Combined computational and experimental study about the incorporation of phosphorus into the structure of graphene oxide.

Phosphorus-containing graphene-based hybrids are materials with outstanding properties for diverse applications. In this work, an easy route to produce phosphorus-graphene oxide hybrid materials is described, involving the use of variable amounts of H3PO4 and H2SO4 during the reaction of oxidation of a graphitic precursor. The physical and chemical features of the hybrids change significantly with the variation in the acid amounts used in the syntheses. XPS and solid-state 13C and 31P NMR results show that the hybrids contain large amounts of oxygen functional groups, with the phosphorus incorporation proceeding mostly through the formation of phosphate-like linkages and other functions with C-O-P bonds. The experimental findings are supported by DFT calculations, which allow the assessment of the energetics and the geometry of the interaction between phosphate groups and graphene-based models; these calculations are also used to predict the chemical shifts in the 31P and 13C NMR spectra of the models, which show good agreement with the experimentally observed solid-state NMR spectra.

Nanostructured faujasite zeolite as metal ion adsorbent: kinetics, equilibrium adsorption and metal recovery studies.

The hydrothermal synthesis of nano-faujasite has been successfully performed and the effects of some crystallization parameters were investigated, along with the use of this material as a heavy-metal ion adsorbent. X-ray diffraction patterns have shown that the structure of the nano-faujasite is strongly dependent on both the crystallization time and the alkalinity of the synthesis medium. According to N2 physisorption, X-ray fluorescence, SEM/EDS, and solid state 29Si and 27Al NMR data, the produced nano-faujasite consists of a solid with low molar Si/Al ratio (1.7), with high availability of ion exchange sites and high surface area/small particle size, allowing easy diffusion of metal ions to adsorbent active sites. As a consequence, an excellent performance on removal of Cd2+, Zn2+ and Cu2+ ions was found for this solid. The adsorption capacity followed the order Cd2+ (133 mg·g-1) > Zn2+ (115 mg·g-1) > Cu2+ (99 mg·g-1), which agrees with the order of increasing absolute values of the hydration energy of the metal ions. Kinetic studies and adsorption isotherms showed that the metal ion removal takes place by ion exchange on the monolayer surface of the nano-faujasite. The electrochemical recovery of copper in metallic form exhibited an efficiency of 80.2% after 120 min, which suggests that this process can be adequately implemented for full-scale metal removal.