Improvement of the Surface Properties of Polyether Ether Ketone via Arc Evaporation for Biomedical Applications.

Polyether ether ketone is a bioinert polymer, that is of high interest in research and medicine as an alternative material for the replacement of bone implants made of metal. The biggest deficit of this polymer is its hydrophobic surface, which is rather unfavorable for cell adhesion and thus leads to slow osseointegration. In order to address this drawback, 3D-printed and polymer extruded polyether ether ketone disc samples that were surface-modified with titanium thin films of four different thicknesses via arc evaporation were investigated and compared with non-modified disc samples. Depending on the modification time, the thickness of the coatings ranged from 40 nm to 450 nm. The 3D-printing process does not affect the surface or bulk properties of polyether ether ketone. It turned out that the chemical composition of the coatings obtained did not depend on the type of substrate. Titanium coatings contain titanium oxide and have an amorphous structure. Microdroplets formed on the sample surfaces during treatment with an arc evaporator contain a rutile phase in their composition. Surface modification of the samples via arc evaporation resulted in an increase in the arithmetic mean roughness from 20 nm to 40 nm for the extruded samples and from 40 nm to 100 nm for the 3D-printed samples, with the mean height difference increasing from 100 nm to 250 nm and from 140 nm to 450 nm. Despite the fact that the hardness and reduced elastic modulus of the unmodified 3D-printed samples (0.33 GPa and 5.80 GPa) are higher than those of the unmodified extruded samples (0.22 GPa and 3.40 GPa), the surface properties of the samples after modification are approximately the same. The water contact angles of the polyether ether ketone sample surfaces decrease from 70° to 10° for the extruded samples and from 80° to 6° for the 3D-printed samples as the thickness of the titanium coating increases, making this type of coating promising for biomedical applications.

Antibacterial Calcium Phosphate Coatings for Biomedical Applications Fabricated via Micro-Arc Oxidation.

A promising method for improving the functional properties of calcium-phosphate coatings is the incorporation of various antibacterial additives into their structure. The microbial contamination of a superficial wound is inevitable, even if the rules of asepsis and antisepsis are optimally applied. One of the main problems is that bacteria often become resistant to antibiotics over time. However, this does not apply to certain elements, chemical compounds and drugs with antimicrobial properties. In this study, the fabrication and properties of zinc-containing calcium-phosphate coatings that were formed via micro-arc oxidation from three different electrolyte solutions are investigated. The first electrolyte is based on calcium oxide, the second on hydroxyapatite and the third on calcium acetate. By adding zinc oxide to the three electrolyte solutions, antibacterial properties of the coatings are achieved. Although the same amount of zinc oxide has been added to each electrolyte solution, the zinc concentration in the coatings obtained vary greatly. Furthermore, this study investigates the morphology, structure and chemical composition of the coatings. The antibacterial properties of the zinc-containing coatings were tested toward three strains of bacteria-Staphylococcus aureus, methicillin-resistant Staphylococcus aureus and Pseudomonas aeruginosa. Coatings of calcium acetate and zinc oxide contained the highest amount of zinc and displayed the highest zinc release. Moreover, coatings containing hydroxyapatite and zinc oxide show the highest antibacterial activity toward Pseudomonas aeruginosa, and coatings containing calcium acetate and zinc oxide show the highest antibacterial activities toward Staphylococcus aureus and methicillin-resistant Staphylococcus aureus.

Biodegradable magnesium fuel-based Janus micromotors with surfactant induced motion direction reversal.

The speed and motion directionality of bubble-propelled micromotors is dependent on bubble lifetime, bubble formation frequency and bubble stabilization. Absence and presence of bubble stabilizing agents should significantly influence speed and propulsion pattern of a micromotor, especially for fast-diffusing molecules like hydrogen. This study demonstrates a fully biodegradable Janus structured micromotor, propelled by hydrogen bubbles generated by the chemical reaction between hydrochloric acid and magnesium. Six different concentrations of hydrochloric acid and five different concentrations of the surfactant Triton X-100 were tested, which also cover the critical micelle concentration at a pH corresponding to an empty stomach. The Janus micromotor reverses its propulsion direction depending on the availability and concentration of a surfactant. Upon surfactant-free condition, the Janus micromotor is propelled by bubble cavitation, causing the micromotor to be pulled at high speed for short time intervals into the direction of the imploding bubble and thus backwards. In case of available surfactant above the critical micelle concentration, the Janus micromotor is pushed forward by the generated bubbles, which emerge at high frequency and form a bubble trail. The finding of the propulsion direction reversal effect demonstrates the importance to investigate the motion properties of artificial micromotors in a variety of different environments prior to application, especially with surfactants, since biological media often contain large amounts of surface-active components.

Polyether Ether Ketone Coated with Ultra-Thin Films of Titanium Oxide and Zirconium Oxide Fabricated by DC Magnetron Sputtering for Biomedical Application.

Recently, polyether ether ketone has raised increasing interest in research and industry as an alternative material for bone implants. This polymer also has some shortcomings, as it is bioinert and its surface is relatively hydrophobic, causing poor cell adhesion and therefore slow integration with bone tissue. In order to improve biocompatibility, the surface of polyether ether ketone-based implants should be modified. Therefore, polished disc-shaped polyether ether ketone samples were surface-modified by direct current magnetron sputtering with ultrathin titanium and zirconium coatings (thickness < 100 nm). The investigation results show a uniform distribution of both types of coatings on the sample surfaces, where the coatings mostly consist of titanium dioxide and zirconium dioxide. Differential scanning calorimetry revealed that the crystalline structure of the polyether ether ketone substrates was not changed by the coating deposition. Both coatings are amorphous, as shown by X-ray diffraction investigations. The roughness of both coating types increases with increasing coating thickness, which is beneficial for cell colonization. The coatings presented and investigated in this study improve wettability, increasing surface energies, in particular the polar component of the surface energies, which, in turn, are important for cell adhesion.