ABSTRACT
Herein, we report a novel type of symmetrical trithiocarbonate chain transfer agent (CTA) based diphenylmethyl as R groups. The utilization of this CTA in the Reversible Addition-Fragmentation chain Transfer (RAFT) process reveals an efficient control in the polymerization of methacrylic monomers and the preparation of block copolymers. The latter are obtained by the (co)polymerization of styrene or butyl acrylate using a functionalized macro-CTA polymethyl methacrylate (PMMA) previously synthesized. Data show low molecular weight dispersity values (D < 1.5) particularly in the polymerization of methacrylic monomers. Considering a typical RAFT mechanism, the leaving groups (R) from the fragmentation of CTA should be able to re-initiate the polymerization (formation of growth chains) allowing an efficient control of the process. Nevertheless, in the case of the polymerization of MMA in the presence of this symmetrical CTA, the polymerization process displays an atypical behavior that requires high [initiator]/[CTA] molar ratios for accessing predictable molecular weights without affecting the D. Some evidence suggests that this does not completely behave as a common RAFT agent as it is not completely consumed during the polymerization reaction, and it needs atypical high molar ratios [initiator]/[CTA] to be closer to the predicted molecular weight without affecting the D. This work demonstrates that MMA and other methacrylic monomers can be polymerized in a controlled way, and with "living" characteristics, using certain symmetrical trithiocarbonates.
ABSTRACT
Chitosan-coated magnetic nanoparticles (CMNP) were prepared in one-step by precipitation in a high-aqueous phase content reverse microemulsion in the presence of chitosan. The high-aqueous phase concentration led to productivities close to 0.49 g CMNP/100 g microemulsion; much higher than those characteristic of precipitation in reverse microemulsions for preparing magnetic nanoparticles. The obtained nanoparticles present a narrow particle size distribution with an average diameter of 4.5 nm; appearing to be formed of a single crystallite; furthermore they present superparamagnetism and high magnetization values; close to 49 emu/g. Characterization of CMNP suggests that chitosan is present as a non-homogeneous very thin layer; which explains the slight reduction in the magnetization value of CMNP in comparison with that of uncoated magnetic nanoparticles. The prepared nanoparticles show high heavy ion removal capability; as demonstrated by their use in the treatment of Pb2+ aqueous solutions; from which lead ions were completely removed within 10 min.
Subject(s)
Chitosan/chemistry , Metal Nanoparticles/chemistry , Chlorides/chemistry , Emulsions , Ferric Compounds/chemistry , Ferrous Compounds/chemistry , Fractional Precipitation , Hydrogen-Ion Concentration , Magnetic Phenomena , Particle Size , Solvents/chemistry , Water/chemistryABSTRACT
The present investigation involves the coordinative chain transfer polymerization (CCTP) of biobased terpenes in order to obtain sustainable polymers from myrcene (My) and farnesene (Fa), using the ternary Ziegler-Natta catalyst system comprising [NdV3]/[Al(i-Bu)2H]/[Me2SiCl2] and Al(i-Bu)2H, which acts as cocatalyst and chain transfer agent (CTA). The polymers were produced with a yield above 85% according to the monomeric consumption at the end of the reaction, and the kinetic examination revealed that the catalyst system proceeded with a reversible chain transfer mechanism in the presence of 15-30 equiv. of CTA. The resulting polyterpenes showed narrow molecular weight distributions (Mw/Mn = 1.4-2.5) and a high percent of 1,4-cis microstructure in the presence of 1 equiv. of Me2SiCl2, having control of the molecular weight distribution in Ziegler-Natta catalytic systems that maintain a high generation of 1,4-cis microstructure.
