ABSTRACT
Magnetic skyrmions are topological spin textures which are envisioned as nanometer scale information carriers in magnetic memory and logic devices. The recent demonstrations of room temperature skyrmions and their current induced manipulation in ultrathin films were first steps toward the realization of such devices. However, important challenges remain regarding the electrical detection and the low-power nucleation of skyrmions, which are required for the read and write operations. Here, we demonstrate, using operando magnetic microscopy experiments, the electrical detection of a single magnetic skyrmion in a magnetic tunnel junction (MTJ) and its nucleation and annihilation by gate voltage via voltage control of magnetic anisotropy. The nucleated skyrmion can be manipulated by both gate voltages and external magnetic fields, leading to tunable intermediate resistance states. Our results unambiguously demonstrate the readout and voltage controlled write operations in a single MTJ device, which is a major milestone for low power skyrmion based technologies.
ABSTRACT
Perpendicular shape anisotropy (PSA) offers a practical solution to downscale spin-transfer torque magnetoresistive random-access memory (STT-MRAM) beyond the sub-20 nm technology node while retaining thermal stability. However, our understanding of the thermomagnetic behavior of PSA-STT-MRAM is often indirect, relying on magnetoresistance measurements and micromagnetic modeling. Here, the magnetism of a NiFe PSA-STT-MRAM nanopillar is investigated using off-axis electron holography, providing spatially resolved magnetic information as a function of temperature. Magnetic induction maps reveal the micromagnetic configuration of the NiFe storage layer (â¼60 nm high, ≤20 nm diameter), confirming the PSA induced by its 3:1 aspect ratio. In situ heating demonstrates that the PSA of the storage layer is maintained up to at least 250 °C, and direct quantitative measurements reveal a moderate decrease of magnetic induction. Hence, this study shows explicitly that PSA provides significant stability in STT-MRAM applications that require reliable performance over a range of operating temperatures.
ABSTRACT
All-graphenic carbon morphologies grown on individual carbon nanotubes (CNTs) consisting of short-fiber segments bearing sharp micro-/nano-cones at both ends were mounted as new probes for scanning probe microscopies (SPM). Three mounting procedures were tested, two based on focused ion and/or electron beam processes operated in scanning electron microscopes, and another based on an irradiation-free procedure under an optical microscope. The benefits and drawbacks of all the methods are described in details. The extent to which the structural integrity of the carbon material of the cones was affected by each of the mounting processes was also investigated using Raman spectroscopy and high-resolution transmission electron microscopy. The carbon cones were found to be sensitive to both ion and electron irradiation to an unusual extent with respect to structurally-close nano-objects such as multi-wall CNTs. This was assumed to be due to the occurrence of a large number of free graphene-edges at the cone surface. The suitability of such carbon cones as SPM probes is demonstrated, the characteristics of which make them potentially superior to Si-, diamond-, or CNT-probes.
ABSTRACT
Graphene-based carbon micro-/nano-cones were prepared by depositing pyrolytic carbon onto individual carbon nanotubes as supports using a specific chemical vapor deposition process. They were investigated by means of high-resolution scanning electron microscopy, low-voltage aberration-corrected transmission electron microscopy, Raman spectroscopy, and molecular dynamics modeling. While the graphenes were confirmed to be perfect, the cone texture was determined to be preferably scroll-like, with the scroll turns being parallel to the cone axis. Correspondingly, many of the concentrically displayed graphenes (actually scroll turns) exhibit the same helicity vector. When radii of curvature are large enough, this could allow for coherent stacking to locally take place in spite of the lattice shift induced by the curvature. A particular care was taken on investigating the cone apexes, in which a specific type of graphene termination was observed, here designated as the "zip" defect. Calculations determined a plausible stable structure that such a defect type may correspond to. This defect was found to generate a very low Raman ID/ID' band ratio (1.5), for which physical reasons are proposed. Combining our results and that of the literature allowed proposing an identification chart for a variety of defects able to affect the graphene lattice or edges.
