Difficulty in etching lithium niobate (LN) results in a relatively high propagation loss, which necessitates sophisticated processes to fabricate high-quality factor (Q) microresonators. Here, we fabricate a multimode microring resonator with an intrinsic Q of 6 × 106, which exhibits a propagation loss 50 times lower than that of a single-mode LN microring fabricated under the same process. Notably, the excitation of higher-order modes in the multimode microring is effectively suppressed by utilizing the Euler bend. The highly regular transmission spectrum of the resonator demonstrates a free spectral range (FSR) of 56â GHz. Based on this microresonator, we implement a bandpass microwave photonic filter with an ultra-narrow 3â dB bandwidth of 47.5â MHz and a large tuning range of 2-26.5â GHz. It can be anticipated that the combination of existing advanced etching techniques with this work will drive the propagation loss of a LN waveguide closer to the material absorption loss, significantly facilitating the optimization of performance in applications requiring ultrahigh-Q LN microresonators, such as frequency combs, frequency conversion, electro-optic modulation, and quantum photonics.
RESUMO
Perovskites have made remarkable advancements in optoelectronics owing to their high light absorption coefficient, tunable bandgap, and long charge diffusion. Nonetheless, the practical applications of Pb-based perovskites have been hindered by the instability and toxicity of Pb, especially in flexible electronics, which require high biosecurity and low toxicity. Hence, the development of stable Pb-free perovskite materials has gained increasing attention. In this study, we synthesized stable CsBi3I10 Pb-free perovskites outside the glovebox and improved the optoelectronic and mechanical performances of the CsBi3I10-based flexible devices through polyvinylcarbazole (PVK) doping. Flexible photodetectors with the device structure of PET/ITO/PEDOT:PSS/CsBi3I10:PVK/Au was fabricated. The results indicated that the introduction of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) reduced the surface roughness of the flexible PET substrate, while PVK doping further improved the surface smoothness of CsBi3I10 thin films, thereby enhancing the interfacial charge transportation. Moreover, PEDOT:PSS and PVK acted as stepwise hole transport layers in the photodetectors. The device demonstrated a maximum responsivity of 0.3 A/W, detectivity of 2.6 × 1011 Jones, and a response time of 102 µs at 650 nm. After subjecting it to 1000 bending tests, the light current retained 80% of its initial value. This study presents a universally applicable method for controlling the surface morphology of a flexible perovskite thin film.