ABSTRACT
A series of copolymers based on ε-caprolactone (ε-CL) in combination with lactone monomers substituted with alkyl groups (4 and 6 carbon atoms), specifically δ-decalactone (δ-DL), ε-decalactone (ε-DL) and δ-dodecalactone (δ-DD), as well as a copolymer using two substituted lactone monomers with alkyl groups (ε-DL and δ-DD) were synthesized in different molar ratios. The objective of the synthesis of these copolymers was to evaluate the effects of branching in the polymer backbone on the crystallinity and the thermal properties of the synthesized materials. All copolymers were obtained via ring-opening polymerization with high conversion values for both comonomers using neodymium isopropoxide (Nd(i-Pr)3) as the initiator, and their compositions were determined by 1H NMR and 13C NMR. The molar masses (M n and M w) and distributions were obtained by GPC measurements. Such measurements showed that a majority of the copolymers exhibited dispersities (Æ) in the range of 1.2-1.6 and M n in the range of 15-40 kDa. First- and second-order transitions such as melting, crystallization and glass transition, as well as the crystallization degree (melting enthalpy), were determined by DSC analysis. Copolymers based on ε-CL developed interesting behaviors, wherein the copolymers with higher percentages of this monomer exhibited semicrystalline behavior, while the copolymers with a higher percentage of the comonomers ε-DL, δ-DL or δ-DD showed amorphous behavior. In contrast, the copolymers synthesized using both monomers from the alkyl group-substituted lactone developed fully amorphous features, regardless of their composition. These changes in the crystalline features of the synthesized copolymers suggest that the content of short branchings on the copolymer backbone will significantly modify their rates of hydrolytic degradation and their potential use in the development of different soft medical devices.
ABSTRACT
Nanoparticles (NP) of 12.7 nm in diameter of the poly(methyl methacrylate (MMA)-co-methacrylic acid (MAA)) copolymer were prepared. 13C-NMR results showed a MMA:MAA molar ratio of 0.64:0.36 in the copolymer, which is similar to the poly(MMA-co-MAA) commercially known as the FDA approved Eudragit S100 (0.67:0.33). The NP prepared in this study were loaded at pH 5 with varying amounts (from 0.54 to 6.91%) of doxorubicin (DOX), an antineoplastic drug. 1H-NMR results indicated the electrostatic interactions between the ionized carboxylic groups of the MAA units in the copolymer and the proton of the glycosidic amine in DOX. Measurements by QLS and TEM indicated that the loading destabilizes the NP, and that for increase stability, they aggregate in a reversible way, forming aggregates with a diameter up to 99.5 nm at a DOX load of 6.91%. The analysis of drug release data at pH 7.4 showed that loaded NP with at least 4.38% DOX release the drug very slowly and follows the Higuchi model; the former suggests that they could remain for long periods in the bloodstream to reach and destroy cancer cells.
Subject(s)
Drug Delivery Systems , Nanoparticles , Doxorubicin , Drug Carriers , Hydrogen-Ion Concentration , Methacrylates , Polymethyl MethacrylateABSTRACT
This article proposes a process to prepare fully bio-based elastomer nanocomposites based on polyfarnesene and cellulose nanocrystals (CNC). To improve the compatibility of cellulose with the hydrophobic matrix of polyfarnesene, the surface of CNC was modified via plasma-induced polymerization, at different powers of the plasma generator, using a trans-ß-farnesene monomer in the plasma reactor. The characteristic features of plasma surface-modified CNC have been corroborated by spectroscopic (XPS) and microscopic (AFM) analyses. Moreover, the cellulose nanocrystals modified at 150 W have been selected to reinforce polyfarnesene-based nanocomposites, synthesized via an in-situ coordination polymerization using a neodymium-based catalytic system. The effect of the different loading content of nanocrystals on the polymerization behavior, as well as on the rheological aspects, was evaluated. The increase in the storage modulus with the incorporation of superficially modified nanocrystals was demonstrated by rheological measurements and these materials exhibited better properties than those containing pristine cellulose nanocrystals. Moreover, we elucidate that the viscoelastic moduli of the elastomer nanocomposites are aligned with power-law model systems with characteristic relaxation time scales similar to commercial nanocomposites, also implying tunable mechanical properties. In this foreground, our findings have important implications in the development of fully bio-based nanocomposites in close competition with the commercial stock, thereby producing alternatives in favor of sustainable materials.
