We report on the investigation of continuous-wave (CW) and SEmiconductor Saturable Absorber Mirror (SESAM) mode-locked operation of a Yb:GdScO3 laser. Using a single-transverse-mode, fiber-coupled InGaAs laser diode at 976â nm as a pump source, the Yb:GdScO3 laser delivers 343â mW output power at 1062â nm in the CW regime, which corresponds to a slope efficiency of 52%. Continuous tuning is possible across a wavelength range of 84â nm (1027-1111â nm). Using a commercial SESAM to initiate mode-locking and stabilize soliton-type pulse shaping, the Yb:GdScO3 laser produces pulses as short as 42 fs at 1065.9â nm, with an average output power of 40â mW at 66.89â MHz. To the best of our knowledge, this is the first demonstration of passively mode-locking with Yb:GdScO3 crystal.
RESUMO
We report on the continuous-wave (CW) and, for what we believe to be the first time, passively mode-locked (ML) laser operation of an Yb3+-doped YSr3(PO4)3 crystal. Utilizing a 976-nm spatially single-mode, fiber-coupled laser diode as pump source, the Yb:YSr3(PO4)3 laser delivers a maximum CW output power of 333â mW at 1045.8â nm with an optical efficiency of 55.7% and a slope efficiency of 60.9%. Employing a quartz-based Lyot filter, an impressive wavelength tuning range of 97â nm at the zero level was achieved in the CW regime, spanning from 1007â nm to 1104â nm. In the ML regime, incorporating a commercially available semiconductor saturable absorber mirror (SESAM) to initiate and maintain soliton-like pulse shaping, the Yb:YSr3(PO4)3 laser generated pulses as short as 61 fs at 1062.7â nm, with an average output power of 38â mW at a repetition rate of â¼66.7â MHz.
RESUMO
We report on the growth, polarized spectroscopy and first laser operation of an orthorhombic (space group Pnma) Tm3+,Ho3+-codoped gadolinium orthoscandate (GdScO3) perovskite-type crystal. A single crystal of 3.76 at.% Tm, 0.35 at.% Ho:GdScO3 was grown by the Czochralski method. Its polarized absorption and fluorescence properties were studied revealing a broadband emission around 2â µm. The parameters of the Tm3+ â Ho3+ energy transfer was quantified, P28 = 1.30 × 10-22 cm3µs-1, and P71 = 0.99 × 10-23 cm3µs-1, and the thermal equilibrium lifetime was measured to be 3.5â ms. The crystal-field splitting of Tm3+ and Ho3+ multiplets in Cs symmetry sites of the perovskite structure was determined by low-temperature spectroscopy and the mechanism of spectral line broadening is discussed. The continuous-wave Tm,Ho:GdScO3 laser generated 1.16 W at â¼2.1â µm with a slope efficiency of 50.5%, a laser threshold of 184â mW, a linear laser polarization (E || c) and a spatially single-mode output. The Tm,Ho:GdScO3 crystal is promising for broadly tunable and femtosecond mode-locked lasers emitting above 2â µm.
RESUMO
We present the growth, spectroscopy, continuous-wave (CW) and passively mode-locked (ML) operation of a novel "mixed" tetragonal calcium rare-earth aluminate crystal, Yb3+:Ca(Gd,Y)AlO4. The absorption, stimulated-emission, and gain cross-sections are derived for π and σ polarizations. The laser performance of a c-cut Yb:Ca(Gd,Y)AlO4 crystal is studied using a spatially single-mode, 976-nm fiber-coupled laser diode as a pump source. A maximum output power of 347â mW is obtained in the CW regime with a slope efficiency of 48.9%. The emission wavelength is continuously tunable across 90â nm (1010 - 1100â nm) using a quartz-based Lyot filter. With a commercial SEmiconductor Saturable Absorber Mirror to initiate and maintain ML operation, soliton pulses as short as 35 fs are generated at 1059.8â nm with an average output power of 51â mW at â¼65.95â MHz. The average output power can be scaled to 105â mW for slightly longer pulses of 42 fs at 1063.5â nm.
