ABSTRACT
Modern technology has enabled the isolation of nanocellulose from plant-based fibers, and the current trend focuses on utilizing nanocellulose in a broad range of sustainable materials applications. Water is generally seen as a detrimental component when in contact with nanocellulose-based materials, just like it is harmful for traditional cellulosic materials such as paper or cardboard. However, water is an integral component in plants, and many applications of nanocellulose already accept the presence of water or make use of it. This review gives a comprehensive account of nanocellulose-water interactions and their repercussions in all key areas of contemporary research: fundamental physical chemistry, chemical modification of nanocellulose, materials applications, and analytical methods to map the water interactions and the effect of water on a nanocellulose matrix.
ABSTRACT
Different cellulose nanocrystal (CNC) forms (dried vs never-dried) can lead to different degrees of CNC reassembly, the formation of nanofibril-like structures, in nanocomposite latex-based pressure-sensitive adhesive (PSA) formulations. CNC reassembly is also affected by CNC sonication and loading as well as the protocol used for CNC addition to the polymerization. In this study, carboxylated CNCs (cCNCs) were incorporated into a seeded, semibatch, 2-ethylhexyl acrylate/methyl methacrylate/styrene emulsion polymerization and cast as pressure-sensitive adhesive (PSA) films. The addition of CNCs led to a simultaneous increase in tack strength, peel strength, and shear adhesion, avoiding the typical trade-off between the adhesive and cohesive strength. Increased CNC reassembly resulted from the use of dried, redispersed, and sonicated cCNCs, along with increased cCNC loading and addition of the cCNCs at the seed stage of the polymerization. The increased degree of CNC reassembly was shown to significantly increase the shear adhesion by enhancing the elastic modulus of the PSA films.
Subject(s)
Adhesives , Cellulose , Latex , Nanoparticles , Cellulose/chemistry , Adhesives/chemistry , Nanoparticles/chemistry , Latex/chemistry , Polymerization , Nanocomposites/chemistry , PressureABSTRACT
Microplastics are an emerging anthropogenic pollutant risk with a significant body of research dedicated to understanding the implications further. To generate the databases required to characterize the impact of microplastics on our environment, and improve recovery and recycling of current plastic materials, we need rapid, in-line characterization that can distinguish individual polymer types. Here, autofluorescence spectroscopy was investigated as an alternative characterization method to the current leading techniques based on vibrational spectroscopy. It was confirmed that the autofluorescence of seven common textile polymers (acrylic, polyester, nylon, polyethylene, polypropylene, cellulose/cotton, wool) arose due to the cluster-triggered emission phenomenon. Both simulated polymer aging via photooxidation and dyeing of the polymers were found to affect the resultant autofluorescence spectra. A total of 1485 spectra from 39 unique sample groups (polymer type, colour, and degree of photooxidation) were analysed via machine learning (k-means cluster analysis). Correct identification of the polymer type was achieved in 71% of the cases from only eight input values (normalized intensity values at three autofluorescence emission wavelengths, the total autofluorescence emission intensity, the sample RGB colour values, and the sample shape). This represents a significant step towards automated polymer identification at the sub-second time scales required for the in-line characterization of microplastics.
ABSTRACT
Cellulose nanocrystals (CNCs) are sustainable particles that are effective at stabilizing emulsions by adsorbing at droplet interfaces and providing a steric barrier to coalescence. However, CNCs have surface charges that reduce the coverage of the emulsion droplets due to the electrostatic repulsion between CNCs. In such cases, adding salt is a typical (and straightforward) way to adjust the formulation so that the charges are screened, allowing increased coverage of the droplets. At the outset of this work, we hypothesized that characterization of the interfacial tension and interfacial shear rheology of the oil-water interface would be correlated to interfacial coverage and therefore predictive of the optimal salt concentration for emulsion stability. Included in the methods section as a useful reference to others is the presentation of a detailed derivation for the equations needed to compute interfacial shear moduli in a custom, double-gap geometry. In contrast to our hypothesis, we found that interfacial tension did not correlate well with emulsion stability and that the native surface-active compounds in corn oil overwhelmed any influence of the CNCs on the interfacial tension. Additionally, we found that interfacial shear rheology (which can be painstakingly difficult to measure) was not a useful tool for formulating these emulsions. This is because at commonly used concentrations of CNCs, the bulk rheology is increased to a much greater degree than that of the interface, making the details of the interfacial rheology unimportant. Finally, we found that at concentrations of CNCs that are typical in industrial processes, characterizing the bulk viscoelastic properties of the aqueous suspending phase without added oil (a relatively simple measurement) is sufficient to predict the influence of NaCl concentration on charge screening between the CNCs and, by extension, increased surface coverage of droplets for greater emulsion stability.
