RESUMO
Chemical processing is among the significant keys to tackle agro-residues utilization field, aiming to obtain value-added materials. Extraction of cellulose nanocrystals (CNCs) is an emerging route to valorize lignocellulosic wastes into high value particles. In this investigation, effect of acidic hydrolysis duration was monitored on size and morphology of obtained crystals; namely: CNCs from Nile roses fibers (NRFs) (Eichhornia crassipes). Different acidic hydrolysis duration range or different characterization techniques set this article apart from relevant literature, including our group research articles. The grinded NRFs were firstly subjected to alkaline and bleaching pretreatments, then acid hydrolysis process was carried out with varied durations ranging from 5 to 30 min. Microcrystalline cellulose (MCC) was used as reference for comparison with NRFs based samples. The extracted CNCs samples were investigated using various techniques such as scanning electron microscopy (SEM), Atomic force microscopy (AFM), Raman spectroscopy, and thermogravimetric (TGA) analysis. The figures gotten from SEM and AFM depicted that NRFs based CNCs appeared as fibril-like shapes, with reduced average size when the NRFs underwent pulping and bleaching processes. This was indicated that the elimination of hemicellulose and lignin components got achieved successfully. This outcome was proven by chemical composition measurements and TGA/DTG curves. On the other hand, AFM-3D images indicated that CNCs topology and surface roughness were mostly affected by increasing hydrolysis durations, besides smooth and homogeneous surfaces were noticed. Moreover, Raman spectra demonstrated that the particle size and crystallinity degree of NRFs based CNCs can be affected by acidic hydrolysis durations and optimum extraction time was found to be 10 min. Thermal stability of extracted CNCs-NRFs and CNCs-MCC was measured by TGA/DTG and the kinetic models were suggested to identify the kinetic parameters of the thermal decomposition of CNCs for each acid hydrolysis duration. Increasing hydrolysis duration promoted thermal stability, particularly for NRFs based CNCs. Results showcased in this article add new perspective to Nile rose nanocellulose and pave down the way to fabricate NRFs based humidity nano-sensors.
Assuntos
Celulose , Eichhornia , Nanopartículas , Celulose/química , Nanopartículas/química , Eichhornia/química , Eichhornia/metabolismo , Hidrólise , Microscopia de Força Atômica , Análise Espectral Raman , Microscopia Eletrônica de Varredura , Termogravimetria , Lignina/químicaRESUMO
Extraction of cellulose nanocrystals (CNCs) from agro-residues has received much attention, not only for their unique properties supporting a wide range of potential applications, but also their limited risk to global climate change. This research was conducted to assess Nile roses (Eichhornia crassipes) fibers as a natural biomass to extract CNCs through an acid hydrolysis approach. Nile roses fibers (NRFs) were initially subjected to alkaline (pulping) and bleaching pretreatments. Microcrystalline cellulose (MCC) was used as control in comparison to Nile rose based samples. All samples underwent acid hydrolysis process at a mild temperature (45 °C). The impact of extraction durations ranging from 5 to 30 min on the morphology structure and crystallinity index of the prepared CNCs was investigated. The prepared CNCs were subjected to various characterization techniques, namely: X-ray diffraction (XRD), FT-IR analysis, Transmission electron microscopy (TEM), and X-ray Photoelectron spectroscopy (XPS). The outcomes obtained by XRD showed that the crystallinity index increased as the duration of acid hydrolysis was prolonged up to 10 min, and then decreased, indicating optimal conditions for the dissolution of amorphous zones of cellulose before eroding the crystallized domains. These data were confirmed by FT-IR spectroscopy. However, a minor effect of hydrolysis duration on the degree of crystallinity was noticed for MCC based samples. TEM images illustrated that a spherical morphology of CNCs was formed as a result of 30 min acid hydrolysis, highlighting the optimal 20 min acid hydrolysis to obtain a fibrillar structure. The XPS study demonstrated that the main constituents of extracted CNCs were carbon and oxygen.