Semiconductor colloidal quantum wells (CQWs) have emerged as a promising class of gain materials to be used in colloidal lasers. Although low gain thresholds are achieved, the required high gain coefficient levels are barely met for the applications of electrically-driven lasers which entails a very thin gain matrix to avoid charge injection limitations. Here, "giant" CdSe@CdS colloidal quantum well heterostructures of 9.5 to 17.5 monolayers (ML) in total with corresponding vertical thickness from 3.0 to 5.8 nm that enable record optical gain is shown. These CQWs achieve ultra-high material gain coefficients up to ≈140 000 cm-1, obtained by systematic variable stripe length (VSL) measurements and independently validated by transient absorption (TA) measurements, owing to their high number of states. This exceptional gain capacity is an order of magnitude higher than the best levels reported for the colloidal quantum dots. From the dispersion of these quantum wells, low threshold amplified spontaneous emission in water providing an excellent platform for optofluidic lasers is demonstrated. Also, employing these giant quantum wells, whispering gallery mode (WGM) lasing with an ultra-low threshold of 8 µJ cm-2 is demonstrated. These findings indicate that giant CQWs offer an exceptional platform for colloidal thin-film lasers and in-solution lasing applications.
RESUMO
Semiconductor colloidal quantum wells (CQWs) provide anisotropic emission behavior originating from their anisotropic optical transition dipole moments (TDMs). Here, solution-processed colloidal quantum well light-emitting diodes (CQW-LEDs) of a single all-face-down oriented self-assembled monolayer (SAM) film of CQWs that collectively enable a supreme level of IP TDMs at 92% in the ensemble emission are shown. This significantly enhances the outcoupling efficiency from 22% (of standard randomly-oriented emitters) to 34% (of face-down oriented emitters) in the LED. As a result, the external quantum efficiency reaches a record high level of 18.1% for the solution-processed type of CQW-LEDs, putting their efficiency performance on par with the hybrid organic-inorganic evaporation-based CQW-LEDs and all other best solution-processed LEDs. This SAM-CQW-LED architecture allows for a high maximum brightness of 19,800 cd m-2 with a long operational lifetime of 247 h at 100 cd m-2 as well as a stable saturated deep-red emission (651 nm) with a low turn-on voltage of 1.7 eV at a current density of 1 mA cm-2 and a high J90 of 99.58 mA cm-2 . These findings indicate the effectiveness of oriented self-assembly of CQWs as an electrically-driven emissive layer in improving outcoupling and external quantum efficiencies in the CQW-LEDs.