Asymmetric Synthesis of Scillascillin-Type Homoisoflavonoid.

The first asymmetric synthesis of a scillascillin-type homoisoflavonoid was reported. Key reactions for the asymmetric synthesis of benzocyclobutene include catalytic reductive desymmetrization of malonic ester and an intramolecular C-H activation of the methyl group.

The Effect of Different Diluents and Curing Agents on the Performance of Epoxy Resin-Based Intumescent Flame-Retardant Coatings.

The epoxy resin-based (ESB) intumescent flame-retardant coatings were modified with 1,4-butanediol diglycidyl ether (14BDDE) and butyl glycidyl ether (BGE) as diluents and T403 and 4,4'-diaminodiphenylmethane (DDM) as curing agents, respectively. The effects of different diluents and curing agents on the flame-retardant and mechanical properties, as well as the composition evolution of the coatings, were investigated by using large-plate combustion, the limiting oxygen index (LOI), vertical combustion, a cone calorimeter, X-ray diffraction, FTIR analysis, a N2 adsorption and desorption test, a scanning electron microscope (SEM), a tensile strength test, and a viscosity test. The results showed that the addition of 14BBDE and T403 promoted the oxidation of B4C and the formation of boron-containing glass or ceramics, increased the residual mass of char, densified the surface char layer, and increased the specific surface area of porous residual char. When their dosage was 30%, ESB-1T-3 coating exhibited the most excellent flame-retardant properties. During the 2 h large-plate combustion test, the backside temperature was only 138.72 °C, without any melting pits. In addition, the peak heat release rate (PHRR), total heat release rate (THR), total smoke production (TSP), and peak smoke production (PSPR) were reduced by 13.15%, 13.9%, 5.48%, and 17.45%, respectively, compared to the blank ESB coating. The LOI value reached 33.4%, and the vertical combustion grade was V-0. In addition, the tensile strength of the ESB-1T-3 sample was increased by 10.94% compared to ESB. In contrast, the addition of BGE and DDM promoted the combustion of the coating, affected the ceramic process of the coating, seriously affected the formation of borosilicate glass, and exhibited poor flame retardancy. The backside temperature reached 190.93 °C after 2 h combustion. A unified rule is that as the amount of diluent and curing agent increases, the flame retardancy improves while the mechanical properties decrease. This work provides data support for the preparation and process optimization of resin-based coatings.

Utilizing symmetrical tetramethyl cucurbit[6]uril-based supramolecular fluorescence probe for detection of paraquat in water.

A supramolecular fluorescence probe has been developed using a symmetrical tetramethyl cucurbit[6]uril (TMeQ[6]) and a styryl derivative (SPy) with a host-guest ratio of 2:1. The introduction of paraquat (PQ) competes with SPy for the TMeQ[6] cavity, resulting in fluorescent quenching. The addition of 17 common herbicides and ions had negligible effects on the fluorescence quenching, indicating that the 2TMeQ[6]/SPy complex exhibits excellent selectivity in detecting PQ. The detection limit was found to be 4.62 × 10-7 M. More importantly, the probe was engineered to detect paraquat in river water by examining post-treatment samples and noting alterations in fluorescence color. The red to blue (R/B) intensity ratio is subsequently calculated to ascertain the PQ concentration. Experimental trials conducted on river water samples yielded recovery rates between 98.21 % and 108 %, with a relative standard deviation of less than 5 %. By pairing this with a smartphone-based colorimetric analysis application, we can facilitate portable PQ detection, enabling efficient and convenient monitoring across various locations.