RESUMO
In this study, titania−silica oxides (TixSiy oxides) were successfully prepared via the sol−gel technique. The Ti and Si precursors were titanium (IV), isopropoxide (TTIP), and tetraethylorthosilicate (TEOS), respectively. In this work, the effects of pH and the Ti/Si atomic ratio of titanium−silicon binary oxide (TixSiy) on the structural characteristics of TixSiy oxide are reported. 29Si solid-state NMR and FTIR were used to validate the chemical structure of TixSiy oxide. The structural characteristics of TixSiy oxide were investigated using X-ray diffraction, XRF, Fe-SEM, diffraction particle size analysis, and nitrogen adsorption measurements. By applying X-ray absorption spectroscopy (XAS) obtained from synchrotron light sources, the qualitative characterization of the Ti−O−Si and Ti−O−Ti bonds in Ti−Si oxides was proposed. Some Si atoms in the SiO2 network were replaced by Ti atoms, suggesting that Si−O−Ti bonds were formed as a result of the synthesis accomplished using the sol−gel technique described in this article. Upon increasing the pH to alkaline conditions (pH 9.0 and 10.0), the nanoparticles acquired a more spherical shape, and their size distribution became more uniform, resulting in an acceptable nanostructure. TixSiy oxide nanoparticles were largely spherical in shape, and agglomeration was minimized. However, the Ti50Si50 oxide particles at pH 10.0 become nano-sized and agglomerated. The presence of a significant pre-edge feature in the spectra of Ti50Si50 oxide samples implied that a higher fraction of Ti atoms occupied tetrahedral symmetry locations, as predicted in samples where Ti directly substituted Si. The proportion of Ti atoms in a tetrahedral environment agreed with the value of 1.83 given for the Ti−O bond distance in TixSiy oxides produced at pH 9.0 using extended X-ray absorption fine structure (EXAFS) analysis. Photocatalysis was improved by adding 3% wt TiO2, SiO2, and TixSiy oxide to the PLA film matrix. TiO2 was more effective than Ti50Si50 pH 9.0, Ti50Si50 pH 10.0, Ti50Si50 pH 8.0, and SiO2 in degrading methylene blue (MB). The most effective method to degrade MB was TiO2 > Ti70Si30 > Ti50Si50 > Ti40Si60 > SiO2. Under these conditions, PLA/Ti70Si30 improved the effectiveness of the photocatalytic activity of PLA.
RESUMO
A mixed oxide of titania-silica oxides (TixSiy oxides) was successfully prepared via the sol-gel technique from our previous work. The use of TixSiy oxides to improve the mechanical properties, photocatalytic efficiency, antibacterial property, permeability tests, and biodegradability of polylactic acid (PLA) was demonstrated in this study. The influence of different types and contents of TixSiy oxides on crystallization behavior, mechanical properties, thermal properties, and morphological properties was presented. In addition, the effect of using TixSiy oxides as a filler in PLA composites on these properties was compared with the use of titanium dioxide (TiO2), silicon dioxide (SiO2), and TiO2SiO2. Among the prepared biocomposite films, the PLA/TixSiy films showed an improvement in the tensile strength and Young's modulus (up to 5% and 31%, respectively) in comparison to neat PLA films. Photocatalytic efficiency to degrade methylene blue (MB), hydrolytic degradation, and in vitro degradation of PLA are significantly improved with the addition of TixSiy oxides. Furthermore, PLA with the addition of TixSiy oxides exhibited an excellent antibacterial effect on Gram-negative bacteria (Escherichia coli or E. coli) and Gram-positive bacteria (Staphylococcus aureus or S. aureus), indicating the improved antimicrobial effectiveness of PLA composites. Importantly, up to 5% TixSiy loading could promote more PLA degradation via the water absorption ability of mixed oxides. According to the research results, the PLA composite films produced with TixSiy oxide were transparent, capable of screening UV radiation, and exhibited superior antibacterial efficacy, making them an excellent food packaging material.