Pt/Al2O3@Ce/ZrO2-S bifunctional catalysts prepared by mechanically milling for selective catalytic oxidation of high-concentration ammonia.
Environ Sci Pollut Res Int
; 31(25): 37746-37756, 2024 May.
Article
en En
| MEDLINE
| ID: mdl-38787474
ABSTRACT
The selective catalytic oxidation (SCO) is an effective method for removing slipped high-concentration ammonia from NH3-fueled engine exhaust gas. Herein a novel bifunctional catalyst was synthesized by mechanically mixing sulfated Ce/ZrO2 (Ce/ZrO2-S) with a small fraction of Pt/Al2O3 (Pt 0.1 wt.%) for SCO of NH3. As expected, the introduction of a small amount of Pt/Al2O3 significantly improved NH3 conversion ability of Ce/ZrO2-S catalysts toward low-temperature direction. When the mass ratio of Pt/Al2O3 to Ce/ZrO2-S was 7.5% (the corresponding mixed catalyst was denoted as P@CZS-7.5), T90 temperature was 312 °C. More importantly, P@CZS-7.5 catalyst exhibited a much better N2 selectivity (> 96%) in a wide temperature range (320 ~ 450 °C). H2-TPR results revealed that the addition of a trace amount of Pt/Al2O3 significantly led to a distinct shift of reduction temperature peak toward low-temperature direction, thereby greatly improved the low-temperature redox performance of mixed catalysts. Furthermore, NH3-TPD and BET results showed that P@CZS-7.5 catalyst exhibited a similar NH3 adsorption capacity to Ce/ZrO2-S catalyst, while the former had a relatively higher specific surface area than the latter. It was considered as a crucial factor for P@CZS-7.5 catalyst maintaining superior N2 selectivity in high-concentration NH3 (5000 ppm) removal processes. In situ DRIFTS results indicated that P@CZS-7.5 catalyst followed the internal selective catalytic reduction (i-SCR) mechanism in NH3-SCO reactions.
Palabras clave
Texto completo:
1
Base de datos:
MEDLINE
Asunto principal:
Oxidación-Reducción
/
Óxido de Aluminio
/
Amoníaco
Idioma:
En
Revista:
Environ Sci Pollut Res Int
Asunto de la revista:
SAUDE AMBIENTAL
/
TOXICOLOGIA
Año:
2024
Tipo del documento:
Article
País de afiliación:
China