RESUMEN
Insertion polynorbornenes (PBNEs) are rigid-rod polymers that have very high glass transition temperatures (Tg). In this study, two functional PNBEs were electrospun in the presence of a variety of cross-linkers, resulting in fibers with Tgs greater than 300 °C. The fibers are long (several mm), rigid, and with diameters that can be tuned in the range 300 nm-10 µm. The electrospinning process can be used to encapsulate dyes or graphene dots. Due to the high cross-linking density of the fiber, dye leaching is prevented. In contrast with other rigid-rod polymers, electrospinning of PNBE is facile and can be performed at injection rates as high as 1 mL/min.
RESUMEN
Norbornene can be polymerized by a variety of mechanisms, including insertion polymerization whereby the double bond is polymerized and the bicyclic nature of the monomer is conserved. The resulting polymer, polynorbornene, has a very high glass transition temperature, Tg, and interesting optical and electrical properties. However, the polymerization of functional norbornenes by this mechanism is complicated by the fact that the endo substituted norbornene monomer has, in general, a very low reactivity. Furthermore, the separation of the endo substituted monomer from the exo monomer is a tedious task. Here, we present a simple protocol for the polymerization of substituted norbornenes (endo:exo ca. 80:20) bearing either a carboxylic acid or a pendant double bond. The process does not require that both isomers be separated, and proceeds with low catalyst loadings (0.01 to 0.02 mol%). The polymer bearing pendant double bonds can be further transformed in high yield, to afford a polymer bearing pendant epoxy groups. These simple procedures can be applied to prepare polynorbornenes with a variety of functional groups, such as esters, alcohols, imides, double bonds, carboxylic acids, bromo-alkyls, aldehydes and anhydrides.