Superwetting Nanofluids of NiOx-Nanocrystals/CsBr Solution for Fabricating Quality NiOx-CsPbBr3 Gradient Hybrid Film in Carbon-Based Perovskite Solar Cells.

The wettability of precursor solution on substrates is the critical factor for fabricating quality film. In this work, superwetting nanofluids (NFs) of non-stoichiometric nickel oxide (NiOx) nanocrystals (NCs)-CsBr solution are first utilized to fabricate quality NiOx-CsPbBr3 hybrid film with gradient-distributed NiOx NCs in the upper part for constructing hole transport ladder in carbon-based perovskite solar cells (C-PSCs). As anticipated, the crystalline properties (improved crystalline grain diameters and reduced impurity phase) and hole extraction/transport of the NiOx-CsPbBr3 hybrid film are improved after incorporating NiOx NCs into CsPbBr3. This originates from the superb wettability of NiOx-CsBr NFs on substrates and the excellent hole-transport properties of NiOx. Consequently, the C-PSCs with the structure of FTO/SnO2/NiOx-CsPbBr3/C displays a power conversion efficiency of 10.07%, resulting in a 23.6% improvement as compared with the pristine CsPbBr3 cell. This work opens up a promising strategy to improve the absorber layer in PSCs by incorporating NCs into perovskite layers through the use of the superwettability of NFs and by composition gradient engineering.

Phase-Engineering of Layered Nickel Hydroxide for Synthesizing High-Quality NiOx Nanocrystals for Efficient Inverted Flexible Perovskite Solar Cells.

Nickel oxide (NiOx) nanocrystals have been widely used in inverted (p-i-n) flexible perovskite solar cells (fPSCs) due to their remarkable advantages of low cost and outstanding stability. However, anion and cation impurities such as NO3- widely exist in the NiOx nanocrystals obtained from calcinated nickel hydroxide (Ni(OH)2). The impurities impair the photovoltaic performance of fPSCs. In this work, we report a facile but effective way to reduce the impurities within the NiOx nanocrystals by regulating the Ni(OH)2 crystal phase. We add different alkalis, such as organic ammonium hydroxide and alkali metal hydroxides, to nickel nitrate solutions to precipitate layered Ni(OH)2 with different crystalline phase compositions (α and ß mixtures). Especially, Ni(OH)2 with a high ß-phase content (such as from KOH) has a narrower crystal plane spacing, resulting in fewer residual impurity ions. Thus, the NiOx nanocrystals, by calcinating the Ni(OH)x with excess ß phase from KOH, show improved performance in inverted fPSCs. A champion power conversion efficiency (PCE) of 20.42% has been achieved, which is among the state-of-art inverted fPSCs based on the NiOx hole transport material. Moreover, the reduced impurities are beneficial for enhancing the fPSCs' stability. This work provides an essential but facile strategy for developing high-performance inverted fPSCs.