Fast Outer-Sphere Electron Transfer and High Specific Capacitance at Covalently Modified Carbon Electrodes.

Carbon electrodes typically display sluggish electron transfer kinetics due to the adsorption of adventitious molecules that effectively insulate the surface. Here, we describe a method for rendering graphitic carbon electrodes permanently hydrophilic by functionalization with 4-(diazonium)benzenesulfonic acid. In aqueous electrolytes, these hydrophilic carbon electrodes exhibit metal-like specific capacitance (∼40 µF/cm2) as measured by cyclic voltammetry, suggesting a change in the double-layer structure at the carbon surface. Additionally, the modified electrodes show fast charge transfer kinetics to outer-sphere one-electron redox couples such as ferro-/ferricyanide as well as improved electron transfer kinetics in alkaline aqueous redox flow batteries.

Electron Transfer Dynamics at Dye-Sensitized SnO2/TiO2 Core/Shell Electrodes in Aqueous/Nonaqueous Electrolyte Mixtures.

The dynamics of photoinduced electron transfer were measured at dye-sensitized photoanodes in aqueous (acetate buffer), nonaqueous (acetonitrile), and mixed solvent electrolytes by nanosecond transient absorption spectroscopy (TAS) and ultrafast optical-pump terahertz-probe spectroscopy (OPTP). Higher injection efficiencies were found in mixed solvent electrolytes for dye-sensitized SnO2/TiO2 core/shell electrodes, whereas the injection efficiency of dye-sensitized TiO2 electrodes decreased with the increasing acetonitrile concentration. The trend in injection efficiency for the TiO2 electrodes was consistent with the solvent-dependent trend in the semiconductor flat band potential. Photoinduced electron injection in core/shell electrodes has been understood as a two-step process involving ultrafast electron trapping in the TiO2 shell followed by slower electron transfer to the SnO2 core. The driving force for shell-to-core electron transfer increases as the flat band potential of TiO2 shifts negatively with increasing concentrations of acetonitrile. In acetonitrile-rich electrolytes, electron injection is suppressed due to the very negative flat band potential of the TiO2 shell. Interestingly, a net negative photoconductivity in the SnO2 core is observed in mixed solvent electrolytes by OPTP. We hypothesize that an electric field is formed across the TiO2 shell from the oxidized dye molecules after injection. Conduction band electrons in SnO2 are trapped at the core/shell interface by the electric field, resulting in a negative photoconductivity transient. The overall electron injection efficiency of the dye-sensitized SnO2/TiO2 core/shell photoanodes is optimized in mixed solvents. The ultrafast transient conductivity data illustrate the crucial role of the electrolyte in regulating the driving forces for electron injection and charge separation at dye-sensitized semiconductor interfaces.

Selective Covalent Basal Plane Modification as a Probe of Hydroxide Ion Conduction Pathways in Magnesium Aluminum Layered Double Hydroxides.

Understanding ionic conduction in layered double hydroxides (LDHs) is a crucial step towards utilizing them as solid, hydroxide ion-conducting electrolytes in energy conversion applications. We selectively modified the interlayer and external surfaces of MgAl LDHs with tris(hydroxymethyl)aminomethane (TRIS) ligands. By adjusting the concentration of the TRIS surface modifier, the LDH basal plane surfaces could be functionalized everywhere (internally and externally) or only externally. External modification resulted in loss of OH-conductivity compared to pristine LDHs, confirming that external platelet surfaces are the primary ion conduction pathway.