ABSTRACT
The influence of the water content in the initial composition on the size of silica particles produced using the Stöber process is well known. We have shown that there are three morphological regimes defined by compositional boundaries. At low water levels (below stoichiometric ratio of water:tetraethoxysilane), very high surface area and aggregated structures are formed; at high water content (>40 wt%) similar structures are also seen. Between these two boundary conditions, discrete particles are formed whose size are dictated by the water content. Within the compositional regime that enables the classical Stöber silica, the structural evolution shows a more rapid attainment of final particle size than the rate of formation of silica supporting the monomer addition hypothesis. The clearer understanding of the role of the initial composition on the output of this synthesis method will be of considerable use for the establishment of reliable reproducible silica production for future industrial adoption.
ABSTRACT
New bio-materials have recently gained interest for use in insulation panels in walls, but wider adoption by the building industry is hindered by their intrinsic properties. The fact that such materials are mainly composed of cellulose makes them combustible, and their hydrophilic surface presents a high water uptake, which would lead to faster biodegradation. A hydrophobic treatment with silica particles was successfully synthesised via Stöber process, characterised, and deposited on hemp shiv. The surface of hemp shiv coated several times with 45 and 120 nm particles were uniformly covered, as well as extensively water repellent. Those samples could withstand in humidity chamber without loss of their hydrophobic property and no sign of mould growth after 72 h of exposure.