RESUMO
Recently emerged lead halide perovskite CsPbX3 (X = Cl, Br, and I) nanocrystals (PNCs) have attracted tremendous attention due to their excellent optical properties. However, the poor water stability, unsatisfactory luminescence efficiency, disappointing lead leakage, and toxicity have restricted their practical applications in photoelectronics and biomedical fields. Herein, a controllable encapsulated strategy is investigated to realize CsPbX3 PNCs/PVP @PMMA composites with superior luminescence properties and excellent biocompatibility. Additionally, the synthesized CsPbBr3 and CsPbBr0.6I2.4 PNCs/PVP@PMMA structures exhibit green and red emissions with a maximal photoluminescence quantum yield (PLQY) of about 70.24% and 98.26%, respectively. These CsPbX3 PNCs/PVP@PMMA structures show high emission efficiency, excellent stability after water storage for 18 months, and low cytotoxicity at the PNC concentration at 500 µg mL-1. Moreover, white light-emitting diode (WLED) devices based on mixtures of CsPbBr3 and CsPbBr0.6I2.4 PNCs/PVP@PMMA perovskite structures are investigated, which exhibit excellent warm-white light emissions at room temperature. A flexible manipulation method is used to fabricate the white light emitters based on these perovskite composites, providing a fantastic platform for fabricating solid-state white light sources and full-color displays.
RESUMO
Regulation of the fluorescence through crystalizing from the matrix in the Carbon dots (CDs)-based solid-state materials has been verified to be one of the effective methods, yet there are not only challenges in preparing such materials efficiently, but also insufficient insight into their regulation mechanisms. Here, a one-pot solvothermal route to synthesize a series of CDs-based composites with crystalline matrix is reported. These crystals exhibited multicolor fluorescence with the feature of multi-peaks emissions with increasing temperatures from 140 â to 220 â, in which the orange emitting O-CDs@PA and the yellow emitting Y-CDs@PA crystals obtained the FLQYs of 22% and 68% respectively due to relatively stable crystalline structures. After comparative analysis to both crystals in detail, the core and the groups associated with them on the interface between CDs and matrix were adjusted in size and species during structural transformation of the crystal matrix, which changes radically the energy band structures to influence fluorescent emitting of both crystals ultimately. In addition, the reasons resulting in higher FLQY for Y-CDs@PA were provided leveraging the schematic illustration presumed based on the PL properties of both crystals. Because of the optimal optical performances, these fluorescent materials promised to fabricate WLED devices and obtained a number of photometric parameters endowed these WLED devices with the feature of warm-white light.