RESUMO
Transition metal tellurides (TMTs) have been ideal materials for exploring exotic properties in condensed-matter physics, chemistry and materials science1-3. Although TMT nanosheets have been produced by top-down exfoliation, their scale is below the gram level and requires a long processing time, restricting their effective application from laboratory to market4-8. We report the fast and scalable synthesis of a wide variety of MTe2 (M = Nb, Mo, W, Ta, Ti) nanosheets by the solid lithiation of bulk MTe2 within 10 min and their subsequent hydrolysis within seconds. Using NbTe2 as a representative, we produced more than a hundred grams (108 g) of NbTe2 nanosheets with 3.2 nm mean thickness, 6.2 µm mean lateral size and a high yield (>80%). Several interesting quantum phenomena, such as quantum oscillations and giant magnetoresistance, were observed that are generally restricted to highly crystalline MTe2 nanosheets. The TMT nanosheets also perform well as electrocatalysts for lithium-oxygen batteries and electrodes for microsupercapacitors (MSCs). Moreover, this synthesis method is efficient for preparing alloyed telluride, selenide and sulfide nanosheets. Our work opens new opportunities for the universal and scalable synthesis of TMT nanosheets for exploring new quantum phenomena, potential applications and commercialization.
RESUMO
Understanding the reconstruction mechanism to rationally design cost-effective electrocatalysts for oxygen evolution reaction (OER) is still challenging. Herein, a defect-rich NiMoO4 precatalyst is used to explore its OER activity and reconstruction mechanism. In situ generated oxygen vacancies, distorted lattices, and edge dislocations expedite the deep reconstruction of NiMoO4 to form polycrystalline Ni (oxy)hydroxides for alkaline oxygen evolution. It only needs ≈230 and ≈285 mV to reach 10 and 100 mA cm-2, respectively. The reconstruction boosted by the redox of Ni is confirmed experimentally by sectionalized cyclic voltammetry activations at different specified potential ranges combined with ex situ characterization techniques. Subsequently, the reconstruction route is presented based on the acid-base electronic theory. Accordingly, the dominant contribution of the adsorbate evolution mechanism to reconstruction during oxygen evolution is revealed. This work develops a novel route to synthesize defect-rich materials and provides new tactics to investigate the reconstruction.
RESUMO
Proton exchange membrane water electrolysis is a highly promising hydrogen production technique for sustainable energy supply, however, achieving a highly active and durable catalyst for acidic water oxidation still remains a formidable challenge. Herein, we propose a local microenvironment regulation strategy for precisely tuning In-RuO2 /graphene (In-RuO2 /G) catalyst with intrinsic electrochemical activity and stability to boost acidic water oxidation. The In-RuO2 /G displays robust acid oxygen evolution reaction performance with a mass activity of 671â A gcat -1 at 1.5â V, an overpotential of 187â mV at 10â mA cm-2 , and long-lasting stability of 350â h at 100â mA cm-2 , which arises from the asymmetric Ru-O-In local structure interactions. Further, it is unraveled theoretically that the asymmetric Ru-O-In structure breaks the thermodynamic activity limit of the traditional adsorption evolution mechanism which significantly weakens the formation energy barrier of OOH*, thus inducing a new rate-determining step of OH* absorption. Therefore, this strategy showcases the immense potential for constructing high-performance acidic catalysts for water electrolyzers.
RESUMO
Owing to the significant latent heat generated at constant temperatures, phase change fibers (PCFs) have recently received much attention in the field of wearable thermal management. However, the phase change materials involved in the existing PCFs still experience a solid-liquid transition process, severely restricting their practicality as wearable thermal management materials. Herein, we, for the first time, developed intrinsically flexible PCFs (polyethylene glycol/4,4'-methylenebis(cyclohexyl isocyanate) fibers, PMFs) through polycondensation and wet-spinning process, exhibiting an inherent solid-solid phase transition property, adjustable phase transition behaviors, and outstanding knittability. The PMFs also present superior mechanical strength (28 MPa), washability (> 100 cycles), thermal cycling stability (> 2000 cycles), facile dyeability, and heat-induced recoverability, all of which are highly significant for practical wearable applications. Additionally, the PMFs can be easily recycled by directly dissolving them in solvents for reprocessing, revealing promising applications as sustainable materials for thermal management. Most importantly, the applicability of the PMFs was demonstrated by knitting them into permeable fabrics, which exhibit considerably improved thermal management performance compared with the cotton fabric. The PMFs offer great potential for intelligent thermal regulation in smart textiles and wearable electronics.
