Mattel's ©Barbie: Preventing Plasticizers Leakage in PVC Artworks and Design Objects through Film-Forming Solutions.

The main conservation problem of p-PVC artworks is phthalate-based plasticizer migration. Phthalate migration from the bulk to the surface of the materials leads to the formation of a glossy and oily film on the outer layers, ultimately reducing the flexibility of the material. This study aimed to develop a removable coating for the preservation of contemporary artworks and design objects made of plasticized polyvinyl chloride (p-PVC). Several coatings incorporating chitosan, collagen, and cellulose ethers were assessed as potential barriers to inhibiting plasticizer migration. Analytical techniques including optical microscopy (OM), ultraviolet/visible/near-infrared spectroscopy (UV/Vis/NIR), Fourier transform infrared spectroscopy with attenuated total reflection (FTIR-ATR), and scanning electron microscopy (SEM) were utilized to evaluate the optical and chemical stability of selected coating formulations applied to laboratory p-PVC sheet specimens. Subsequently, formulations were tested on a real tangible example of a design object, ©Barbie doll, characterized by the prevalent issue of plasticizer migration. Furthermore, the results obtained with the tested formulations were evaluated by a group of conservators using a tailored survey. Finally, a suitable coating formulation capable of safeguarding plastic substrates was suggested.

Mattel's Barbie: Investigation of a Symbol-Analysis of Polymeric Matrices and Degradation Phenomena for Sixteen Dolls from 1959 to 1976.

Mattel's Barbie dolls are the most famous and iconic dolls since 1959. Today, they are being collected by individuals and often conserved in museum environments due to their cultural and historical significance reflecting everyday life and historical events. However, just like most museum objects made of plastics, both historical and more recent Barbies show evident degradation phenomena. Firstly, Barbies were made of plasticized polyvinyl chloride (PVC), affected by the migration of additives-mostly the plasticizers-from the bulk phase to the outermost layer, appearing as a tacky and glossy exudate. Over the years, Barbies' polymeric constituents were replaced with more stable ones, whose additives migration is limited compared to PVC, even though still occurring. Multispectral photography in visible (VIS) and ultraviolet (UV) light, microscopical observations in VIS and UV light, and Fourier Transform Infrared spectroscopy in the Attenuated Total Reflectance mode (FT-IR ATR) were performed to characterize the constituent materials of 15 Barbies produced between 1959 and 1976, bridging the information gap on their processing over the years. The micro-invasive multi-analytical approach also allowed for the characterization of the degradation products, permitting the reference of the exudated compound to the specific bulk polymer.