ABSTRACT
In this work, we explore the statistical copolymerization of 1,3-butadiene with the terpenic monomers myrcene and farnesene, carried out via coordination polymerization using a neodymium-based ternary catalytic system. The resultant copolymers, poly(butadiene-co-myrcene) and poly(butadiene-co-farnesene), were synthesized at different monomer ratios, elucidating the influence of the bio-based monomer content over the kinetic variables, molecular and thermal properties, and the reactivity constants (Fineman-Ross and Kelen-Tüdös methods) of the resultant copolymers. The results indicate that through the herein employed conditions, it is possible to obtain "more sustainable" high-cis (≈95%) polybutadiene elastomers with random and tunable content of bio-based monomer. Moreover, the polymers exhibit fairly high molecular weights and a rather low dispersity index. Upon copolymerization, the T g of high-cis PB can be shifted from -106 to -75 °C (farnesene) or -107 to -64 °C (myrcene), without altering the microstructure control. This work contributes to the development of more environmentally friendly elastomers, to form "green" rubber materials.
ABSTRACT
This article proposes a method to produce bio-elastomer nanocomposites, based on polyfarnesene or polymyrcene, reinforced with surface-modified graphene oxide (GO). The surface modification is performed by grafting alkylamines (octyl-, dodecyl-, and hexadecylamine) onto the surface of GO. The successful grafting was confirmed via spectroscopic (FTIR and Raman) and X-ray diffraction techniques. The estimated grafted amines appear to be around 30 wt%, as calculated via thermogravimetric analysis, increasing the inter-planar spacing among the nanosheets as a function of alkyl length in the amine. The resulting modified GOs were then used to prepare bio-elastomer nanocomposites via in situ coordination polymerization (using a ternary neodymium-based catalytic system), acting as reinforcing additives of polymyrcene and polyfarnesene. We demonstrated that the presence of the modified GO does not affect significantly the catalytic activity, nor the microstructure-control of the catalyst, which led to high cis-1,4 content bio-elastomers (>95%). Moreover, we show via rheometry that the presence of the modified-GO expands the capacity of the elastomer to store deformation or applied stress, as well as exhibit an activation energy an order of magnitude higher.
ABSTRACT
Towards the development of eco-friendly alternatives of elastomeric materials, which can replace petroleum-based materials, it is crucial to explore different monomers and catalytic systems in order to find the best possible combinations for specific applications. Herein, we report the synthesis of polyocimene via coordination polymerization using two different neodymium-based catalysts (NdV3 and Nd(Oi-Pr)3), activated by alkylaluminums/organoboron compounds. By varying the type of co-catalyst species, halide donors, and reaction parameters, we have demonstrated the possibility to obtain polymers with a controlled microstructure and tunable properties, in terms of molecular weight characteristics and kinetics. Our results provide important insights towards the search for the optimum catalytic system to produce bio-elastomers.
ABSTRACT
Ibuprofen-loaded polymeric particles with around 9.2 nm in mean diameter, as determined by electron microscopy, dispersed in an aqueous media containing up to 12.8% solids were prepared by semicontinuous heterophase polymerization. The polymeric material is a (2/1 mol/mol) methyl methacrylate-co-methacrylic acid copolymer similar to Eudragit S100, deemed safe for human consumption and used in the manufacturing of drug-loaded pills as well as micro- and nanoparticles. The loading efficiency was 100%, attaining around 10-12% in drug content. Release studies showed that the drug is released from the nanoparticles at a slower rate than that in the case of free IB. Given their size as well as the pH values required for their dissolution, it is believed that this type of particles could be used as a basis for preparing nanosystems loaded with a variety of drugs.