RESUMO
Electrooxidation of biomass-derived glycerol which is regarded as a main byproduct of industrial biodiesel production, is an innovative strategy to produce value-added chemicals, but currently showcases slow kinetics, limited Faraday efficiency, and unclear catalytic mechanism. Herein, we report high-efficiency electrooxidation of glycerol into formate via a Cu doped NiCo alloy catalyst supported on nickel foam (Cu-NiCo/NF) in a coupled system paired with nitrate reduction. The designed Cu-NiCo/NF delivers only 1.23 V vs. RHE at 10 mA cm-2, and a record Faraday efficiency of formate of 93.8%. The superior performance is ascribed to the rapid generation of NiIII-OOH and CoIII-OOH and favorable coupling of surface *O with reactive intermediates. Using Cu-NiCo/NF as a bifunctional catalyst, the coupled system synchronously produces NH3 and formate, showing 290 mV lower than the coupling of hydrogen evolution reaction, together with excellent long-term stability for up to 144 h. This work lays out new guidelines and reliable strategies from catalyst design to system coupling for biomass-derived electrochemical refinery.
RESUMO
Metallic Na is a promising metal anode for large-scale energy storage. Nevertheless, unstable solid electrolyte interphase (SEI) and uncontrollable Na dendrite growth lead to disastrous short circuit and poor cycle life. Through phase field and ab initio molecular dynamics simulation, we first predict that the sodium bromide (NaBr) with the lowest Na ion diffusion energy barrier among sodium halogen compounds (NaX, X=F, Cl, Br, I) is the ideal SEI composition to induce the spherical Na deposition for suppressing dendrite growth. Then, 1,2-dibromobenzene (1,2-DBB) additive is introduced into the common fluoroethylene carbonate-based carbonate electrolyte (the corresponding SEI has high mechanical stability) to construct a desirable NaBr-rich stable SEI layer. When the Na||Na3 V2 (PO4 )3 cell utilizes the electrolyte with 1,2-DBB additive, an extraordinary capacity retention of 94 % is achieved after 2000â cycles at a high rate of 10â C. This study provides a design philosophy for dendrite-free Na metal anode and can be expanded to other metal anodes.
RESUMO
Pursuing high areal energy density and developing scalable fabrication strategies of micro-batteries are the key for the progressive printed microelectronics. Herein, the scalable fabrication of multi-layer printable lithium ion micro-batteries (LIMBs) with ultrahigh areal energy density and exceptional flexibility is reported, based on highly conductive and mechanically stable inks by fully incorporating the polyurethane binders in dibasic esters with high-conducting additives of graphene and carbon nanotubes into active materials to construct a cross-linked conductive network. Benefiting from relatively higher electrical conductivity (≈7000 mS cm-1 ) and stably connected network of microelectrodes, the as-fabricated LIMBs by multi-layer printing display robust areal capacity of 398 µAh cm-2 , and remarkable areal energy density of 695 µWh cm-2 , which are much higher than most LIMBs reported. Further, the printed LIMBs show notable capacity retention of 88% after 3000 cycles, and outstanding flexibility without any structure degradation under various torsion states and folding angles. Importantly, a wearable smart bracelet, composed of a serially connected LIMBs pack, a temperature sensor, and a light-emitting diode, is realized for the automatic detection of body temperature. Therefore, this strategy of fabricating highly conductive and mechanically stable printable ink will open a new avenue for developing high-performance printable LIMBs for smart microelectronics.
Assuntos
Nanotubos de Carbono , Dispositivos Eletrônicos Vestíveis , Eletrônica , Tinta , Lítio/química , Nanotubos de Carbono/químicaRESUMO
The prosperity of smart portable microdevices urgently requires an advanced integrated microsystem equipped with cost-effective safe microbatteries and ultra-stable sensitive sensors. However, the practical application of smart microdevices is limited by complex active materials with single function. Here, the two-dimensional (2D) mesoporous nanosheets of polyaniline decorated on graphene with large specific surface area of 141 m2 g-1 , ample active sites, comparable conductivity, and ordered mesopores of 18 nm for a new-type co-planar integrated microsystem of zinc ion microbattery and gas sensor are developed. These unique triple-function mesoporous nanosheets are well proved for dendrite-free zinc anode with long cyclability (>500 h) and small overpotential (48 mV), a high performance cathode of zinc ion microbattery with outstanding volumetric capacity of 78 mAh cm-3 outperforming their counterparts reported, and a highly sensitive gas sensor with a resistance response (ΔR/R0 %) of 118% for 20 ppm NH3 . Moreover, the co-planar battery-sensor integrated microsystem exhibits superior mechanical stability and smart integration. Therefore, this work will open many opportunities to develop multifunctional 2D mesoporous materials for high performance smart integrated microsystems.