RESUMO
We report on a Kerr-lens mode-locked laser based on an Yb3+-doped disordered calcium lithium niobium gallium garnet (Yb:CLNGG) crystal. Pumping by a spatially single-mode Yb fiber laser at 976â nm, the Yb:CLNGG laser delivers soliton pulses as short as 31 fs at 1056.8â nm with an average output power of 66â mW and a pulse repetition rate of â¼77.6â MHz via soft-aperture Kerr-lens mode-locking. The maximum output power of the Kerr-lens mode-locked laser amounted to 203â mW for slightly longer pulses of 37 fs at an absorbed pump power of 0.74 W, which corresponds to a peak power of 62.2â kW and an optical efficiency of 20.3%.
RESUMO
We report on sub-40 fs pulse generation from a Yb:Sc2SiO5 laser pumped by a spatially single-mode fiber-coupled laser diode at 976â nm. A maximum output power of 545â mW was obtained at 1062.6â nm in the continuous-wave regime, corresponding to a slope efficiency of 64% and a laser threshold of 143â mW. A continuous wavelength tuning across 80â nm (1030 -1110â nm) was also achieved. Implementing a SESAM for starting and stabilizing the mode-locked operation, the Yb:Sc2SiO5 laser delivered soliton pulses as short as 38 fs at 1069.5â nm with an average output power of 76â mW at a pulse repetition rate of â¼79.8â MHz. The maximum output power was scaled to 216â mW for slightly longer pulses of 42 fs, which corresponded to a peak power of 56.6â kW and an optical efficiency of 22.7%. To the best of our knowledge, these results represent the shortest pulses ever achieved with any Yb3+-doped rare-earth oxyorthosilicate crystal.
RESUMO
We report on the first sub-60 fs pulse generated from a diode-pumped SESAM mode-locked Yb-laser based on a non-centrosymmetric Yb:YAl3(BO3)4 crystal as a gain medium. In the continuous-wave regime, pumping with a spatially single-mode, fiber-coupled 976â nm InGaAs laser diode, the Yb:YAl3(BO3)4 laser generated 391â mW at 1041.7â nm with a slope efficiency as high as 65.1%, and a wavelength tuning across 59â nm (1019 to 1078â nm) was achieved. By implementing a commercial SESAM to initiate and sustain the soliton type mode-locking, and using only a 1â mm-thick laser crystal, the Yb:YAl3(BO3)4 laser delivered pulses as short as 56 fs at a central wavelength of 1044.6â nm with an average output power of 76â mW at a pulse repetition rate of â¼67.55â MHz. To the best of our knowledge, this result represents the shortest pulses ever achieved from Yb:YAB crystal.
RESUMO
We report on sub-50 fs pulse generation from a passively mode-locked Yb:SrF2 laser pumped with a spatially single-mode, fiber-coupled laser diode at 976â nm. In the continuous-wave regime, the Yb:SrF2 laser generated a maximum output power of 704â mW at 1048â nm with a threshold of 64â mW and a slope efficiency of 77.2%. A continuous wavelength tuning across 89â nm (1006 - 1095â nm) was achieved with a Lyot filter. By implementing a SEmiconductor Saturable Absorber Mirror (SESAM) for initiating and sustaining the mode-locked operation, soliton pulses as short as 49 fs were generated at 1057â nm with an average output power of 117â mW at a pulse repetition rate of â¼75.9â MHz. The maximum average output power of the mode-locked Yb:SrF2 laser was scaled up to 313â mW for slightly longer pulses of 70 fs at 1049.4â nm, corresponding to a peak power of 51.9â kW and an optical efficiency of 34.7%.
RESUMO
We report on sub-30 fs pulse generation from a semiconductor saturable absorber mirror mode-locked Yb:YAP laser. Pumping by a spatially single-mode Yb fiber laser at 979 nm, soliton pulses as short as 29 fs were generated at 1091 nm with an average output power of 156 mW and a pulse repetition rate of 85.1 MHz. The maximum output power of the mode-locked Yb:YAP laser amounted to 320 mW for slightly longer pulses (32 fs) at an incident pump power of 1.52 W, corresponding to a peak power of 103 kW and an optical efficiency of 20.5%. To the best of our knowledge, this result represents the shortest pulses ever achieved from any solid-state Yb laser mode-locked by a slow, i.e., physical saturable absorber.
