At Least 10-fold Higher Lubricity of Molecularly Thin D2O vs H2O Films at Single-Layer Graphene-Mica Interfaces.

Interfacial water is a widespread lubricant down to the nanometer scale. We investigate the lubricities of molecularly thin H2O and D2O films confined between mica and graphene, via the relaxation of initially applied strain in graphene employing Raman spectroscopy. Surprisingly, the D2O films are at least 1 order of magnitude more lubricant than H2O films, despite the similar bulk viscosities of the two liquids. We propose a mechanism based on the known selective permeation of protons vs deuterons through graphene. Permeated protons and left behind hydroxides may form ion pairs clamping across the graphene sheet and thereby hindering the graphene from sliding on the water layer. This explains the lower lubricity but also the hindering diffusivity of the water layer, which yields a high effective viscosity in accordance with findings in dewetting experiments. Our work elucidates an unexpected effect and provides clues to the behavior of graphene on hydrous surfaces.

Bulk-suppressed and surface-sensitive Raman scattering by transferable plasmonic membranes with irregular slot-shaped nanopores.

Raman spectroscopy enables the non-destructive characterization of chemical composition, crystallinity, defects, or strain in countless materials. However, the Raman response of surfaces or thin films is often weak and obscured by dominant bulk signals. Here we overcome this limitation by placing a transferable porous gold membrane, (PAuM) on the surface of interest. Slot-shaped nanopores in the membrane act as plasmonic antennas and enhance the Raman response of the surface or thin film underneath. Simultaneously, the PAuM suppresses the penetration of the excitation laser into the bulk, efficiently blocking its Raman signal. Using graphene as a model surface, we show that this method increases the surface-to-bulk Raman signal ratio by three orders of magnitude. We find that 90% of the Raman enhancement occurs within the top 2.5 nm of the material, demonstrating truly surface-sensitive Raman scattering. To validate our approach, we quantify the strain in a 12.5 nm thin Silicon film and analyze the surface of a LaNiO3 thin film. We observe a Raman mode splitting for the LaNiO3 surface-layer, which is spectroscopic evidence that the surface structure differs from the bulk. These results validate that PAuM gives direct access to Raman signatures of thin films and surfaces.