostatic charge/discharge (GCD) and electrochemical impedance spectroscopy measurements. The flexible electrode with Fe2O3/MLG-Cu NPs composites exhibits the best specific capacitance of 1092.6 mF cm-2at 1 A g-1, which is much higher than those of electrodes with Fe2O3(863.7 mF cm-2), MLG-Cu NPs (257.4 mF cm-2), multilayer graphene hollow balls (MLGHBs, 14.4 mF cm-2) and Fe2O3/MLGHBs (287.2 mF cm-2). Fe2O3/MLG-Cu NPs electrode also exhibits an excellent GCD durability, and its capacitance remains 88% of its original value after 5000 cycles of the GCD process. Finally, a supercapacitor system consisted of four Fe2O3/MLG-Cu NPs/CC electrodes can efficiently power various light-emitting diodes (i.e. red, yellow, green, and blue lights), demonstrating the practical application of Fe2O3/MLG-Cu NPs/CC electrode.

Polypyrrole-coated copper@graphene core-shell nanoparticles for supercapacitor application.

The performance of supercapacitors strongly depends on the electrochemical characterizations of electrode materials. Herein, a composite material consisted of polypyrrole (PPy) and multilayer graphene-wrapped copper nanoparticles (PPy/MLG-Cu NPs) is fabricated on a flexible carbon cloth (CC) substrate via two-step synthesis process for supercapacitor application. Where, MLG-Cu NPs are prepared on CC by one-step chemical vapor deposition synthesis approach; thereafter, the PPy is further deposited on the MLG-Cu NPs/CC via electropolymerization. The related material characterizations of PPy/MLG-Cu NPs are well investigated by scanning electron microscopic, high resolution transmission electron microscopy, Raman spectrometer and x-ray photoelectron spectroscopy; the electrochemical behaviors of the pertinent electrodes are studied by cyclic voltammogram, galvanostatic charge/discharge and electrochemical impedance spectroscopy measurements. The flexible electrode with PPy/MLG-Cu NPs composites exhibits the best specific capacitance of 845.38 F g-1at 1 A g-1, which is much higher than those of electrodes with PPy (214.30 F g-1), MLG-Cu NPs (6.34 F g-1), multilayer graphene hollow balls (MLGHBs; 52.72 F g-1), and PPy/MLGHBs (237.84 F g-1). Finally, a supercapacitor system consisted of four PPy/MLG-Cu NPs/CC electrodes can efficiently power various light-emitting diodes (i.e. red, yellow, green and blue lighs), demonstrating the practical application of PPy/MLG-Cu NPs/CC electrode.