ABSTRACT
An important method that coal-fired power plants use to realise low-cost zero discharge of desulfurisation wastewater (FGD wastewater) is to utilise wet slag removal systems. However, the high Cl- content of FGD wastewater in wet slag removal systems causes environmental damage. In this study, the corrosion behaviour of the inner guide wheel material, 20CrMnTi, was studied using dynamic weight loss and electrochemical methods. X-ray diffraction, scanning electron microscopy, and energy spectroscopy were used to analyse the organisational and phase changes on the surfaces and cross sections of the samples at different Cl- concentrations. The corrosion rate increased with the Cl- concentration up to 20 g/L, but it decreased slightly when the Cl- concentration exceeded 20 g/L. In all the cases, the corrosion rate exceeded 0.8 mm/a. The corrosion product film density initially increased and then decreased as the Cl- concentration increased. The corrosion products comprised mainly α-FeOOH, γ-FeOOH, ß-FeOOH, Fe3O4, and γ-Fe2O3.