Effect of the Introduction of Reactive Fillers and Metakaolin in Waste Clay-Based Materials for Geopolymerization Processes.

In this study, the role of two reactive fillers, specifically a sand from a clay washing process as an alternative to waste glass powder and a commercial metakaolin (MK), into the geopolymerization process of waste clay-based materials was assessed. Three kinds of clayey wastes from mining operations-halloysitic, kaolinitic and smectitic clays-were tested as potential precursor of geopolymeric materials in view of a potential valorisation of these by-products. A mix-design based on the addition of low percentages (20%) of these fillers or MK to improve the mechanical and chemico-physical properties of geopolymeric formulations was evaluated. All the clays were thermally treated at a temperature of 650 °C, while the geopolymeric pastes were cured at room temperature. In particular, the chemical stability in water (pH and ionic conductivity of leachate water, weight loss), the variations in the microstructure (XRD, SEM), and in the mechanical performance (compressive strength) were analysed. The most reactive additive was MK, followed by sand and waste glass at very similar levels-1:1 or 2:1-depending upon the type of the clay but not strictly related to the clay type. The increase of geopolymeric gel densification due to the presence of MK and sand was replaced by a crack deflection mechanism in the case of the WG grains. The worst performance (chemical stability and mechanical properties) was found for the halloysitic clay, while kaolinitic and smectitic clays developed strengths slightly below 30 MPa.

Mine Clay Washing Residues as a Source for Alkali-Activated Binders.

The aim of this paper is to promote the use of mine clay washing residues for the preparation of alkali activated materials (AAMs). In particular, the influence of the calcination temperature of the clayey by-product on the geopolymerization process was investigated in terms of chemical stability and durability in water. The halloysitic clay, a mining by-product, has been used after calcination and mixed with an alkaline solution to form alkali activated binders. Attention was focused on the influence of the clay's calcination treatment (450-500-600 °C) on the geopolymers' microstructure of samples, remaining in the lower limit indicated by the literature for kaolinite or illite calcination. The mixtures of clay and alkali activators (NaOH 8M and Na-silicate) were cured at room temperature for 28 days. The influence of solid to liquid ratio in the mix formulation was also tested in terms of chemical stability measuring the pH and the ionic conductivity of the eluate after 24-h immersion time in water. The results reported values of ionic conductivity higher for samples made with untreated clay or with low temperature of calcination (≥756 mS/m) compared with values of samples made with calcined clay (292 mS/m). This result suggests that without a proper calcination of the as-received clay it was not possible to obtain 25 °C-consolidated AAMs with good chemical stability and dense microstructure. The measures of integrity test, pH, and ionic conductivity in water confirmed that the best sample is made with calcined clay at 600 °C, being similar (53% higher ionic conductivity of the eluate) or equal (integrity test and pH) to values recorded for the metakaolin-based geopolymer considered the reference material. These results were reflected in term of reticulation and morphology of samples through the analysis with scanning electron microscope (SEM) and X-ray diffraction (XRD), which show a dense and homogeneous microstructure predominantly amorphous with minor amounts of quartz, halloysite, and illite crystalline phases. Special attention was dedicated to this by-product to promote its use, given that kaolinite (and metakaolin), as primary mineral product, has a strong impact on the environment. The results obtained led us to consider this halloysite clay very interesting as an aluminosilicate precursor, and extensively deepening its properties and reactivity for the alkaline activation. In fact, the heart of this work is to study the possibility of reusing this by-product of an industrial process to obtain more sustainable high-performance binders.

Environmentally-Friendly Dense and Porous Geopolymers Using Fly Ash and Rice Husk Ash as Raw Materials.

This paper assesses the feasibility of two industrial wastes, fly ash (FA) and rice husk ash (RHA), as raw materials for the production of geopolymeric pastes. Three typologies of samples were thus produced: (i) halloysite activated with potassium hydroxide and nanosilica, used as the reference sample (HL-S); (ii) halloysite activated with rice husk ash dissolved into KOH solution (HL-R); (iii) FA activated with the alkaline solution realized with the rice husk ash (FA-R). Dense and porous samples were produced and characterized in terms of mechanical properties and environmental impact. The flexural and compressive strength of HL-R reached about 9 and 43 MPa, respectively. On the contrary, the compressive strength of FA-R is significantly lower than the HL-R one, in spite of a comparable flexural strength being reached. However, when porous samples are concerned, FA-R shows comparable or even higher strength than HL-R. Thus, the current results show that RHA is a valuable alternative to silica nanopowder to prepare the activator solution, to be used either with calcined clay and fly ash feedstock materials. Finally, a preliminary evaluation of the global warming potential (GWP) was performed for the three investigated formulations. With the mix containing FA and RHA-based silica solution, a reduction of about 90% of GWP was achieved with respect to the values obtained for the reference formulation.

Setup of Extruded Cementitious Hollow Tubes as Containing/Releasing Devices in Self-Healing Systems.

The aim of this research is to produce self-healing cementitious composites based on the use of cylindrical capsules containing a repairing agent. Cementitious hollow tubes (CHT) having two different internal diameters (of 2 mm and 7.5 mm) were produced by extrusion and used as containers and releasing devices for cement paste/mortar healing agents. Based on the results of preliminary mechanical tests, sodium silicate was selected as the healing agent. The morphological features of several mix designs used to manufacture the extruded hollow tubes, as well as the coatings applied to increase the durability of both core and shell materials are discussed. Three-point bending tests were performed on samples produced with the addition of the above-mentioned cementitious hollow tubes to verify the self-healing effectiveness of the proposed solution. Promising results were achieved, in particular when tubes with a bigger diameter were used. In this case, a substantial strength and stiffness recovery was observed, even in specimens presenting large cracks (>1 mm). The method is inexpensive and simple to scale up; however, further research is needed in view of a final optimization.