RESUMO
Modulation of A-site defects is crucial to the redox reactions on ABO3 perovskites for both clean air application and electrochemical energy storage. Herein we report a scalable one-pot strategy for in situ regulation of La vacancies (VLa ) in LaMnO3.15 by simply introducing urea in the traditional citrate process, and further reveal the fundamental relationship between VLa creation and surface lattice oxygen (Olatt ) activation. The underlying mechanism is shortened Mn-O bonds, decreased orbital ordering, promoted MnO6 bending vibration and weakened Jahn-Teller distortion, ultimately realizing enhanced Mn-3d and O-2p orbital hybridization. The LaMnO3.15 with optimized VLa exhibits order of magnitude increase in toluene oxidation and ca. 0.05â V versus RHE (reversible hydrogen electrode) increase of half-wave potential in oxygen reduction reaction (ORR). The reported strategy can benefit the development of novel defect-meditated perovskites in both heterocatalysis and electrocatalysis.
RESUMO
Guiding the lithium ion (Li-ion) transport for homogeneous, dispersive distribution is crucial for dendrite-free Li anodes with high current density and long-term cyclability, but remains challenging for the unavailable well-designed nanostructures. Herein, we propose a two-dimensional (2D) heterostructure composed of defective graphene oxide (GO) clipped on mesoporous polypyrrole (mPPy) as a dual-functional Li-ion redistributor to regulate the stepwise Li-ion distribution and Li deposition for extremely stable, dendrite-free Li anodes. Owing to the synergy between the Li-ion transport nanochannels of mPPy and the Li-ion nanosieves of defective GO, the 2D mPPy-GO heterostructure achieves ultralong cycling stability (1000â cycles), even tests at 0 and 50 °C, and an ultralow overpotential of 70â mV at a high current density of 10.0â mA cm-2 , outperforming most reported Li anodes. Furthermore, mPPy-GO-Li/LiCoO2 full batteries demonstrate remarkably enhanced performance with a capacity retention of >90 % after 450â cycles. Therefore, this work opens many opportunities for creating 2D heterostructures for high-energy-density Li metal batteries.
RESUMO
Switchable structured adhesion on rough surfaces is highly desired for a wide range of applications. Combing the advantages of gecko seta and creeper root, a switchable fibrillar adhesive composed of polyurethane (PU) as the backing layer and graphene/shape memory polymer (GSMP) as the pillar array is developed. The photothermal effect of graphene (under UV irradiation) changes GSMP micropillars into the viscoelastic state, allowing easy and intimate contact on surfaces with a wide range of roughness. By controlling the phase state of GSMP via UV irradiation during detachment, the GSMP micropillar array can be switched between the robust-adhesion state (UV off) and low-adhesion state (UV on). The state of GSMP micropillars determines the adhesion force capacity and the stress distribution at the detaching interface, and therefore the adhesion performance. The PU-GSMP adhesive achieves large adhesion strength (278 kPa), high switching ratio (29), and fast switching (10 s) at the same time. The results suggest a design principle for bioinspired structured adhesives, especially for reversible adhesion on surfaces with a wide range of roughness.
RESUMO
Free-standing 2D porous nanomaterials have attracted considerable interest as ideal candidates of 2D film electrodes for planar energy storage devices. Nevertheless, the construction of well-defined mesopore arrays parallel to the lateral surface, which facilitate fast in-plane ionic diffusion, is a challenge. Now, a universal interface self-assembly strategy is used for patterning 2D porous polymers, for example, polypyrrole, polyaniline, and polydopamine, with cylindrical mesopores on graphene nanosheets. The resultant 2D sandwich-structured nanohybrids are employed as the interdigital microelectrodes for the assembly of planar micro-supercapacitors (MSCs), which deliver outstanding volumetric capacitance of 102â F cm-3 and energy density of 2.3â mWh cm-3 , outperforming most reported MSCs. The MSCs display remarkable flexibility and superior integration for boosting output voltage and capacitance.
