RESUMO
We present a systematic 2D spatial-coherence analysis of the soft-X-ray beamline P04 at PETRA III for various beamline configurations. The influence of two different beam-defining apertures on the spatial coherence properties of the beam is discussed and optimal conditions for coherence-based experiments are found. A significant degradation of the spatial coherence in the vertical direction has been measured and sources of this degradation are identified and discussed. The Fourier-analysis method, which gives fast and simple access to the 2D spatial coherence function of the X-ray beam, is used for the experiment. Here, we exploit the charge scattering of a disordered nanodot sample allowing the use of arbitrary X-ray photon energies with this method.
RESUMO
Direct 2D spatial-coherence measurements are increasingly gaining importance at synchrotron beamlines, especially due to present and future upgrades of synchrotron facilities to diffraction-limited storage rings. We present a method to determine the 2D spatial coherence of synchrotron radiation in a direct and particularly simple way by using the Fourier-analysis method in conjunction with curved gratings. Direct photon-beam monitoring provided by a curved grating circumvents the otherwise necessary separate determination of the illuminating intensity distribution required for the Fourier-analysis method. Hence, combining these two methods allows for time-resolved spatial-coherence measurements. As a consequence, spatial-coherence degradation effects caused by beamline optics vibrations, which is one of the key issues of state-of-the-art X-ray imaging and scattering beamlines, can be identified and analyzed.
RESUMO
We present a comparative study of the morphology and structural as well as magnetic properties of crystalline Fe3O4/NiO bilayers grown on both MgO(001) and SrTiO3(001) substrates by reactive molecular beam epitaxy. These structures were investigated by means of X-ray photoelectron spectroscopy, low-energy electron diffraction, X-ray reflectivity and diffraction, as well as vibrating sample magnetometry. While the lattice mismatch of NiO grown on MgO(001) was only 0.8%, it was exposed to a lateral lattice mismatch of −6.9% if grown on SrTiO3. In the case of Fe3O4, the misfit strain on MgO(001) and SrTiO3(001) amounted to 0.3% and −7.5%, respectively. To clarify the relaxation process of the bilayer system, the film thicknesses of the magnetite and nickel oxide films were varied between 5 and 20 nm. While NiO films were well ordered on both substrates, Fe3O4 films grown on NiO/SrTiO3 exhibited a higher surface roughness as well as lower structural ordering compared to films grown on NiO/MgO. Further, NiO films grew pseudomorphic in the investigated thickness range on MgO substrates without any indication of relaxation, whereas on SrTiO3 the NiO films showed strong strain relaxation. Fe3O4 films also exhibited strong relaxation, even for films of 5 nm thickness on both NiO/MgO and NiO/SrTiO3. The magnetite layers on both substrates showed a fourfold magnetic in-plane anisotropy with magnetic easy axes pointing in 100 directions. The coercive field was strongly enhanced for magnetite grown on NiO/SrTiO3 due to the higher density of structural defects, compared to magnetite grown on NiO/MgO.