Influence of Phosphorus Structures and Their Oxidation States on Flame-Retardant Properties of Polyhydroxyurethanes.

This article focuses on the synthesis of polyhydroxyurethane (PHU) materials containing novel phosphorus flame retardants (FR). Four different phosphorus compounds were grafted onto cyclic carbonate: 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO), diethyl phosphite (DEP), diphenyl phosphite (DPP) and dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide (BPPO). Thus, three novel phosphorus reactive cyclic carbonates which have never been reported so far were synthetized. Phosphorus FR containing PHU materials were characterized by FTIR to evidence the total conversion of the cyclic carbonate. Moreover, the gel contents up to 80% confirmed the formation of the polymer network. Then, the thermal stability and the flame-retardant properties were investigated by thermogravimetric analyses, cone calorimeter and pyrolysis combustion flow calorimeter. The mode of action of phosphorus compounds, depending on the oxidation state, was especially highlighted. Phosphonate (+III) provided better action in a condensed phase than phosphinate thanks to a more efficient char formation. Among phosphonates, differences were observed in terms of char-formation rate and expansion. DEP provided the best flame-retardant properties, with a reduction of 76% of pHRR with 2 wt% of phosphorus in cone calorimeter analysis. Therefore, this article highlighted the different modes of action of phosphorus flame retardants, depending on the oxidation state of phosphorus, in PHU materials.

Phosphorus Modified Cardanol: A Greener Route to Reduce VolaTile Organic Compounds and Impart Flame Retardant Properties to Alkyd Resin Coatings.

Novel phosphorylated cardanol molecules based on phosphonate (PO3CR) and phosphate (PO4CR) functions were synthetized. Those molecules have two main actions which are described in this article: the reduction in volatile organic compounds (VOC) and the development of flame retardant (FR) properties conferred on alkyd resins used as coatings for wood specimen. Phosphorylated cardanol compounds have been successfully grafted by covalent bonds to alkyd resins thanks to an auto-oxidative reaction. The impact of the introduction of PO3CR and PO4CR on the film properties such as drying time and flexibility has been studied and the thermal and flame retardant properties through differential scanning calorimeter, thermogravimetric analysis and pyrolysis-combustion flow calorimeter. These studies underscored an increase in the thermal stability and FR properties of the alkyd resins. In the cone calorimeter test, the lowest pHRR was obtained with 3 wt% P of phosphate-cardanol and exhibited a value of 170 KW.m-2, which represented a decrease of almost 46% compared to the POxCR-free alkyd resins. Moreover, a difference in the mode of action between phosphonate and phosphate compounds has been highlighted. The most effective coating which combined excellent FR properties and good coating properties has been obtained with 2 wt% P of phosphate-cardanol. Indeed, the film properties were closed to the POxCR-free alkyd resin and the pHRR decreased by 41% compared to the reference alkyd resin.