ABSTRACT
The scale of production of cellulose nanocrystals (CNCs) has increased dramatically to meet the growing demand for sustainably sourced materials. This work defines the colloidal stability window for commercially produced carboxylated CNCs (DextraCel) compared to the more traditional sulfated CNCs. Phase diagrams showing the stable, reversibly agglomerated, irreversibly aggregated/sedimented, and colloidal glass "zones" as a function of suspension pH, ionic strength, CNC surface charge content, counterion, and concentration are presented. The pKa of carboxylated CNCs was measured to be 5.1, and suspensions of carboxylated CNCs (0.5-1.5 wt %) were visually stable from pH 3 to 11 (without salt). Carboxylated CNCs were highly sensitive to ionic strength, demonstrating some agglomeration with as little as 5 mM NaCl, supporting that weak acid surface groups and lower charge contents make CNCs more sensitive to solution conditions. Surface charge content had the greatest influence on colloidal stability followed by the counterion; carboxylated CNCs were more stable in the "as-received" sodium form, whereas sulfated CNCs had improved stability in acid form after ion exchange. The stability of carboxylated CNCs with industrially relevant additives (ionic and nonionic surfactants and initiators) was also investigated. Less concentrated suspensions were more colloidally stable, emphasizing that characterization and processing of CNCs favor dilute conditions. If carboxylated CNCs are subjected to conditions outside of their colloidal stability window, simple dilution or pH adjustment does not return them to colloidally stable discrete nanoparticles; however, ultrasonication can redisperse agglomerates. This study offers guidelines for handling carboxylated CNCs to broaden the range of products that can be improved by their incorporation.
ABSTRACT
PURPOSE: Intratracheal delivery and consistent dosing of dry powder vaccines is especially challenging in mice. To address this issue, device design of positive pressure dosators and actuation parameters were assessed for their impacts on powder flowability and in vivo dry powder delivery. METHODS: A chamber-loading dosator assembled with stainless-steel, polypropylene or polytetrafluoroethylene needle-tips was used to determine optimal actuation parameters. Powder loading methods including tamp-loading, chamber-loading and pipette tip-loading were compared to assess performance of the dosator delivery device in mice. RESULTS: Available dose was highest (45%) with a stainless-steel tip loaded with an optimal mass and syringe air volume, primarily due to the ability of this configuration to dissipate static charge. However, this tip encouraged more agglomeration along its flow path in the presence of humidity and was too rigid for intubation of mice compared to a more flexible polypropylene tip. Using optimized actuation parameters, the polypropylene pipette tip-loading dosator achieved an acceptable in vivo emitted dose of 50% in mice. After administering two doses of a spray dried adenovirus encapsulated in mannitol-dextran, high bioactivity was observed in excised mouse lung tissue three days post-infection. CONCLUSIONS: This proof-of-concept study demonstrates for the first time that intratracheal delivery of a thermally stable, viral-vectored dry powder can achieve equivalent bioactivity to the same powder, reconstituted and delivered intratracheally. This work may guide the design and device selection process for murine intratracheal delivery of dry powder vaccines to help progress this promising area of inhalable therapeutics.
