Physicochemical characteristics of lignin-g-PMMA/PLA blend via atom transfer radical polymerization depending on the structural difference of organosolv lignin.

Lignin has different structural characteristics depending on the extraction conditions. In this study, three types of ethanol organosolv lignin (EOL) were produced under different extraction conditions involving the reaction temperature (140, 160, 180 °C), sulfuric acid concentration (0.5, 1, 1.5 %), and ethanol concentration (40, 60, 80 %) to compare the difference in properties when mixed with polylactic acid (PLA) matrix after atom transfer radical polymerization (ATRP). ATRP of EOL was conducted to improve its compatibility with PLA using methyl methacrylate (MMA) as a monomer. The molecular weight of each EOL increased significantly, and the glass transition temperature (Tg) decreased from approximately 150 to 110 °C. The EOL-g-PMMA copolymer exhibited a melting point (Tm), whereas EOL did not, implying that the thermoplasticity increased. The EOL-g-PMMA/PLA blend and film were prepared with 10 % of the copolymer in the PLA matrix. The tensile strength and strain of the blend were higher than those of unmodified organosolv lignin as the compatibility increased, and the UV transmittance was lower than that of neat PLA because of the UV protecting properties of EOL moiety.