RESUMO
We report on the continuous-wave (CW) and mode-locked (ML) laser performance of an Yb3+-doped yttrium-gadolinium orthoaluminate crystal, Yb:(Y,Gd)AlO3. Pumping by a single-transverse-mode fiber-coupled 976 nm InGaAs laser diode, the maximum output power in the CW regime amounted to 429 mW at 1041.8 nm corresponding to a slope efficiency of 51.1% and a continuous wavelength tuning across 84 nm (1011-1095 nm) was achieved. The self-starting ML operation of the Yb:(Y,Gd)AlO3 laser was stabilized by a semiconductor saturable absorber mirror. Soliton pulses as short as 43 fs were generated at 1052.3 nm with an average output power of 103 mW and a pulse repetition rate of â¼70.8 MHz. To the best of our knowledge, our result represents the first report on the passively mode-locked operation of a Yb:(Y,Gd)AlO3 laser, and the shortest pulse duration ever achieved from any Yb3+-doped orthorhombic perovskite aluminate crystals.
RESUMO
We report on a soliton mode-locked Yb:Ca3Gd2(BO3)4 laser at â¼1.06 µm stabilized by a semiconductor saturable absorber mirror. Pumping with a single-transverse mode, fiber-coupled laser diode at 976 nm, the Yb:Ca3Gd2(BO3)4 laser delivers soliton pulses as short as 39 fs at a central wavelength of 1059.2 nm with an average output power of 70 mW and a pulse repetition rate of â¼67.3 MHz.
RESUMO
We demonstrate the first sub-40 fs soliton pulse generation from a diode-pumped Yb:Sr3Y2(BO3)4 laser passively mode-locked by a semiconductor saturable absorber mirror. Pulses as short as 38 fs at a central wavelength of 1051.7 nm were achieved with an average output power of 115 mW and a pulse repetition rate of 67.7 MHz. The maximum average output power reached 303 mW at 1057.8 nm with a slightly longer pulse duration of 52 fs, which corresponded to a peak power of 76.9 kW and an optical efficiency of 25.3%.
RESUMO
We report on a continuous-wave (CW) and passively mode-locked operation of a fluorite-type Yb:BaF2 crystal. Pumped with a spatially single-mode, fiber-coupled InGaAs laser diode at 976 nm, the Yb:BaF2 laser generated a maximum CW output power of 512 mW at 1054.4 nm, corresponding to a laser threshold of 36.5 mW and a slope efficiency of 65.0%. A continuous wavelength tuning across 85 nm (1007-1092 nm) was achieved. By implementing a semiconductor saturable absorber mirror for initiating and sustaining the soliton pulse shaping, near Fourier-transform-limited pulses as short as 52 fs were generated at 1058.2 nm with an average output power of 129 mW at a pulse repetition rate of â¼79.5 MHz. To the best of our knowledge, this is the first report on the passively mode-locked operation of the Yb:BaF2 crystal.
RESUMO
We report on a Kerr-lens mode-locked Yb:YAlO3 laser generating soliton pulses as short as 24 fs at 1085â nm with an average output power of 186 mW and a pulse repetition rate of 87.5â MHz, representing the shortest pulses ever achieved from any mode-locked laser based on Yb3+-doped structurally ordered crystal. Optimized for power-scalable operation, the Yb:YAlO3 laser delivers 1.9 W at 1060â nm at the expense of a longer pulse duration of 44 fs, corresponding to a peak power of 462â kW and an optical efficiency of 43.2%.
RESUMO
We report on the first, to the best of our knowledge, Kerr-lens mode-locked laser based on an Yb3+-doped perovskite-type orthoaluminate crystal exploiting two different principal light polarizations. The Yb:(Y,Gd)AlO3 laser delivers soliton pulses as short as 32 fs at 1067â nm with an average output power of 328â mW and a pulse repetition rate of â¼84.6â MHz for E || a polarization. For the orthogonal E || b polarization, 33-fs pulses are generated at 1057â nm with an average output power of 305â mW. Power scaling to a maximum average output power reaching 2.07 W is achieved at the expense of longer pulse duration (72 fs for E || b), corresponding to an optical efficiency of 43.9% and a peak power of 303â kW.