Subject(s)
Biological Products , Animals , Mice , Administration, Inhalation , Powders , Polypropylenes , Steel , Dry Powder Inhalers , Particle Size , AerosolsABSTRACT
Blended films comprising poly(butyl acrylate) (PBA)-grafted cellulose nanocrystals (CNCs) and poly(3-hexylthiophene) (P3HT), exhibited more intense photoluminescence (PL) and longer PL emission lifetimes compared to pristine P3HT films. Optical absorption and photoluminescence spectra indicated reduced torsional disorder i.e. enhanced backbone planarity in the P3HT@CNC blended composites compared to the bare P3HT. Such molecule-level geometrical modification resulted in both smaller interchain and higher intrachain exciton bandwidth in the blended composites compared to the bare P3HT, because of reduced interchain interactions and enhanced intrachain order. These results indicate a potential switch of the aggregation behavior from dominant H-aggregates to J-aggregates, supported by Raman spectroscopy. The reorganization of micromolecular structure and concomitant macroscopic aggregation of the conjugated polymer chains resulted in a longer conjugation length for the P3HT@CNC blended composites compared to the bare P3HT. Additionally, this nanoscale morphological change produced a reduction in the highest occupied molecular orbital (HOMO)-lowest unoccupied molecular orbital (LUMO) energy gap of the blends, evidenced from optical absorption spectra. Classical molecular dynamics simulation studies predicted the probability of enhanced planarity in the polymer backbone following interactions with CNC surfaces. Theoretical results from density functional theory calculations corroborate the experimentally observed reduction of optical bandgap in the blends compared to bare P3HT. The blended composite outperformed the bare P3HT in nitro-group PL sensing tests with a pronounced difference in the reaction kinetics. While the PL quenching dynamics for bare P3HT followed Stern-Volmer kinetics, the P3HT@CNC blended composite exhibited a drastic deviation from the same. This work shows the potential of a functionalized rod-like biopolymer in tuning the optoelectronic properties of a technologically important polymeric organic semiconductor through control of the nanoscale morphology.
ABSTRACT
PURPOSE: Thermally stable, spray dried vaccines targeting respiratory diseases are promising candidates for pulmonary delivery, requiring careful excipient formulation to effectively encapsulate and protect labile biologics. This study investigates the impact of dextran mass ratio and molecular weight on activity retention, thermal stability and aerosol behaviour of a labile adenoviral vector (AdHu5) encapsulated within a spray dried mannitol-dextran blend. METHODS: Comparing formulations using 40 kDa or 500 kDa dextran at mass ratios of 1:3 and 3:1 mannitol to dextran, in vitro quantification of activity losses and powder flowability was used to assess suitability for inhalation. RESULTS: Incorporating mannitol in a 1:3 ratio with 500 kDa dextran reduced viral titre processing losses below 0.5 log and displayed strong thermal stability under accelerated aging conditions. Moisture absorption and agglomeration was higher in dextran-rich formulations, but under low humidity the 1:3 ratio with 500 kDa dextran powder had the lowest mass median aerodynamic diameter (4.4 µm) and 84% emitted dose from an intratracheal dosator, indicating strong aerosol performance. CONCLUSIONS: Overall, dextran-rich formulations increased viscosity during drying which slowed self-diffusion and favorably hindered viral partitioning at the particle surface. Reducing mannitol content also minimized AdHu5 exclusion from crystalline regions that can force the vector to air-solid interfaces where deactivation occurs. Although increased dextran molecular weight improved activity retention at the 1:3 ratio, it was less influential than the ratio parameter. Improving encapsulation ultimately allows inhalable vaccines to be prepared at higher potency, requiring less powder mass per inhaled dose and higher delivery efficiency.
Subject(s)
Excipients , Vaccines , Administration, Inhalation , Aerosols/chemistry , Dextrans/chemistry , Dry Powder Inhalers , Excipients/chemistry , Mannitol/chemistry , Particle Size , Powders/chemistryABSTRACT
The demand for industrially produced cellulose nanocrystals (CNCs) has been growing since 2012, when CelluForce Inc. opened its inaugural demonstration plant with a production capacity of 1 tonne per day. Currently, there are 10 industrial CNC producers worldwide, each producing a unique material. Thus, academic researchers and commercial users alike must consider the properties of all available CNCs and carefully select the material which will optimize the performance of their desired application. To support these efforts, this article presents a thorough characterization of four new industrially produced CNCs including sulfated CNCs from NORAM Engineering and Constructors Ltd. (in cooperation with InnoTech Alberta and Alberta-Pacific Forest Industries Inc.) and Melodea Ltd., as well as carboxylated CNCs from Anomera Inc. and Blue Goose Biorefineries Inc. These materials were benchmarked against typical lab-made, sulfated CNCs. While all CNCs were similar in size, shape, crystallinity, and suspension quality, the sulfated CNCs had a higher surface charge density than their carboxylated counterparts, leading to higher colloidal stability. Additionally, significant differences in the rheological profiles of aqueous CNC suspensions, as well as CNC thermal stability and self-assembly behavior, were observed. As such, this article highlights both the subtle and significant differences between five CNC types and acts as a guide for end-users looking to optimize the performance of CNC-based materials.
