Effect of Silicon Carbide Fiber Length on the Flexural Strength and Flexural Modulus of Short Silicon Carbide Fiber-Reinforced Resin.
J Funct Biomater
; 15(2)2024 Jan 26.
Article
en En
| MEDLINE
| ID: mdl-38391883
ABSTRACT
Silicon carbide fibers have superior flexural properties and chemical stability compared to glass fibers. We investigated the flexural strength and modulus of an experimental, short silicon carbide fiber-reinforced resin. Short silicon carbide fibers with lengths of ~0.5, 1, 2, and 3 mm were prepared and silanized. Urethane dimethacrylate and triethylene glycol dimethacrylate were mixed at a 7030 wt% ratio and used as the matrix resins. Each length of short silicon carbide fibers and the matrix resin were combined using a mixing machine and then used for specimen preparation. The three-point bending test conditions were in accordance with ISO 40492009. The fracture surfaces of the specimens after the three-point bending test were observed using secondary electron images. The data were statistically analyzed with a one-way analysis of variance and Tukey's HSD test (α = 0.05). The flexural strength and modulus of the specimens containing 2 mm or 3 mm silicon carbide fibers were significantly higher than the other specimens. The river pattern was observed more clearly in specimens containing shorter silicon carbide fibers, although this pattern was observed in all specimens.
Texto completo:
1
Base de datos:
MEDLINE
Idioma:
En
Revista:
J Funct Biomater
Año:
2024
Tipo del documento:
Article
País de afiliación:
Japón