RESUMO
Scalable production of high-quality heteroatom-modified graphene is critical for microscale supercapacitors but remains a great challenge. Herein, we demonstrate a scalable, single-step electrochemical exfoliation of graphite into highly solution-processable fluorine-modified graphene (FG), achieved in an aqueous fluorine-containing neutral electrolyte, for flexible and high-energy-density ionogel-based microsupercapacitors (FG-MSCs). The electrochemically exfoliated FG nanosheets are characterized by atomic thinness, large lateral size (up to 12 µm), a high yield of >70% with ≤3 layers, and a fluorine doping of 3 at%, allowing for large-scale production of FG-MSCs. Our ionogel-based FG-MSCs deliver high energy density of 56 mWh cm-3, by far outperforming the most reported MSCs. Furthermore, the all-solid-state microdevices offer exceptional cyclability with â¼93% after 5000 cycles, robust mechanical flexibility with 100% of capacitance retention bended at 180°, and outstanding serial and parallel integration without the requirement of metal-based interconnects for high-voltage and high-capacitance output. Therefore, these FG-MSCs represent remarkable potential for electronics.
RESUMO
Nitrogen-enriched porous nanocarbon, graphene, and conductive polymers attract increasing attention for application in supercapacitors. However, electrode materials with a large specific surface area (SSA) and a high nitrogen doping concentration, which is needed for excellent supercapacitors, has not been achieved thus far. Herein, we developed a class of tetracyanoquinodimethane-derived conductive microporous covalent triazine-based frameworks (TCNQ-CTFs) with both high nitrogen content (>8 %) and large SSA (>3600â m2 g-1 ). These CTFs exhibited excellent specific capacitances with the highest value exceeding 380â F g-1 , considerable energy density of 42.8â Wh kg-1 , and remarkable cycling stability without any capacitance degradation after 10 000 cycles. This class of CTFs should hold a great potential as high-performance electrode material for electrochemical energy-storage systems.
RESUMO
Heteroatom doping of nanocarbon films can efficiently boost the pseudocapacitance of micro-supercapacitors (MSCs); however, wafer-scale fabrication of sulfur-doped graphene films with a tailored thickness and homogeneous doping for MSCs remains a great challenge. Here we demonstrate the bottom-up fabrication of continuous, uniform, and ultrathin sulfur-doped graphene (SG) films, derived from the peripherical trisulfur-annulated hexa-peri-hexabenzocoronene (SHBC), for ultrahigh-rate MSCs (SG-MSCs) with landmark volumetric capacitance. The SG film was prepared by thermal annealing of the spray-coated SHBC-based film, with assistance of a thin Au protecting layer, at 800 °C for 30 min. SHBC with 12 phenylthio groups decorated at the periphery is critical as a precursor for the formation of the continuous and ultrathin SG film, with a uniform thickness of â¼10.0 nm. Notably, the as-produced all-solid-state planar SG-MSCs exhibited a highly stable pseudocapacitive behavior with a volumetric capacitance of â¼582 F cm-3 at 10 mV s-1, excellent rate capability with a remarkable capacitance of 8.1 F cm-3 even at an ultrahigh rate of 2000 V s-1, ultrafast frequency response with a short time constant of 0.26 ms, and ultrahigh power density of â¼1191 W cm-3. It is noteworthy that these values obtained are among the best values for carbon-based MSCs reported to date.
RESUMO
Despite the intensive research efforts devoted to graphene fabrication over the past decade, the production of high-quality graphene on a large scale, at an affordable cost, and in a reproducible manner still represents a great challenge. Here, we report a novel method based on the controlled electrochemical exfoliation of graphite in aqueous ammonium sulfate electrolyte to produce graphene in large quantities and with outstanding quality. Because the radicals (e.g., HO(â¢)) generated from water electrolysis are responsible for defect formation on graphene during electrochemical exfoliation, a series of reducing agents as additives (e.g., (2,2,6,6-tetramethylpiperidin-1-yl)oxyl (TEMPO), ascorbic acid, and sodium borohydride) have been investigated to eliminate these radicals and thus control the exfoliation process. Remarkably, TEMPO-assisted exfoliation results in large graphene sheets (5-10 µm on average), which exhibit outstanding hole mobilities (â¼405 cm(2) V(-1) s(-1)), very low Raman I(D)/I(G) ratios (below 0.1), and extremely high carbon to oxygen (C/O) ratios (â¼25.3). Moreover, the graphene ink prepared in dimethylformamide can exhibit concentrations as high as 6 mg mL(-1), thus qualifying this material for intriguing applications such as transparent conductive films and flexible supercapacitors. In general, this robust method for electrochemical exfoliation of graphite offers great promise for the preparation of graphene that can be utilized in industrial applications to create integrated nanocomposites, conductive or mechanical additives, as well as energy storage and conversion devices.