Subject(s)
Cellulose , Nanoparticles , Benchmarking , Suspensions , WaterABSTRACT
The trend to replace petroleum-based products with sustainable alternatives has shifted research efforts toward plant-based materials such as cellulose nanocrystals (CNCs). CNCs show promise in numerous applications (e.g., composites and rheological modifiers); however, maximizing their performance often requires surface modifications with complex chemistries and purification steps. Presented here is a novel surface modification method with the potential to tune CNC properties through the in situ deposition of cellulose phosphate oligosaccharides during CNC production. This was achieved by leveraging the selective solubility of oligosaccharides, which are soluble at a low pH (during the CNC hydrolysis) yet become insoluble and precipitate onto CNC surfaces upon increasing pH during quenching. Oligosaccharide-coated CNCs demonstrated subtle changes including higher surface charge densities and lower water adsorption capacities and viscosities than their unmodified counterparts. CNC surface coverage was tuned by controlling the oligosaccharide degree of polymerization. Overall, this fundamental study introduces an easily scalable modification route that opens the door for expanded CNC functionality and applications.
Subject(s)
Cellulose , Nanoparticles , Oligosaccharides , Polymerization , WaterABSTRACT
Hydrophobic polymer-grafted cellulose nanocrystals (CNCs) were produced via surface-initiated atom-transfer radical polymerization (SI-ATRP) in two different solvents to examine the role of reaction media on the extent of surface modification. Poly(butyl acrylate)-grafted CNCs were synthesized in either dimethylformamide (DMF) (D-PBA-g-CNCs) or toluene (T-PBA-g-CNCs) alongside a free polymer from a sacrificial initiator. The colloidal stability of unmodified CNCs, initiator-modified CNCs, and PBA-g-CNCs in water, DMF, and toluene was evaluated by optical transmittance. The enhanced colloidal stability of initiator-modified CNCs in DMF led to improved accessibility to initiator groups during polymer grafting; D-PBA-g-CNCs had 30 times more grafted chains than T-PBA-g-CNCs, determined by thermogravimetric and elemental analysis. D-PBA-g-CNCs dispersed well in toluene and were hydrophobic with a water contact angle of 124° (for polymer grafts > 13 kDa) compared to 25° for T-PBA-g-CNCs. The cellulose crystal structure was preserved, and individual nanoparticles were retained when grafting was carried out in either solvent. This work highlights that optimizing CNC colloidal stability prior to grafting is more crucial than solvent-polymer compatibility to obtain high graft densities and highly hydrophobic CNCs via SI-ATRP.
Subject(s)
Cellulose , Nanoparticles , Hydrophobic and Hydrophilic Interactions , Polymerization , PolymersABSTRACT
The hydrophilic polymer poly[2-(2-(2-methoxy ethoxy)ethoxy)ethylacrylate] (POEG3A) was grafted onto the reducing end-groups (REGs) of cellulose nanocrystal (CNC) allomorphs, and their liquid crystalline properties were investigated. The REGs on CNCs extracted from cellulose I (CNC-I) are exclusively located at one end of the crystallite, whereas CNCs extracted from cellulose II (CNC-II) feature REGs at both ends of the crystallite, so that grafting from the REGs affords asymmetrically and symmetrically decorated CNCs, respectively. To confirm the REG modification, several complementary analytical techniques were applied. The grafting of POEG3A onto the CNC REGs was evidenced by Fourier transform infrared spectroscopy, atomic force microscopy, and the coil-globule conformational transition of this polymer above 60 °C, i.e., its lower critical solution temperature. Furthermore, we investigated the self-assembly of end-tethered CNC-hybrids into chiral nematic liquid crystalline phases. Above a critical concentration, both end-grafted CNC allomorphs form chiral nematic tactoids. The introduction of POEG3A to CNC-I does not disturb the surface of the CNCs along the rods, allowing the modified CNCs to approach each other and form helicoidal textures. End-grafted CNC-II formed chiral nematic tactoids with a pitch observable by polarized optical microscopy. This is likely due to their increase in hydrodynamic radius or the introduced steric stabilization of the end-grafted polymer.
