Tuning the Refractive Index Sensitivity of LSPR Transducers Based on Nanocomposite Thin Films Composed of Noble Metal Nanoparticles Dispersed in TiO2.

ABSTRACT

This work reports on the development of nanoplasmonic thin films consisting of Au, Ag, or Au-Ag nanoparticles dispersed in a TiO2 matrix and the optimization of the deposition parameters to tune their optical response. The thin films were produced by reactive DC magnetron sputtering of a Ti target with Au and/or Ag pellets placed on the erosion zone. The thicknesses (50 and 100 nm) of the films, the current density (75 and 100 A/m2) applied to the target (titanium), and the number of pellets placed on its surface were the deposition conditions that were used to tailor the optical (LSPR) response. The total noble metal content varied between 13 and 28 at.% for Au/TiO2 films, between 22 and 30 at.% for Ag/TiO2 films, and 8 to 29 at% for the Au-Ag/TiO2 systems with 11, 11.5, and 12 AuAg atomic ratios. After thermal annealing at 400 and 600 °C, LSPR bands were found for all films concerning the Au-TiO2 and Au-Ag/TiO2, while for Ag/TiO2, only for thin films with 28 and 30 at.% of Ag concentration. Refractive index sensitivity (RIS) was evaluated for Au and Au-Ag/TiO2 thin films. It was found that for bimetallic nanoparticles, the sensitivity can increase up to five times when compared to a monometallic nanoplasmonic system. Using Au-Ag/TiO2 thin films can decrease the cost of fabrication of LSPR transducers while improving their sensitivity.