In Situ Construction of Highly Dispersed Pd on Cobalt Nanoparticle on Hollow Functional Cubic Graphene by Double Framework for ORR.

Developing advanced functional carbon materials is essential for electrocatalysis, caused by their vast merits for boosting many key energy conversion reactions. Herein, the covalent organic frameworks (COFs) is utilized on metal-organic frameworks (MOFs) as the template, under the controllable metal atoms thermal migration process successfully in situ constructs Pd-Co alloy nanoparticles on hollow cubic graphene. The electrocatalytic oxygen reduction reaction (ORR) evaluation showed excellent performances with a half-wave potential of 0.866 V, and a limited current density of 4.975 mA cm-2, that superior to the commercial Pt/C and Co nanoparticles. The contrast experiments and X-ray absorption spectrum demonstrated the aggregated electrons at highly dispersed Pd atoms on Co nanoparticle that promoted the main activities. This work not only enlightens the novel carbon materials designing strategies but also suggests heterogeneous electrocatalysis.

Cu@Co with Dilatation Strain for High-Performance Electrocatalytic Reduction of Low-Concentration Nitric Oxide.

Electrocatalytic reduction of nitric oxide (NO) to ammonia (NH3 ) is a clean and sustainable strategy to simultaneously remove NO and synthesize NH3 . However, the conversion of low concentration NO to NH3 is still a huge challenge. In this work, the dilatation strain between Cu and Co interface over Cu@Co catalyst is built up and investigated for electroreduction of low concentration NO (volume ratio of 1%) to NH3 . The catalyst shows a high NH3 yield of 627.20 µg h-1 cm-2 and a Faradaic efficiency of 76.54%. Through the combination of spherical aberration-corrected transmission electron microscopy and geometric phase analyses, it shows that Co atoms occupy Cu lattice sites to form dilatation strain in the xy direction within Co region. Further density functional theory calculations and NO temperature-programmed desorption (NO-TPD) results show that the surface dilatation strain on Cu@Co is helpful to enhance the NO adsorption and reduce energy barrier of the rate-determining step (*NO to *NOH), thereby accelerating the catalytic reaction. To simultaneously realize NO exhaust gas removal, NH3 green synthesis, and electricity output, a Zn-NO battery with Cu@Co cathode is assembled with a power density of 3.08 mW cm-2 and an NH3 yield of 273.37 µg h-1 cm-2 .