Subject(s)
Liquid Crystals , Nanoparticles , Cellulose , Hydrophobic and Hydrophilic Interactions , PolymersABSTRACT
Thermoresponsive hydrogels present unique properties, such as tunable mechanical performance or changes in volume, which make them attractive for applications including wound healing dressings, drug delivery vehicles, and implants, among others. This work reports the implementation of bioinspired thermoresponsive hydrogels composed of xyloglucan (XG) and cellulose nanocrystals (CNCs). Starting from tamarind seed XG (XGt), thermoresponsive XG was obtained by enzymatic degalactosylation (DG-XG), which reduced the galactose residue content by â¼50% and imparted a reversible thermal transition. XG with native composition and comparable molar mass to DG-XG was produced by an ultrasonication treatment (XGu) for a direct comparison of behavior. The hydrogels were prepared by simple mixing of DG-XG or XGu with CNCs in water. Phase diagrams were established to identify the ratios of DG-XG or XGu to CNCs that yielded a viscous liquid, a phase-separated mixture, a simple gel, or a thermoresponsive gel. Gelation occurred at a DG-XG or XGu to CNC ratio higher than that needed for the full surface coverage of CNCs and required relatively high overall concentrations of both components (tested concentrations up to 20 g/L XG and 30 g/L CNCs). This is likely a result of the increase in effective hydrodynamic volume of CNCs due to the formation of XG-CNC complexes. Investigation of the adsorption behavior indicated that DG-XG formed a more rigid layer on CNCs compared to XGu. Rheological properties of the hydrogels were characterized, and a reversible thermal transition was found for DG-XG/CNC gels at 35 °C. This thermoresponsive behavior provides opportunities to apply this system widely, especially in the biomedical field, where the mechanical properties could be further tuned by adjusting the CNC content.
Subject(s)
Cellulose , Nanoparticles , Glucans , Hydrogels , XylansABSTRACT
When cellulose nanocrystals (CNCs) are isolated from cellulose microfibrils, the parallel arrangement of the cellulose chains in the crystalline domains is retained so that all reducing end-groups (REGs) point to one crystallite end. This permits the selective chemical modification of one end of the CNCs. In this study, two reaction pathways are compared to selectively attach atom-transfer radical polymerization (ATRP) initiators to the REGs of CNCs, using reductive amination. This modification further enabled the site-specific grafting of the anionic polyelectrolyte poly(sodium 4-styrenesulfonate) (PSS) from the CNCs. Different analytical methods, including colorimetry and solution-state NMR analysis, were combined to confirm the REG-modification with ATRP-initiators and PSS. The achieved grafting yield was low due to either a limited conversion of the CNC REGs or side reactions on the polymerization initiator during the reductive amination. The end-tethered CNCs were easy to redisperse in water after freeze-drying, and the shear birefringence of colloidal suspensions is maintained after this process.
Subject(s)
Cellulose , Nanoparticles , Polymerization , WaterABSTRACT
Cellulose nanocrystals (CNCs), a sustainable nanomaterial, are in situ incorporated into emulsion-based pressure-sensitive adhesives (PSAs). Commercially available CNCs with different surface hydrophilicity and surface charge (CNC101 and CNC103 from CelluForce) are used to explore their role in PSA property modification. Viscosity measurements and atomic force microscopy reveal differences in degree of association between the CNCs and the latex particles depending on the surface properties of the CNCs. The more hydrophilic and higher surface charge CNCs (CNC101) show less association with the latex particles. Dynamic strain sweep tests are used to analyze the strain-softening of the nanocomposites based on CNC type and loading. The CNC101 nanocomposites soften at lower strains than their CNC103 counterparts. This behavior is confirmed via dynamic frequency tests and modeling of the nanocomposites' storage moduli, which suggest the formation of CNC aggregates of, on average, 3.8 CNC101 and 1.3 CNC103 nanoparticles. Finally, PSA properties, i.e., tack, peel strength, and shear strength, simultaneously increase upon addition of both CNC types, although to different extents. The relationship between the PSA properties and CNC surface properties confirms that the less hydrophilic CNCs lead to improved CNC dispersion in the PSA films and therefore, enhance PSA properties.
