RESUMEN
Transition-metal-oxide@heteroatom doped porous carbon composites have attracted considerable research interest because of their large theoretical adsorption capacity, excellent electrical conductivity and well-developed pore structure. Herein, Mn3O4-loaded phosphorus-doped porous carbon composites (Mn3O4@PC-900) were designed and fabricated for the electrosorption of La3+ in aqueous solutions. Due to the synergistic effect between Mn3O4 and PC-900, and the active sites provided by Mn-O-Mn, C/PO, C-P-O and Mn-OH, Mn3O4@PC-900 exhibits high electrosorption performance. The electrosorption value of Mn3O4@PC-900 was 45.34% higher than that of PC-900, reaching 93.02 mg g-1. Moreover, the adsorption selectivity reached 87.93% and 89.27% in La3+/Ca2+ and La3+/Na+ coexistence system, respectively. After 15 adsorption-desorption cycles, its adsorption capacity and retention rate were 50.34 mg g-1 and 54.12%, respectively. The electrosorption process is that La3+ first accesses the pores of Mn3O4@PC-900 to generate an electric double layer (EDL), and then undergoes further Faradaic reaction with Mn3O4 and phosphorus-containing functional groups through intercalation, surface adsorption and complexation. This work is hoped to offer a new idea for exploring transition-metal-oxide @ heteroatom doped porous carbon composites for separation and recovery of rare earth elements (REEs) by capacitive deionization.
Asunto(s)
Carbono , Electrodos , Lantano , Fósforo , Lantano/química , Fósforo/química , Carbono/química , Adsorción , Porosidad , Óxidos/química , Iones , Compuestos de Manganeso/químicaRESUMEN
Using diammonium hydrogen phosphate as an activator and N and P source and and bamboo chips as the carbon source, N, P co-doped activated carbon was prepared by one-step pyrolysis and used to efficiently remove La3+ in aqueous solutions. The effects of activation temperature and pH value on the adsorption performance of La3+ were analyzed, and the activation and adsorption mechanisms were explored using TG-IR, SEM-EDX, pore structure, XPS, and hydrophilicity. The results showed that diammonium hydrogen phosphate easily decomposed at a high temperature to produce ammonia and phosphoric acid, which activated the material and promoted the increase in the specific surface area and pore volume of the activated carbon. As an N and P source, the addition of diammonium hydrogen phosphate successfully achieved the N, P co-doping of activated carbon, and the introduction of N- and P-containing functional groups was the key to enhance the adsorption of La3+. Among them, graphitic nitrogen could provide interactions between La3+-π bonds, and C-P=O and C/P-O-P could provide active sites for the adsorption of La3+ through complexation and electrostatic interaction. The adsorption of La3+ on N, P co-doped activated carbons was endothermic and spontaneous, and the adsorption process conformed to the Langmuir isotherm and secondary kinetic model. Under the process conditions of an activation temperature of 900â and pH=6, the adsorption capacity of the N, P co-doped activated carbon was as high as 55.18 mg·g-1, which was 2.53 times higher than that of the undoped sample, and its adsorption selectivity for La3+ in the La3+/Na+and La3+/Ca2+ coexistence systems reached 93.49% and 82.49%, respectively. Additionally, the removal efficiency remained above 54% after five successive adsorption-desorption cycle experiments.