RESUMO
Mass production of high-quality graphene sheets is essential for their practical application in electronics, optoelectronics, composite materials, and energy-storage devices. Here we report a prompt electrochemical exfoliation of graphene sheets into aqueous solutions of different inorganic salts ((NH4)2SO4, Na2SO4, K2SO4, etc.). Exfoliation in these electrolytes leads to graphene with a high yield (>85%, ≤3 layers), large lateral size (up to 44 µm), low oxidation degree (a C/O ratio of 17.2), and a remarkable hole mobility of 310 cm(2) V(-1) s(-1). Further, highly conductive graphene films (11 Ω sq(-1)) are readily fabricated on an A4-size paper by applying brush painting of a concentrated graphene ink (10 mg mL(-1), in N,N'-dimethylformamide). All-solid-state flexible supercapacitors manufactured on the basis of such graphene films deliver a high area capacitance of 11.3 mF cm(-2) and an excellent rate capability of 5000 mV s(-1). The described electrochemical exfoliation shows great promise for the industrial-scale synthesis of high-quality graphene for numerous advanced applications.
RESUMO
Two-dimensional (2D) materials show intriguing and diverse properties in different fields, stimulating chemists to develop synthetic and functional methodologies for producing solution-processable nanosheets on a large scale. However, it is still challenging to prepare 2D materials for industrial applications without sacrificing their lab-scale properties. Solid lithiation and exfoliation can achieve the hundred-gram-scale production of transition metal telluride nanosheets, making it one of the most effective strategies for mass production of 2D nanomaterials. In this Perspective, we highlight the advantages, propose the challenges, and discuss the opportunities of solid lithiation and exfoliation as a promising and commercially viable production method for 2D nanomaterials.
RESUMO
MXenes are promising materials for electrocatalysis due to their excellent metallic conductivity, hydrophilicity, high specific surface area, and excellent electrochemical properties. Herein, we summarize the recent advancement of MXene-based materials for electrocatalysis and highlight their key challenges and opportunities. In particular, this review emphasizes on the major design principles of MXene-based electrocatalysts, including (1) coupling MXene with active materials or heteroatomic doping to create highly active synergistic catalyst sites; (2) construction of 3D MXene structure or introducing interlayer spacers to increase active areas and form fast mass-charge transfer channel; and (3) protecting edge of MXene or in situ transforming the surface of MXene to stable active substance that inhibits the oxidation of MXene and then enhances the stability. Consequently, MXene-based materials exhibit outstanding performance for a variety of electrocatalytic reactions. Finally, the key challenges and promising prospects of the practical applications of MXene-based electrocatalysts are briefly proposed.
RESUMO
A supercapacitor is a potential electrochemical energy storage device with high-power density (PD) for driving flexible, smart, electronic devices. In particular, flexible supercapacitors (FSCs) have reliable mechanical and electrochemical properties and have become an important part of wearable, smart, electronic devices. It is noteworthy that the flexible electrode, electrolyte, separator and current collector all play key roles in overall FSCs. In this review, the unique mechanical properties, structural designs and fabrication methods of each flexible component are systematically classified, summarized and discussed based on the recent progress of FSCs. Further, the practical applications of FSCs are delineated, and the opportunities and challenges of FSCs in wearable technologies are proposed. The development of high-performance FSCs will greatly promote electricity storage toward more practical and widely varying fields. However, with the development of portable equipment, simple FSCs cannot satisfy the needs of integrated and intelligent flexible wearable devices for long durations. It is anticipated that the combining an FSC and a flexible power source such as flexible solar cells is an effective strategy to solve this problem. This review also includes some discussions of flexible self-powered devices.