ABSTRACT
Off-axis electron holography was used to observe and quantify the magnetic microstructure of a perpendicular magnetic anisotropic (PMA) recording media. Thin foils of PMA materials exhibit an interesting up and down domain configuration. These domains are found to be very stable and were observed at the same time with their stray field, closing magnetic flux in the vacuum. The magnetic moment can thus be determined locally in a volume as small as few tens of cubic nanometers().
ABSTRACT
Focused Electron Beam Induced Deposition (FEBID) for magnetic tip fabrication is presented in this work as an alternative to conventional sputtering-based Magnetic Force Microscopy (MFM) tips. FEBID enables the growth of a high-aspect-ratio magnetic nanorod with customized geometry and composition to overcome the key technical limitations of MFM probes currently on the market. The biggest advantage of these tips, in comparison with CoCr coated pyramidal probes, lies in the capability of creating sharp ends, nearly 10 nm in diameter, which provides remarkable (topographic and magnetic) lateral resolution in samples with magnetic features close to the resolution limits of the MFM technique itself. The shape of the nanorods produces a very confined magnetic stray field, whose interaction with the sample is extremely localized and perpendicular to the surface, with negligible in-plane components. This effect can lead to a better analytical and numerical modelling of the MFM probes and to an increase in the sensitivity without perturbing the magnetic configuration of soft samples. Besides, the high-aspect ratio achievable in FEBID nanorod tips makes them magnetically harder than the commercial ones, reaching coercive fields higher than 900 Oe. According to the results shown, tips based on magnetic nanorods grown by FEBID can be eventually used for quantitative analysis in MFM measurements. Moreover, the customized growth of Co- or Fe-based tips onto levers with different mechanical properties allows MFM studies that demand different measuring conditions. To showcase the versatility of this type of probe, as a last step, MFM is performed in a liquid environment, which still remains a challenge for the MFM community largely due to the lack of appropriate probes on the market. This opens up new possibilities in the investigation of magnetic biological samples.
ABSTRACT
Cold-field emission properties of carbon cone nanotips (CCnTs) have been studied in situ in the transmission electron microscope (TEM). The current as a function of voltage, i(V), was measured and analyzed using the Fowler-Nordheim (F-N) equation. Off-axis electron holography was employed to map the electric field around the tip at the nanometer scale, and combined with finite element modeling, a quantitative value of the electric field has been obtained. For a tip-anode separation distance of 680 nm (measured with TEM) and a field emission onset voltage of 80 V, the local electric field was 2.55 V/nm. With this knowledge together with recorded i(V) curves, a work function of 4.8±0.3 eV for the CCnT was extracted using the F-N equation.
ABSTRACT
A micromagnetic study of epitaxial micron-sized iron dots is reported through the analysis of Fresnel contrast in Lorentz Microscopy. Their use is reviewed and developed through analysis of various magnetic structures in such dots. Simple Landau configuration is used to investigate various aspects of asymmetric Bloch domain walls. The experimental width of such a complex wall is first derived and its value is discussed with the help of micromagnetic simulations. Combination of these two approaches enables us to define what is really extracted when estimating asymmetric wall width in Lorentz Microscopy. Moreover, quantitative data on the magnetization inside the dot is retrieved using phase retrieval as well as new information on the degrees of freedom of such walls. Finally, it is shown how the existence and the propagation of a surface vortex can be characterized and monitored. This demonstrates the ability to reach a magnetic sensitivity a priori hidden in Fresnel contrast, based on an original image treatment and backed-up by the evaluation of contrasts obtained from micromagnetic simulations.
ABSTRACT
Thin film alloys with perpendicular anisotropy were studied using Lorentz transmission electron microscopy (LTEM). This work focuses on the configuration of domain walls and demonstrates the suitability and accuracy of LTEM for the magnetic characterization of perpendicular magnetic anisotropy materials. Thin films of chemically ordered (L1(0)) FePd alloys were investigated by micro-magnetic modeling and LTEM phase retrieval approach. The different components of magnetization described by the modeling were studied on experimental images and confirmed by LTEM contrast simulation. Furthermore, quantitative measurements of magnetic induction inside the domain walls were made by using an original method to separate the electrical and magnetical contributions to the phase information. Irregularities were also observed along the domain walls which could play a major role during the magnetization processes.