RESUMO
Sn-rich solder joints in three-dimensional integrated circuits and their reliability issues, such as the electromigration (EM), thermomigration (TM), and thermomechanical fatigue (TMF), have drawn attention related to their use in electronic packaging. The Sn grain orientation is recognized as playing an important role in reliability issues due to its anisotropic diffusivity, mechanical properties, and coefficient of thermal expansion. This study reviews the effects of the Sn grain orientation on the EM, TM, and TMF in Sn-rich solder joints. The findings indicate that in spite of the failure modes dominated by the Sn grain orientation, the size and shape of the solder joint, as well as the Sn microstructures, such as the cycling twining boundary (CTB), single crystals, and misorientations of the Sn grain boundary, should be considered in more detail. In addition, we show that two methods, involving a strong magnetic field and seed crystal layers, can control the Sn grain orientations during the solidification of Sn-rich solder joints.
RESUMO
Fine grained and nanotwinned Au has many excellent properties and is widely used in electronic devices. We have fabricated [Formula: see text] preferred-oriented Au thin films by DC plating at 5 mA/cm2. Microstructure analysis of the films show a unique fine grain structure with a twin formation. Hardness tests performed on electroplated [Formula: see text] Au films show a hardness 47% greater than random and untwinned Au. We then achieved direct bonding between two Au [Formula: see text] surfaces operating at 200 °C for an hour in a vacuum oven. The highly-oriented [Formula: see text] nanotwinned Au films could be an ideal material in many gold products.
RESUMO
We have reported a method of fabricating (111)-orientated nanotwinned copper (nt-Cu) by direct current electroplating. X-ray analysis was performed for the samples annealed at 200 to 350 °C for an hour. X-ray diffraction indicates that the (200) signal intensity increases while (111) decreases. Abnormal grain growth normally results from transformation of surface energy or strain energy density. The average grain size increased from 3.8 µm for the as-deposited Cu films to 65-70 µm after the annealing at 250 °C for 1 h. For comparison, no significant grain growth behavior was observed by random Cu film after annealing for an hour. This research shows the potential for its broad electric application in interconnects and three-dimensional integrated circuit (3D IC) packaging.
RESUMO
We reported that highly (111)-oriented nanotwinned gold can be fabricated by periodical-reverse electroplating. The as-deposited films are shown to have a strong (111) preferred orientation, increasing with the reverse current time. The ratios of I(111)/I(220) and I(111)/I(200) in X-ray diffraction signals indicates a strong (111) preferred orientation. Using the advantage of the fast surface diffusion of (111) plane compared to the other planes of gold, we performed direct bonding with different thicknesses. Grain growth was observed over two films' interfaces to eliminate the bonding interface, when annealed at 250 °C for 1 h. Shear tests were performed to gain insight on the bonding quality. All the chips failed at either the silicon substrate or substrate-adhesion layer, showing possible higher strength than the tested maximum, 40.8 MPa.