Surface activation of Hastalex by vacuum argon plasma for cytocompatibility enhancement.

Here, we present surface analysis and biocompatibility evaluation of novel composite material based on graphene oxide traded as Hastalex. First, the surface morphology and elemental analysis of the pristine material were examined by atomic force and scanning electron microscopies, and by energy-dispersive and X-ray photoelectron spectroscopies, respectively. The Hastalex surface was then modified by plasma (3 and 8 W with exposure times up to 240 s), the impact of which on the material surface wettability and morphology was further evaluated. In addition, the material aging was studied at room and elevated temperatures. Significant changes in surface roughness, morphology, and area were detected at the nanometer scale after plasma exposure. An increase in oxygen content due to the plasma exposure was observed both for 3 and 8 W. The plasma treatment had an outstanding effect on the cytocompatibility of Hastalex foil treated at both input powers of 3 and 8 W. The cell number of human MRC-5 fibroblasts on Hastalex foils exposed to plasma increased significantly compared to pristine Hastalex and even to tissue culture polystyrene. The plasma exposure also affected the fibroblasts' cell growth and shape.

Design of polar self-assembling lactic acid derivatives possessing submicrometre helical pitch.

Several new lactic acid derivatives containing the keto linkage group far from the chiral part and short alkyl chains have been synthesized and characterised by polarising optical microscopy, differential scanning calorimetry, as well as electro-optic and dielectric spectroscopy. The materials possess a self-assembling behaviour on the nanoscale level as they form polar smectic liquid crystalline mesophases, namely the orthogonal paraelectric SmA* and the tilted ferroelectric SmC* phases, in a broad temperature range down to room temperature. A short helical pitch (≈120-320 nm), relatively high spontaneous polarisation (≈150 nC/cm2) and reasonable tilt angle values have been determined within the temperature range of the tilted ferroelectric SmC* phase. The obtained results make the new materials useful for the advanced mixture design and for further utilisation in electro-optic devices based on the deformed helix ferroelectric effect.