Depth-Resolved Characterization of Perylenediimide Side-Chain Polymer Thin Film Structure Using Grazing-Incidence Wide-Angle X-ray Diffraction with Tender X-rays.

Polymers with a perylenediimide (PDI) side chain (PAc12PDI) consist of two kinds of crystalline structures with various types of orientations in a thin film. Understanding the population of the microcrystalline structure and its orientation along the thickness is strongly desired. Grazing-incidence wide-angle X-ray diffraction (GIWAXD) measurements with hard X-rays, which are generally chosen as λ = 0.1 nm, are a powerful tool to evaluate the molecular aggregation structure in thin films. A depth-resolved analysis for the outermost surface of the polymeric materials using conventional GIWAXD measurements, however, has limitations on depth resolution because the X-ray penetration depth dramatically increases above the critical angle. Meanwhile, tender X-rays (λ = 0.5 nm) have the potential advantage that the penetration depth gradually increases above the critical angle, leading to precise characterization for the population of crystallite distribution along the thickness. The population of the microcrystalline states in the PAc12PDI thin film was precisely characterized utilizing GIWAXD measurements using tender X-rays. The outermost surface of the PAc12PDI thin film is occupied by a monoclinic lattice with a = 2.38 nm, b = 0.74 nm, c = 5.98 nm, and ß = 108.13°, while maintaining the c-axis perpendicular to the substrate surface. Additionally, the presence of solid substrate controls the formation of the crystallite with unidirectional orientation.

Preparation of High-Density Polymer Brushes with a Multihelical Structure.

It is well-known that a mixture of isotactic and syndiotactic polymethyl methacrylate (PMMA) forms a stereocomplex consisting of a multihelical structure in which an isotactic chain is surrounded by a syndiotactic chain. Here, we report the basic structure of the stereocomplex formed when the syndiotactic PMMA chains are tethered to a silicon substrate and form a high-density polymer brush. The influence of geometric confinement was investigated by preparing the high-density polymer brushes on a flat and spherical substrate. In both cases, mixing the untethered isotactic PMMA with the grafted syndiotactic PMMA led to the formation of a stereocomplex with a multihelical structure. Static contact angle measurements showed a hindered surface mobility at the outermost surface of the polymer brush, indicating that the stereocomplex forms a crystalline structure. A syndiotactic polymer brush with substituted fluoroalkyl groups was prepared to increase the contrast for grazing incidence wide-angle X-ray diffraction (GIWAXD) measurements. The GIWAXD results verified that the stereocomplex forms a crystalline structure oriented perpendicular to the substrate with a relatively low degree of orientation.