RESUMEN
Titanium oxynitride (TiOxNy) thin films are fabricated using reactive magnetron sputtering. The mechanism of their growth formation is explained, and their optical properties are presented. The films grown when the level of residual oxygen in the background vacuum was between 5 nTorr to 20 nTorr exhibit double epsilon-near-Zero (2-ENZ) behavior with ENZ1 and ENZ2 wavelengths tunable in the 700-850 and 1100-1350 nm spectral ranges, respectively. Samples fabricated when the level of residual oxygen in the background vacuum was above 2 × 10-8 Torr exhibit nonmetallic behavior, while the layers deposited when the level of residual oxygen in the background vacuum was below 5 × 10-9 Torr show metallic behavior with a single ENZ value. The double ENZ phenomenon is related to the level of residual oxygen in the background vacuum and is attributed to the mixture of TiN and TiOxNy and TiOx phases in the films. Varying the partial pressure of nitrogen during the deposition can further control the amount of TiN, TiOx, and TiOxNy compounds in the films and, therefore, tune the screened plasma wavelengths. A good approximation of the ellipsometric behavior is achieved with Maxwell-Garnett theory for a composite film formed by a mixture of TiO2 and TiN phases suggesting that double ENZ TiOxNy films are formed by inclusions of TiN within a TiO2 matrix. These oxynitride compounds could be considered as new materials exhibiting double ENZ in the visible and near-IR spectral ranges. Materials with ENZ properties are advantageous for designing the enhanced nonlinear optical response, metasurfaces, and nonreciprocal behavior.
RESUMEN
Hyperbolic metamaterials comprised of an array of plasmonic nanorods provide a unique platform for designing optical sensors and integrating nonlinear and active nanophotonic functionalities. In this work, the waveguiding properties and mode structure of planar anisotropic metamaterial waveguides are characterized experimentally and theoretically. While ordinary modes are the typical guided modes of the highly anisotropic waveguides, extraordinary modes, below the effective plasma frequency, exist in a hyperbolic metamaterial slab in the form of bulk plasmon-polaritons, in analogy to planar-cavity exciton-polaritons in semiconductors. They may have very low or negative group velocity with high effective refractive indices (up to 10) and have an unusual cut-off from the high-frequency side, providing deep-subwavelength (λ0/6-λ0/8 waveguide thickness) single-mode guiding. These properties, dictated by the hyperbolic anisotropy of the metamaterial, may be tuned by altering the geometrical parameters of the nanorod composite.
RESUMEN
Several new plasmonic materials have recently been introduced in order to achieve better temperature stability than conventional plasmonic metals and control field localization with a choice of plasma frequencies in a wide spectral range. Here, epitaxial SrRuO3 thin films with low surface roughness fabricated by pulsed laser deposition are studied. The influence of the oxygen deposition pressure (20-300 mTorr) on the charge carrier dynamics and optical constants of the thin films in the near-infrared spectral range is elucidated. It is demonstrated that SrRuO3 thin films exhibit plasmonic behavior of the thin films in the near-infrared spectral range with the plasma frequency in 3.16-3.86â eV range and epsilon-near-zero wavelength in 1.11-1.47â µm range that could be controlled by the deposition conditions. The possible applications of these films range from the heat-generating nanostructures in the near-infrared spectral range, to metamaterial-based ideal absorbers and epsilon-near-zero components, where the interplay between real and imaginary parts of the permittivity in a given spectral range is needed for optimizing the spectral performance.