Subject(s)
Nanocomposites , Nanoparticles , Adhesives , Cellulose , Hydrophobic and Hydrophilic InteractionsABSTRACT
Emulsion polymerized latex-based pressure-sensitive adhesives (PSAs) are more environmentally benign because they are synthesized in water but often underperform compared to their solution polymerized counterparts. Studies have shown a simultaneous improvement in the tack, and peel and shear strength of various acrylic PSAs upon the addition of cellulose nanocrystals (CNCs). This work uses atomic force microscopy (AFM) to examine the role of CNCs in (i) the coalescence of hydrophobic 2-ethyl hexyl acrylate/n-butyl acrylate/methyl methacrylate (EHA/BA/MMA) latex films and (ii) as adhesion modifiers over multiple length scales. Thin films with varying solids content and CNC loading were prepared by spin coating. AFM revealed that CNCs lowered the solids content threshold for latex particle coalescence during film formation. This improved the cohesive strength of the films, which was directly reflected in the increased shear strength of the EHA/BA/MMA PSAs with increasing CNC loading. Colloidal probe AFM indicated that the nano-adhesion of thicker continuous latex films increased with CNC loading when measured over small contact areas where the effect of surface roughness was negligible. Conversely, the beneficial effects of the CNCs on macroscopic PSA tack and peel strength were outweighed by the effects of increased surface roughness with increasing CNC loading over larger surface areas. This highlights that CNCs can improve both cohesive and adhesive PSA properties; however, the effects are most pronounced when the CNCs interact favourably with the latex polymer and are uniformly dispersed throughout the adhesive film. This article is part of the theme issue 'Bio-derived and bioinspired sustainable advanced materials for emerging technologies (part 1)'.
Subject(s)
Cellulose , Nanoparticles , Adhesives , Hydrophobic and Hydrophilic Interactions , PolymerizationABSTRACT
Interactions between polysaccharides, specifically between cellulose and hemicelluloses like xyloglucan (XG), govern the mechanical properties of the plant cell wall. This work aims to understand how XG molecular weight (MW) and the removal of saccharide residues impact the elastic modulus of XG-cellulose materials. Layered sub-micrometer-thick films of cellulose nanocrystals (CNCs) and XG were employed to mimic the structure of the plant cell wall and contained either (1) unmodified XG, (2) low MW XG produced by ultrasonication (USXG), or (3) XG with a reduced degree of galactosylation (DGXG). Their mechanical properties were characterized through thermal shrinking-induced buckling. Elastic moduli of 19 ± 2, 27 ± 1, and 75 ± 6 GPa were determined for XG-CNC, USXG-CNC, and DGXG-CNC films, respectively. The conformation of XG adsorbed on CNCs is influenced by MW, which impacts mechanical properties. To a greater degree, partial degalactosylation, which is known to increase XG self-association and binding capacity of XG to cellulose, increases the modulus by fourfold for DGXG-CNC films compared to XG-CNC. Films were also buckled while fully hydrated by using the thermal shrinking method but applying the heat using an autoclave; the results implied that hydrated films are thicker and softer, exhibiting a lower elastic modulus compared to dry films. This work contributes to the understanding of structure-function relationships in the plant cell wall and may aid in the design of tunable biobased materials for applications in biosensing, packaging, drug delivery, and tissue engineering.
