Pt/MnO Interface Induced Defects for High Reverse Water Gas Shift Activity.

The implementation of supported metal catalysts heavily relies on the synergistic interactions between metal nanoparticles and the material they are dispersed on. It is clear that interfacial perimeter sites have outstanding skills for turning catalytic reactions over, however, high activity and selectivity of the designed interface-induced metal distortion can also obtain catalysts for the most crucial industrial processes as evidenced in this paper. Herein, the beneficial synergy established between designed Pt nanoparticles and MnO in the course of the reverse water gas shift (RWGS) reaction resulted in a Pt/MnO catalyst having ≈10 times higher activity compared to the reference Pt/SBA-15 catalyst with >99 % CO selectivity. Under activation, a crystal assembly through the metallic Pt (110) and MnO evolved, where the plane distance differences caused a mismatched-row structure in softer Pt nanoparticles, which was identified by microscopic and surface-sensitive spectroscopic characterizations combined with density functional theory simulations. The generated edge dislocations caused the Pt lattice expansion which led to the weakening of the Pt-CO bond. Even though MnO also exhibited an adverse effect on Pt by lowering the number of exposed metal sites, rapid desorption of the linearly adsorbed CO species governed the performance of the Pt/MnO in the RWGS.

Ca Solubility in a BiFeO3-Based System with a Secondary Bi2O3 Phase on a Nanoscale.

In BiFeO3 (BFO), Bi2O3 (BO) is a known secondary phase, which can appear under certain growth conditions. However, BO is not just an unwanted parasitic phase but can be used to create the super-tetragonal BFO phase in films on substrates, which would otherwise grow in the regular rhombohedral phase (R-phase). The super-tetragonal BFO phase has the advantage of a much larger ferroelectric polarization of 130-150 µC/cm2, which is around 1.5 times the value of the rhombohedral phase with 80-100 µC/cm2. Here, we report that the solubility of Ca, which is a common dopant of bismuth ferrite materials to tune their properties, is significantly lower in the secondary BO phase than in the observed R-phase BFO. Starting from the film growth, this leads to completely different Ca concentrations in the two phases. We show this with advanced analytical transmission electron microscopy techniques and confirm the experimental results with density functional theory (DFT) calculations. At the film's fabrication temperature, caused by different solubilities, about 50 times higher Ca concentration is expected in the BFO phase than in the secondary one. Depending on the cooling rate after fabrication, this can further increase since a larger Ca concentration difference is expected at lower temperatures. When fabricating functional devices using Ca doping and the secondary BO phase, the difference in solubility must be considered because, depending on the ratio of the BO phase, the Ca concentration in the BFO phase can become much higher than intended. This can be critical for the intended device functionality because the Ca concentration strongly influences and modifies the BFO properties.

Negatively Charged In-Plane and Out-Of-Plane Domain Walls with Oxygen-Vacancy Agglomerations in a Ca-Doped Bismuth-Ferrite Thin Film.

The interaction of oxygen vacancies and ferroelectric domain walls is of great scientific interest because it leads to different domain-structure behaviors. Here, we use high-resolution scanning transmission electron microscopy to study the ferroelectric domain structure and oxygen-vacancy ordering in a compressively strained Bi0.9Ca0.1FeO3-δ thin film. It was found that atomic plates, in which agglomerated oxygen vacancies are ordered, appear without any periodicity between the plates in out-of-plane and in-plane orientation. The oxygen non-stoichiometry with δ ≈ 1 in FeO2-δ planes is identical in both orientations and shows no preference. Within the plates, the oxygen vacancies form 1D channels in a pseudocubic [010] direction with a high number of vacancies that alternate with oxygen columns with few vacancies. These plates of oxygen vacancies always coincide with charged domain walls in a tail-to-tail configuration. Defects such as ordered oxygen vacancies are thereby known to lead to a pinning effect of the ferroelectric domain walls (causing application-critical aspects, such as fatigue mechanisms and countering of retention failure) and to have a critical influence on the domain-wall conductivity. Thus, intentional oxygen vacancy defect engineering could be useful for the design of multiferroic devices with advanced functionality.

Study on Ca Segregation toward an Epitaxial Interface between Bismuth Ferrite and Strontium Titanate.

Segregation is a crucial phenomenon, which has to be considered in functional material design. Segregation processes in perovskite oxides have been the subject of ongoing scientific interest, since they can lead to a modification of properties and a loss of functionality. Many studies in oxide thin films have focused on segregation toward the surface using a variety of surface-sensitive analysis techniques. In contrast, here we report a Ca segregation toward an in-plane compressively strained heterostructure interface in a Ca- and Mn-codoped bismuth ferrite film. We are using advanced transmission electron microscopy techniques, X-ray photoelectron spectroscopy, and density functional theory (DFT) calculations. Ca segregation is found to trigger atomic and electronic structure changes at the interface. This includes the reduction of the interface strain according to the Ca concentration gradient, interplanar spacing variations, and oxygen vacancies at the interface. The experimental results are supported by DFT calculations, which explore two segregation scenarios, i.e., one without oxygen vacancies and Fe oxidation from 3+ to 4+ and one with vacancies for charge compensation. Comparison with electron energy loss spectroscopy (EELS) measurements confirms the second segregation scenario with vacancy formation. The findings contribute to the understanding of segregation and indicate promising effects of a Ca-rich buffer layer in this heterostructure system.

Direct-Write 3D Nanoprinting of Plasmonic Structures.

During the past decade, significant progress has been made in the field of resonant optics ranging from fundamental aspects to concrete applications. While several techniques have been introduced for the fabrication of highly defined metallic nanostructures, the synthesis of complex, free-standing three-dimensional (3D) structures is still an intriguing, but so far intractable, challenge. In this study, we demonstrate a 3D direct-write synthesis approach that addresses this challenge. Specifically, we succeeded in the direct-write fabrication of 3D nanoarchitectures via electron-stimulated reactions, which are applicable on virtually any material and surface morphology. By that, complex 3D nanostructures composed of highly compact, pure gold can be fabricated, which reveal strong plasmonic activity and pave the way for a new generation of 3D nanoplasmonic architectures that can be printed on-demand.