RESUMEN
We report on the synthesis, crystal, and electronic structure, as well as the magnetic, and electric properties of the phosphorus-containing tantalum nitride P1-xTa8+xN13 (x = 0.1-0.15). A high-pressure high-temperature reaction (8 GPa, 1400 °C) of Ta3N5 and P3N5 with NH4F as a mineralizing agent yields the compound in the form of black, rod-shaped crystals. Single-crystal X-ray structure elucidation (space group C2/m (no. 12), a = 16.202(3), b = 2.9155(4), c = 11.089(2) Å, ß = 126.698(7)°, Z = 2) shows a network of face- and edge-sharing Ta-centered polyhedra that contains small vacant channels and PN6 octahedra strands. Atomic resolution transmission electron microscopy reveals an unusual P/Ta disorder. Mixed-valent tantalum atoms exhibit interatomic distances similar to those in metallic tantalum, however, the electrical resistivity is quite high in the order of 101 Ω cm. The density of states and the electron localization function indicate localized electrons in both covalent and ionic bonds between P/Ta and N atoms, combined with less localized electrons that do not contribute to interatomic bonds.
RESUMEN
Tetrahedron-based nitrides offer a wide range of properties and applications. Highly condensed nitridophosphates are examples of nitrides that exhibit fascinating luminescence properties when doped with Eu2+, making them appealing for industrial applications. Here, we present the first nitridomagnesophosphate solid solution series Ba3-xSrx[Mg2P10N20] : Eu2+ (x=0-3), synthesized by a high-pressure high-temperature approach using the multianvil technique (3â GPa, 1400 °C). Starting from the binary nitrides P3N5 and Mg3N2 and the respective alkaline earth azides, we incorporate Mg into the P/N framework to increase the degree of condensation κ to 0.6, the highest observed value for alkaline earth nitridophosphates. The crystal structure was elucidated by single-crystal X-ray diffraction, powder X-ray diffraction, energy-dispersive X-ray spectroscopy (EDX), and solid-state NMR. DFT calculations were performed on the title compounds and other related highly condensed nitridophosphates to investigate the influence of Mg in the P/N network. Eu2+-doped samples of the solid solution series show a tunable narrow-band emission from cyan to green (492-515â nm), which is attributed to the preferred doping of a single crystallographic site. Experimental confirmation of this assumption was provided by overdoping experiments and STEM-HAADF studies on the series as well on the stoichiometric compound Ba2Eu[Mg2P10N20] with additional atomic resolution energy-dispersive X-ray spectroscopy (EDX) mapping.
RESUMEN
A series of isostructural imidonitridophosphates AE2AlP8N15(NH) (AE=Ca, Sr, Ba) was synthesized at high-pressure/high-temperature conditions (1400 °C and 5-9 GPa) from alkaline-earth metal nitrides or azides Ca3N2/Sr(N3)2/Ba(N3)2 and the binary nitrides AlN and P3N5. NH4F served as a hydrogen source and mineralizing agent. The crystal structures were determined by single-crystal X-ray diffraction and feature a three-dimensional network of vertex-sharing PN4-tetrahedra forming diverse-sized rings that are occupied by aluminum and alkaline earth ions. These structures represent another example of nitridophosphate-based networks that simultaneously incorporate AlN6-octahedra and alkaline-earth-centered polyhedra, with aluminum not participating in the tetrahedra network. They differ from previously reported ones by incorporating non-condensed octahedra instead of strongly condensed octahedra units and contribute to the diversity of multicationic nitridophosphate network structures. The results are supported by atomic resolution EDX mapping, solid-state NMR and FTIR measurements. Eu2+-doped samples show strong luminescence with narrow emissions in the range of green to blue under UV excitation, marking another instance of Eu2+-luminescence within imidonitridophosphates.
RESUMEN
The first nitridic analog of an amphibole mineral, the quaternary nitridosilicate phosphate Cr5.7Si2.3P8N24 was synthesized under high-pressure high-temperature conditions at 1400 °C and 12â GPa from the binary nitrides Cr2N, Si3N4 and P3N5, using NH4N3 and NH4F as additional nitrogen source and mineralizing agent, respectively. The crystal structure was elucidated by single-crystal X-ray diffraction with microfocused synchrotron radiation (C2/m, a=9.6002(19), b=17.107(3), c=4.8530(10)â Å, ß=109.65(3)°). The elemental composition was analyzed by energy dispersive X-ray spectroscopy. The structure consists of vertex-sharing PN4-tetrahedra forming zweier double chains and edge-sharing (Si,Cr)-centered octahedra forming separated ribbons. Atomic resolution scanning transmission electron microscopy shows ordered Si and Cr sites next to a disordered Si/Cr site. Optical spectroscopy indicates a band gap of 2.1â eV. Susceptibility measurements show paramagnetic behavior and support the oxidation state Cr+IV, which is confirmed by EPR. The comprehensive analysis expands the field of Cr-N chemistry and provides access to a nitride analog of one of the most prevalent silicate structures.
RESUMEN
In this work, we present the synthesis, characterization, and optical properties of Sr5Si7P2N16:Eu2+, the first tetrahedral (Si,P)-N network in which Si occupies more than 50% of the tetrahedra. While past studies have shown progress with anionic (Si,P)-N networks, the potential of silicon-rich compounds remains untapped. The synthesized compound Sr5Si7P2N16 exhibits a unique mixture of substitutional order and positional disorder within its network. The analytical challenges posed by the similarities between Si4+ and P5+, along with the network's disorder, were overcome by combining single-crystal X-ray diffraction and scanning transmission electron microscopy EDX mapping. Low-cost crystallographic calculations provided additional insights into the identification of tetrahedral occupations in mixed networks. Luminescence investigations on Sr5Si7P2N16:Eu2+ revealed yellow emission, adding to the known blue, green, and orange emission maxima of Sr-(Si,P)-N networks, highlighting the variability of such compounds.