Enhanced battery capacity and cycle life due to suppressed side reactions on the surface of Ni-rich LiNi0.8Co0.1Mn0.1O2 cathode materials coated with Co3(PO4)2.
J Colloid Interface Sci
; 670: 729-741, 2024 Sep 15.
Article
em En
| MEDLINE
| ID: mdl-38788440
ABSTRACT
This study explores a strategy to mitigate capacity fading in secondary batteries, which is primarily attributed to side reactions caused by residual Li impurities (LiOH or Li2CO3) on the surface of Ni-rich LiNi0.8Co0.1Mn0.1O2 (NCM811) layered cathode materials. By applying a 1.5 wt% Co3(PO4)2 coating, we successfully formed a thin and stable LiF cathode-electrolyte interface (CEI) layer, which resulted in decreased battery resistance and enhanced diffusion of Li+ ions within the electrolyte. This coating significantly improved the interface stability of NCM811, leading to superior battery performance. Specifically, the discharge capacity of uncoated NCM811 was 190 mA h g-1 at a charge of 4.3 V and a rate of 0.1C, whereas the 1.5Co3(PO4)2/NCM811 exhibited an increased capacity of 213 mA h g-1. Furthermore, the Co3(PO4)2 coating effectively reduced the levels of LiOH and Li2CO3 on the NCM811 surface to only 0.1 %, thereby minimizing adverse side reactions with the electrolyte salt (LiPF6), cation mixing between Ni2+ and Li+, and defects at the NCM811 interface. As a result, battery lifespan was significantly extended. This study presents a robust approach for enhancing battery stability and performance by efficiently reducing residual Li+ ions on the surface of NCM811 through strategic Co3(PO4)2 coating.
Texto completo:
1
Base de dados:
MEDLINE
Idioma:
En
Ano de publicação:
2024
Tipo de documento:
Article