Subject(s)
Cellulose , Nanoparticles , Glucans , XylansABSTRACT
This study investigates the adsorption of a block copolymer composed of a poly(2-(dimethylamino)ethyl methacrylate) (PDMAEMA) cationic polyelectrolyte and a poly(di(ethylene glycol) methyl ethermethacrylate) (PDEGMA) on oxidized cellulose nanocrystals (TO-CNCs) to produce hydrogels. PDMEAMA- b-PDEGMA was synthesized by atom-transfer radical polymerization. The extent and dynamics of the adsorption of PDMAEMA- b-PDEGMA on TO-CNCs were determined by electromechanical microbalance and optical techniques. Electrostatic adsorption was identified on TO-CNCs with the quaternized block copolymer. Small-angle neutron scattering experiments were performed to investigate the polymer behavior on the TO-CNC surfaces. Depending on the temperature, block copolymer induces the aggregation of nanocrystals after adsorption by connecting CNCs bundles with block copolymer chains. A reversible liquid-to-gel transition, triggered by temperature, was clearly detected by rheological measurements for the copolymer-CNC mixtures. At the optimal copolymer to CNC ratio the viscosity increased by 4 orders of magnitude at low shear rates. These stimuli-responsive CNC-based materials could be used as injectable biomedical systems.
Subject(s)
Cellulose/chemistry , Hydrogels/chemistry , Nanoparticles/chemistry , Rheology , Adsorption , Methacrylates/chemistry , Nylons/chemistryABSTRACT
A new family of materials comprised of cellulose, cellulose nanomaterials (CNMs), having properties and functionalities distinct from molecular cellulose and wood pulp, is being developed for applications that were once thought impossible for cellulosic materials. Commercialization, paralleled by research in this field, is fueled by the unique combination of characteristics, such as high on-axis stiffness, sustainability, scalability, and mechanical reinforcement of a wide variety of materials, leading to their utility across a broad spectrum of high-performance material applications. However, with this exponential growth in interest/activity, the development of measurement protocols necessary for consistent, reliable and accurate materials characterization has been outpaced. These protocols, developed in the broader research community, are critical for the advancement in understanding, process optimization, and utilization of CNMs in materials development. This review establishes detailed best practices, methods and techniques for characterizing CNM particle morphology, surface chemistry, surface charge, purity, crystallinity, rheological properties, mechanical properties, and toxicity for two distinct forms of CNMs: cellulose nanocrystals and cellulose nanofibrils.
ABSTRACT
Recent developments in ionic liquid electrolytes for cellulose or biomass dissolution has also allowed for high-resolution 1H and 13C NMR on very high molecular weight cellulose. This permits the development of advanced liquid-state quantitative NMR methods for characterization of unsubstituted and low degree of substitution celluloses, for example, surface-modified nanocelluloses, which are insoluble in all molecular solvents. As such, we present the use of the tetrabutylphosphonium acetate ([P4444][OAc]):DMSO- d6 electrolyte in the 1D and 2D NMR characterization of poly(methyl methacrylate) (PMMA)-grafted cellulose nanocrystals (CNCs). PMMA- g-CNCs was chosen as a difficult model to study, to illustrate the potential of the technique. The chemical shift range of [P4444][OAc] is completely upfield of the cellulose backbone signals, avoiding signal overlap. In addition, application of diffusion-editing for 1H and HSQC was shown to be effective in the discrimination between PMMA polymer graft resonances and those from low molecular weight components arising from the solvent system. The bulk ratio of methyl methacrylate monomer to anhydroglucose unit was determined using a combination of HSQC and quantitative 13C NMR. After detachment and recovery of the PMMA grafts, through methanolysis, DOSY NMR was used to determine the average self-diffusion coefficient and, hence, molecular weight of the grafts compared to self-diffusion coefficients for PMMA GPC standards. This finally led to a calculation of both graft length and graft density using liquid-state NMR techniques. In addition, it was possible to discriminate between triads and tetrads, associated with PMMA tacticity, of the PMMA still attached to the CNCs (before methanolysis). CNC reducing end and sulfate half ester resonances, from sulfuric acid hydrolysis, were also assignable. Furthermore, other biopolymers, such as hemicelluloses and proteins (silk and wool), were found to be soluble in the electrolyte media, allowing for wider application of this method beyond just cellulose analytics.